Abstract: An electron beam is radiated on an ion-plating material to heat and evaporate this material, thereby generating a vapor flow of the material. The vapor flow of the material is converged by a hood-like electrode, and at the same time, a positive voltage is applied to the electrode to attract thermoelectrons from the material. The vapor flow is ionized by the thermoelectrons. The converged and ionized vapor flow is deposited on a surface of a strip, thereby performing ion plating.

Abstract: The invention relates to a plated steel sheet for cans which must have high workability and corrosion resistance and can prevent bimetallic corrosion and a method of manufacturing the same. The plated steel sheet is manufactured by forming an electroplated chromium layer on the surface of a steel, removing a hydrated chromium oxide layer formed on the surface of the chromium layer, and forming an aluminum plating layer, so that the electroplated chromium layer and the aluminum plating layer are stacked in direct contact with each other. Another plated steel sheet is manufactured by forming a vacuum deposited chromium layer on the surface of a steel, and forming an aluminum plating layer.

Abstract: The invention relates to a plated steel sheet for cans which must have high workability and corrosion resistance and can prevent bimetallic corrosion and a method of manufacturing the same. The plated steel sheet is manufactured by forming an electroplated chromium layer on the surface of a steel, removing a hydrated chromium oxide layer formed on the surface of the chromium layer, and forming an aluminum plating layer, so that the electroplated chromium layer and the aluminum plating layer are stacked in direct contact with each other. Another plated steel sheet is manufactured by forming a vacuum deposited chromium layer on the surface of a steel, and forming an aluminum plating layer.

Abstract: Titanium magnetic disk substrates are manufactured by preparing a base by stripping not less than 5 .mu.m from the surface layer of a titanium cold-rolled plate, and then forming a film of not less than 5 .mu.m consisting of 1 or more non-magnetic transition metal elements belonging to Groups IVA, VA, VIA, VIIA and VIIIA of the Periodic Table, on the surface of this base.

Abstract: The invention relates to a plated steel sheet for cans which must have high workability and corrosion resistance and can prevent bimetallic corrosion and a method of manufacturing the same. The plated steel sheet is manufactured by forming an electroplated chromium layer on the surface of a steel, removing a hydrated chromium oxide layer formed on the surface of the chromium layer, and forming an aluminum plating layer, so that the electroplated chromium layer and the aluminum plating layer are stacked in direct contact with each other. Another plated steel sheet is manufactured by forming a vacuum deposited chromium layer on the surface of a steel, and forming an aluminum plating layer.