Abstract: For integrally bonding a first member and a second member made of copper or a copper alloy by brazing, a paste brazing material composed essentially of copper (Cu), tin (Sn), nickel (Ni) and phosphorus (P) is beforehand applied to at least one of the first and second members. A base material is exposed at the whole or a part of a contact portion between the first and second members. Thereafter, the first and second members are assembled at a predetermined position, and heated at a temperature in a range of 600° C.-800° C. within a reducing atmosphere furnace. By the brazing method, an oxide film on the surface of the base material can be sufficiently removed, so that the paste brazing material can smoothly flow on the surface at the contact portion.

Abstract: A method of brazing brass parts without oxidation of zinc, which is contained in the parts, during brazing of the parts with phosphorous bronze solder at relatively low temperature of 630-700° C., the brazing being made by making the wall of brazing furnace or muffle of carbon material, like graphite etc., making an inert nitrogen gas or mixture of nitrogen and hydrogen in the furnace atmosphere contact with the carbon material above, producing CO less the P co=10?3 atm. in the furnace, and making the furnace atmosphere reductive against zinc in the brass parts and/or flux in the solder.

Abstract: For integrally bonding a first member and a second member made of copper or a copper alloy by brazing, a paste brazing material composed essentially of copper (Cu), tin (Sn), nickel (Ni) and phosphorus (P) is beforehand applied to at least one of the first and second members. A base material is exposed at the whole or a part of a contact portion between the first and second members. Thereafter, the first and second members are assembled at a predetermined position, and heated at a temperature in a range of 600° C.-800° C. within a reducing atmosphere furnace. By the brazing method, an oxide film on the surface of the base material can be sufficiently removed, so that the paste brazing material can smoothly flow on the surface at the contact portion.

Abstract: A brazing method for brazing components is provided. The method includes the steps of: coating a bonding portion between the components with a brazing material made of Cu—Sn—Ni—P alloy; introducing reducing gas into a brazing furnace; mounting the components in the brazing furnace; and increasing temperature in the brazing furnace so that the components are brazed. The brazing method provides excellent bonding condition. Specifically, the brazing material steadily penetrates into the bonding portion between the components so that the components are brazed steadily.