Abstract: A pneumatic tire includes metal cords each made of metal filaments twisted together, the metal cords having an initial elongation in a range of from 0.05 to 0.20% and a standard deviation of the initial elongation in a range of not more than 0.02. A method of manufacturing the metal cord comprises shaping metal filaments in a two-dimensional zigzag waveform, and twisting the shaped metal filaments together, wherein the number of the filaments is in a range of from 8 to 12, the metal filaments have the same diameter (d) of from 0.15 to 0.30 mm, the shaped metal filaments have the same zigzag waveforms, the zigzag waveform of each said shaped metal filament has constant wave lengths (P) and constant wave heights (h) wherein the ratio (P/d) is in the range of 100/3 to 700/3, and the ratio (h/d) is in the range of 5/3 to 80/3.

Abstract: A pneumatic tire includes metal cords each made of metal filaments twisted together, the metal cords having an initial elongation in a range of from 0.05 to 0.20% and a standard deviation of the initial elongation in a range of not more than 0.02. A method of manufacturing the metal cord comprises shaping metal filaments in a two-dimensional zigzag waveform, and twisting the shaped metal filaments together, wherein the number of the filaments is in a range of from 8 to 12, the metal filaments have the same diameter (d) of from 0.15 to 0.30 mm, the shaped metal filaments have the same zigzag waveforms, the zigzag waveform of each said shaped metal filament has constant wave lengths (P) and constant wave heights (h) wherein the ratio (P/d) is in the range of 100/3 to 700/3, and the ratio (h/d) is in the range of 5/3 to 80/3.

Abstract: A rubber composition obtained by (a) kneading at least one low air permeable rubber having vulcanizable functional group and a curing agent, which can vulcanize the low air permeable rubber having vulcanizable functional group, at a temperature within a range where the low air permeable rubber having vulcanizable functional group is not vulcanized, and (b) blending 25 to 100 parts by weight of at least one rubber having vulcanizable carbon-carbon double bond per 100 parts by weight of the low air permeable rubber having vulcanizable functional group with the kneaded product, kneading at a temperature within a range where the low air permeable rubber having vulcanizable functional group can be vulcanized to selectively vulcanize the low air permeable rubber having vulcanizable functional group.

Abstract: A rubber composition obtained by