Abstract: A crosslinked fluororesin includes 10 ppb or less of a perfluoro compound with 8 carbons. The crosslinked fluororesin exhibits no melt flowability when heated above a melting point of the crosslinked fluororesin. A molded body includes a base resin, and the crosslinked fluororesin mixed with the base resin. A crosslinked fluororesin producing method includes crosslinking a fluororesin by being irradiated with ionizing radiation at a temperature higher than a melting point of the fluororesin to provide a crosslinked fluororesin, and performing heat treatment on the crosslinked fluororesin to reduce a content of a perfluoro compound in the crosslinked fluororesin.

Abstract: A resin tube is a tube that is composed of a first fluoropolymer and a second fluoropolymer. The first fluoropolymer is made of a melt-type fluoropolymer that melts at a temperature higher than a melting point, and the second fluoropolymer is made of polytetrafluoroethylene or a cross-linked fluoropolymer. An inner circumferential surface of the tube has irregularities with arithmetic average roughness Ra of 1 ?m or more.

Abstract: A method of manufacturing a crosslinked fluororesin powder includes forming a powder mixture by mixing a fluororesin powder as a first powder with a second powder not fusing to the fluororesin powder even under conditions for crosslinking of the fluororesin powder, and conducting a cross-linking treatment to the formed powder mixture.

Abstract: A method of manufacturing a crosslinked fluororesin powder includes forming a powder mixture by mixing a fluororesin powder as a first powder with a second powder not fusing to the fluororesin powder even under conditions for crosslinking of the fluororesin powder, and conducting a cross-linking treatment to the formed powder mixture.

Abstract: A medical cable is composed of a cable core, a jacket formed around a circumference of the cable core, and a protective film formed around a circumference of the jacket. The jacket is formed of a silicone rubber. The protective film is a resin layer including a mixture of a fluorine resin and a silicone resin. A medical cable producing method includes applying a solution including a fluorine resin and a silicone resin dissolved or dispersed therein to a circumference of a jacket, and baking to form a protective film.

Abstract: A modified fluorocarbon resin composition and a modified molded product of fluorocarbon resin composition having an excellent abrasion resistivity and low friction property under high pressure, are provided. The modified fluorocarbon resin composition comprises a blend of fluorocarbon resin and aromatic engineering plastic, which is modified by irradiation of ionizing radiation.

Abstract: A modified fluorocarbon resin composition and a modified molded product of fluorocarbon resin composition having an excellent abrasion resistivity and low friction property under high pressure, are provided. The modified fluorocarbon resin composition comprises a blend of fluorocarbon resin and aromatic engineering plastic, which is modified by irradiation of ionizing radiation.

Abstract: A seal ring (10) of the present invention seals operating oil hermetically and is attached to an annular seal ring groove (16) provided on an outer circumference of a shaft member (12). The seal ring (10) includes fluororesin, modified fluororesin formed by being irradiated with an ionizing radiation in a range from 1 kGy to 10 MGy inclusive in a state of being heated up to a melting point thereof or higher under an inert gas atmosphere with an oxygen partial pressure of 1.33 kPa or less, and synthetic resin having a surface energy ranging from +0 N/cm to 20˜10?5 N/cm inclusive of that of the operating oil.

Abstract: A sliding member used in a chain system of an automotive internal combustion engine and made of a resin composition. The resin composition includes a matrix resin which is a thermoplastic resin having a number average molecular weight of not less than 20000; and a fluororesin in an amount ranging from 5 to 40% by mass based on a total amount of the resin composition, the fluororesin having a surface energy ranging from 200 to 400 ?N/cm and a visible light transmittance of not less than 10% at a wavelength of 600 nm.

Abstract: A seal ring (10) of the present invention seals operating oil hermetically and is attached to an annular seal ring groove (16) provided on an outer circumference of a shaft member (12). The seal ring (10) includes fluororesin, modified fluororesin formed by being irradiated with an ionizing radiation in a range from 1 kGy to 10 MGy inclusive in a state of being heated up to a melting point thereof or higher under an inert gas atmosphere with an oxygen partial pressure of 1.33 kPa or less, and synthetic resin having a surface energy ranging 14 from +0 N/cm to 20 ˜10?5 N/cm inclusive of that of the operating oil.

Abstract: A seal ring seals operating oil hermetically and is attached to an annular seal ring groove provided on an outer circumference of a shaft member. The seal ring comprises fluororesin, metal powder having a hardness equal to or more than that of any of a side surface of the seal ring groove serving as a sliding partner and an inner circumferential surface of a housing engaged relatively rotatable with the outer circumference of the shaft member, and modified fluororesin formed by irradiating an ionizing radiation in a range from 1 kGy to 10 MGy inclusive in a state of being heated up to a melting point thereof or higher under an inert gas atmosphere with an oxygen partial pressure of 1.33 kPa or less.

Abstract: A seal ring seals operating oil hermetically and is attached to an annular seal ring groove provided on an outer circumference of a shaft member. The seal ring comprises fluororesin, metal powder having a hardness equal to or more than that of any of a side surface of the seal ring groove serving as a sliding partner and an inner circumferential surface of a housing engaged relatively rotatable with the outer circumference of the shaft member, and modified fluororesin formed by irradiating an ionizing radiation in a range from 1 kGy to 10 MGy inclusive in a state of being heated up to a melting point thereof or higher under an inert gas atmosphere with an oxygen partial pressure of 1.33 kPa or less.

Abstract: A fluororesin heated at a temperature at or above the melting point of the resin is exposed in an inert gas atmosphere having an oxygen concentration of not more than 10 Torr to an ionizing radiation at a radiation dose of 0.1 kGy to 10 MGy to prepare a crosslinked fluororesin. The crosslinked fluororesin is exposed to an ionizing radiation at a radiation dose of 10 kGy to 5 MGy, and is then brought into contact with a functional group-containing organic compound to cause a graft reaction. By virtue of this constitution, a modified fluororesin is provided which has satisfactory mechanical strength and, at the same time, has, imparted thereto, for example, ion-exchange capacity, hydrophilicity, adhesive property, or abrasion resistance.

Abstract: A fluororesin heated at a temperature at or above the melting point of the resin is exposed in an inert gas atmosphere having an oxygen concentration of not more than 10 Torr to an ionizing radiation at a radiation dose of 0.1 kGy to 10 MGy to prepare a crosslinked fluororesin. The crosslinked fluororesin is exposed to an ionizing radiation at a radiation dose of 10 kGy to 5 MGy, and is then brought into contact with a functional group-containing organic compound to cause a graft reaction. By virtue of this constitution, a modified fluororesin is provided which has satisfactory mechanical strength and, at the same time, has, imparted thereto, for example, ion-exchange capacity, hydrophilicity, adhesive property, or abrasion resistance.

Abstract: A fluoroplastic-based product having reduced friction and improved abrasion resistance having excellent abrasion resistance as well as good characteristics being inherent to fluoroplastics comprises a fluoroplastic molded material containing a modified fluoroplastic prepared by applying ionizing radiation to a fluoroplastic (I) heated at the melting point or a higher temperature under an inert gas atmosphere having 10 torr or less oxygen concentration within a range of irradiation doses of from 1 KGy to 10 MGy; and an unmodified fluoroplastic (II).