Abstract: Provided is a pressure-sensitive adhesive (PSA) sheet including a PSA layer formed from a PSA composition including a base polymer, crosslinking agents of two or more species having mutually different types of crosslinkable functional groups, and an azole-based rust inhibitor. Here, one of the crosslinking agents of two or more species is an isocyanate-based crosslinking agent. Monomeric components constituting the base polymer include a carboxy group-containing monomer. The amount of the azole-based rust inhibitor in the PSA layer is less than 8 parts by weight with respect to 100 parts by weight of the base polymer.

Abstract: A composition according to the present invention is a silicone adhesive composition including 100 parts by weight of a peroxide-curable silicone, 1.2 to 3.2 parts by weight of an organic peroxide curing agent, and 2 to 9 parts by weight of an addition reaction-curable silicone rubber. An adhesive tape according to the present invention is a tape including a base and an adhesive layer placed on the base, the adhesive layer being formed from the above silicone adhesive composition. The adhesive composition according to the present invention exhibits high load bearing capacity even in higher-temperature environments than ever before. The adhesive tape according to the present invention exhibits high load bearing capacity and good shelf life even in such high-temperature environments.

Abstract: An adhesive tape substrate production method disclosed in the present description includes the steps of: decreasing the amount of a sizing agent contained in a glass cloth by heat; impregnating the glass cloth for which the amount of the sizing agent has been decreased with a dispersion of a fluorine resin; and heating the impregnated glass cloth to a temperature equal to or higher than a melting point of the fluorine resin. Thus, an adhesive tape substrate including the glass cloth impregnated with the fluorine resin is obtained. This method are more productive of adhesive tape substrates and adhesive tapes than conventional methods. In addition, adhesive tape substrates and adhesive tapes for which the occurrence of defects in appearance are reduced can be produced.

Abstract: The present invention provides a double-sided adhesive tape in which the adhesive strength between a substrate and each adhesive layer is high and the rupture of the substrate is unlikely to occur. Also, the present invention is a method for producing a double-sided adhesive tape having a polytetrafluoroethylene porous film substrate and adhesive layers formed respectively on both sides of the substrate. The method includes the following steps (1) to (4) in order: (1) the step of putting an adhesive composition on a first release liner; (2) the step of bonding the first release liner on which the adhesive composition has been put to one main surface of the polytetrafluoroethylene porous film substrate; (3) the step of forming a first adhesive layer by heating the substrate to which the first release liner has been bonded; and (4) the step of providing a second adhesive layer on another main surface of the substrate, a part of an adhesive in the second adhesive layer being penetrated into the substrate.