Abstract: An object of the present invention is to provide a highly versatile master batch for producing a fiber-reinforced resin composition with high strength even when a highly hydrophobic resin is used as a resin for dilution (a resin that constitutes a fiber-reinforced resin composition). The master batch contains AcylMFs (A), a Pm (B), and a Com (C) and is for use in the production of a fiber-reinforced resin composition by mixing with a Pd (D), wherein the AcylMFs (A), Pm (B), Com (C), and Pd (D) satisfy the following conditions: (a) the AcylMFs (A) have an SPacylmf of 10 or more; (b) the Pm (B) has an SPpm of 9 to 15, and the SPpm is equal to or greater than the SPpd of the Pd (D); and (c) the Com (C) has an SPcom equal to or less than the SPacylmf of the AcylMFs (A).

Abstract: An object of the present invention is to provide a highly versatile master batch for producing a fiber-reinforced resin composition with high strength even when a highly hydrophobic resin is used as a resin for dilution (a resin that constitutes a fiber-reinforced resin composition). The master batch contains AcylMFs (A), a Pm (B), and a Com (C) and is for use in the production of a fiber-reinforced resin composition by mixing with a Pd (D), wherein the AcylMFs (A), Pm (B), Com (C), and Pd (D) satisfy the following conditions: (a) the AcylMFs (A) have an SPacylmf of 10 or more; (b) the Pm (B) has an SPpm of 9 to 15, and the SPpm is equal to or greater than the SPpd of the Pd (D); and (c) the Com (C) has an SPcom equal to or less than the SPacylmf of the AcylMFs (A).

Abstract: The invention provides a method of obtaining a compatible resin blend from at least two incompatible resins which are not conventionally blended with each other. The blend of an incompatible resins is dissolved at a molecular level by being melted and sheared under a high shearing rate by rotating a screw without adding a compatibilizer or the like.

Abstract: The present invention provides a resin composition high in melting flow, exhibiting good properties, excellent in moldability and shrinkage properties, and hence suitable for automobile exteriors, by including (A) propylene/ethylene block copolymer having a melt flow rate (MFR) of 100 to 200 g/10 min., its propylene homopolymer component having an MFR of 210 to 400 g/10 min. and isotactic pentad fraction of 0.98 or more, and its copolymer portion containing propylene at 65 to 85% by weight; 50 to 70% by weight, (B) ethylene/octene and/or ethylene/butene random copolymer; 10 to 25% by weight, (C) styrene-based hydrogenated block copolymer rubber; 4 to 9% by weight and (D) talc; 16 to 24% by weight.

Abstract: The present invention provides a resin composition high in melting flow, exhibiting good properties, excellent in moldability and shrinkage properties, and hence suitable for automobile exteriors, by including (A) propylene/ethylene block copolymer having a melt flow rate (MFR) of 100 to 200 g/10 min., its propylene homopolymer component having an MFR of 210 to 400 g/10 min. and isotactic pentad fraction of 0.98 or more, and its copolymer portion containing propylene at 65 to 85% by weight; 50 to 70% by weight, (B) ethylene/octene and/or ethylene/butene random copolymer; 10 to 25% by weight, (C) styrene-based hydrogenated block copolymer rubber; 4 to 9% by weight and (D) talc; 16 to 24% by weight.

Abstract: A block copolymer is provided comprising one or more blocks of a propylene polymer (PP) and one or more blocks of an ethylene-propylene copolymer (EPR) having the properties: (1) the interface thickness of the PP block with EPR block is from 20-1000 nm; (2) the weight average molecular weight of the PP block is 10,000-1,000,000; (3) the proportion of mesopentad chain in the PP block is not less than 95%; (4) the particle diameter of the disperse phase in EPR block is 0.2-3 microns; (5) the weight average molecular weight of the EPR block is 50,000-1000,000; (6) the propylene content in the EPR block is 20-80 mole %; (7) the composition fluctuation in molecular weight in EPR block is within +/−5% from the average composition.

Abstract: The present invention provides a polypropylene block copolymer or resin composition excellent in impact resistance and rigidity.

Abstract: A thermoplastic resin composition comprising (A) a propylene/ethylene block copolymer, (B) a combination of a low-crystalline ethylene/butene random copolymer resin and an amorphous ethylene/butene random copolymer rubber, or a combination of an ethylene/octene copolymer rubber and an ethylene/propylene copolymer rubber, (C) a specific block elastomer, and (D) talc. This composition has good injection molding properties, can reveal excellent flexural modulus, heat resistance and surface hardness, and is suitable for producing such injection-molded products as interior automotive trims.

Abstract: There is provided a crystalline thermoplastic resin composition comprising (a) 100 parts by weight of a crystalline thermoplastic resin and (b) 0.01 to 11 parts by weight of a laminar structure of silicate, said laminar structure of silicate being present in the form of crystal nuclei dispersed at a molecular level in said resin, and having an aspect ratio of at least 20 as represented by a length-to-breadth ratio of said crystal nuclei.

Abstract: Disclosed is a molded product of a thermoplastic resin composition which comprises:(a) a non-crystalline thermoplastic resin,(b) a crystalline thermoplastic resin and(c) an inorganic filler, if necessary,wherein a portion in which Component (a) takes a structure forming a matrix and a portion in which Component (b) takes a structure forming a matrix coexist.

Abstract: Disclosed is a thermoplast resin composition comprising:30 to 97% by weight of at least one of(a) a crystalline thermoplastic resin component and(b) a non-crystalline thermoplastic resin component,3 to 70% by weight of (c) a rubbery polymer component which is ununiformly mixed with at least one of Component (a) and Component (b) and0 to 40% by weight of (d) an inorganic filler,wherein Component (c) forms a network and at least one of the ratio of flexural modulus of Component (a) to Component (c) and that of Component (b) to Component (c) is 5 or more.

Abstract: A process for producing an oriented blown film of a thermoplastic resin by blown film extrusion, carried out by blowing air into an extruded bubble of the resin extruded from a ring die to expand the bubble and cooling the expanded bubble with air from a cooling air ring, wherein blown film extrusion is carried out under such conditions that the ratio of (b) the final diameter of the expanded bubble to (a) the diameter of the bubble at the crystallizing temperature of the thermoplastic resin ((b)/(a)) ranges from 1.5 to 10. The process provides an oriented blown film excellent in strength, appearance, and heat shrinkage characteristics.

Abstract: Disclosed is a thermoplastic resin composition comprising:30 to 97% by weight of at least one of (a) a crystalline thermoplastic resin component and (b) a non-crystalline thermoplastic resin component, 3 to 70% by weight of (c) a rubbery polymer component which is ununiformly mixed with at least one of Component (a) and Component (b) and 0 to 40% by weight of (d) an inorganic filler,wherein Component (c) forms a network and at least one of the ratio of flexural modulus of Component (a) to Component (c) and that of Component (b) to Component (c) is 5 or more.

Abstract: A polyolefin-based wrapping film having one or more layers which satisfies the following conditions (1) to (4):(1) the film has a thickness ranging from 6 to 100 .mu.m;(2) the film has a birefringence .DELTA.n.sub.A of from 0.6.times.10.sup.-3 to 8.times.10.sup.-3 ;(3) the film has a ratio of percent heat shrinkage in MD to percent heat shrinkage in TD of from 0.65 to 1.50 in a silicon oil bath at 140.degree. C. for 3 minutes; and(4) the film has a strain recovery of at least 18 mm,which provides excellent performance properties in stretch wrapping, especially in the area of high deformation recover.

Abstract: A plated polyamide resin article obtained by plating, with a suitable plating substance, a molded article of a polyamide resin composition is disclosed, the polyamide resin composition comprising (A) from 30 to 80% by weight of a polyamide resin, (B) from 20 to 70% by weight of a polyphenylene ether resin, (C) from 1 to 50 parts by weight, per 100 parts by weight of the sum of (A) and (B), of an impact modifier, and (D) from 0.01 to 30 parts by weight, per 100 parts by weight of the sum of (A) and (B), of a compatibilizer, in which the polyamide resin forms a continuous phase, and the polyphenylene ether resin forms a dispersed phase, with the polyamide resin having a crystallinity of from 20 to 55% with the crystalline region thereof being not less than 72% in the .gamma. crystal form. The plated article is excellent in heat resistance, impact resistance, and appearance.

Abstract: An injection-molded product comprising: component A: 45 to 70% by weight of a propylene polymer 2.16 kg) of 10 to 100 g/10 min and an ethylene content of 0 to 15% by weight; and component B: 30 to 55% by weight of an ethylene/propylene copolymer-based rubber having a melt flow rate (at 230.degree. C. under a load of 5 kg) of 0.5 to 20 g/10 min and a propylene content of 20 to 40% by weight; the ratio MFR.sub.A /MFR.sub.B of the melt flow rate (MFR.sub.A) of component A to the melt flow rate (MFR.sub.B) of component B being 0.5 to 50, and the molded product having such physical properties as expressed in terms of a modulus in flexure of 2,000 to 5,000 kg/cm.sup.2, as determined according to JIS-K7203 and a coefficient of linear expansion of 10 .times.10.sup.-5 /.degree. C. or below, as determined according to ASTM-D696, and having an average thickness of 2 to 7 mm.

Abstract: There is disclosed a resin composition comprising:(a) 28 to 78% by weight of a polyamide resin,(b) 20 to 70% by weight of a polyphenylene ether resin,(c) 2 to 40% by weight of a block copolymer composed of an alkenyl aromatic polymer and a conjugated diene polymer wherein a content of an alkenyl aromatic polymer structure unit is 10 to 45% by weight and at least 50% of a conjugated diene polymer structure unit is hydrogenated and(d) at least one compound selected from the group consisting of .alpha.,.beta.-unsaturated dicarboxylic acid, an acid anhydride and derivatives thereof with an amount of 0.01 to 10 parts by weight based on 100 parts by weight of the sum of Components (a), (b) and (c),which has a specific dispersion state.The resin composition has excellent thermal stability and also good balance between impact strength, rigidity and high temperature rigidity with high degree.

Abstract: A resin composition comprising an amorphous polymer as component (1), a crystalline polymer as component (2) and a rubber like polymer as component (3), wherein component (1) is dispersed in component (2) and component (3) is dispersed in component (2) in network form is disclosed. The resin composition has excellent mechanical properties such as impact strength, flexural modulus, etc.

Abstract: A resin composition comprising (a) a polyphenylene ether resin, (b) a non-crystalline or low-crystalline polyamide resin, (c) a crystalline polyamide resin and, if desired, (d) a polar compound or a low-molecular diene polymer or the component (d) and (e) a rubbery polymer or an alkenyl aromatic compound/conjugated diene copolymer or a hydrogeneration product thereof. The composition is excellent in both impact strength, particularly on a plane part of a plate-molded article, and dimensional stability.

Abstract: A resin composition comprising a resin component comprising a polyphenylene ether resin and a polyamide resin, an aromatic vinyl compound-conjugated diene block copolymer, and a compound having an unsaturated group and a polar group in the molecule thereof. The composition is excellent in impact strength both at low temperature and room temperature, tensile elongation indicative of toughness, and organic solvent resistance.