Abstract: The present invention enables magnetic domain control by the method of forming a magnetic coating layer of an Ni—Fe alloy comprised of Fe: 10 to 50 mass % and Ni: 90 to 50 mass % on the surface of grain-oriented electrical steel sheet having mainly {110}<001> orientation texture so that even if annealing after core formation, the iron loss improving effect will not be lost and the magnetic flux density will not be greatly reduced.

Abstract: The present invention stably provides a high-strength hot-dip galvanized steel sheet having a high tensile strength and no non-plated portions and being excellent in workability and surface properties even when the employed equipment has only a reduction annealing furnace and a steel sheet containing relatively large amounts of Si, Mn and Al that are regarded as likely to cause non-plated portions is used as the substrate.

Abstract: Grain-oriented electrical steel sheet having a chrome-free high tensile strength insulating film characterized by comprising steel sheet on the surface of which is formed an insulating film containing a phosphate and colloidal silica as main ingredients and containing crystalline magnesium phosphate uniformly dispersed over the entire surface.

Abstract: The present invention provides a grain-oriented electrical steel sheet product having a superior corrosion resistance, annealing resistance, film tension, and the like in insulating treatment based on a phosphate not containing chromium and a treatment agent for the same, so provides grain-oriented electrical steel sheet having an insulating film not containing chromium characterized by the insulating film containing a phosphate and one or more compounds selected from inorganic compounds of Fe, Ni, Co, Cu, Sr, and Mo in an amount, as metal elements, of 0.06 to 2.10 moles per mole of phosphate, and an insulating film agent of the same.

Abstract: A baseball or softball bat which enables a ball to fly farther than a conventional bat. The bat is made of metal, wood or carbon fiber-reinforced plastic and its cylindrical ball-hitting part has an axial cross section shape as follows: a lot of concave-surfaced grooves and convex-surfaced ridges are arranged in parallel alternately along the circumference of the bat and the convex parts are round and curved outward. The concave and convex parts are covered by a cylindrical sheet of polyurethane elastomer or similar material. Also, a metal baseball or softball bat is manufactured by grooving the cylindrical ball-hitting part surface by a lathe using a roller.

Abstract: A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 ?m, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.

Abstract: In a method for manufacturing grain-oriented silicon steel with mirror-like surface by applying an aqueous slurry of an annealing separator, magnetic properties are stabilized by controlling the amount of moisture, carried in the annealing separator consisting mainly of alumina after application and drying thereof, to not more than 1.5%, controlling the partial water vapor pressure during finish-annealing and eliminating the variation (instability) in secondary recrystallization caused by the inhibitor reaction at the interface.

Abstract: The present invention stably provides a high-strength hot-dip galvanized steel sheet having a high tensile strength and no non-plated portions and being excellent in workability and surface properties even when the employed equipment has only a reduction annealing furnace and a steel sheet containing relatively large amounts of Si, Mn and Al that are regarded as likely to cause non-plated portions is used as the substrate.

Abstract: The present invention stably provides a high-strength hot-dip galvanized steel sheet having a high tensile strength and no non-plated portions and being excellent in workability and surface properties even when the employed equipment has only a reduction annealing furnace and a steel sheet containing relatively large amounts of Si, Mn and Al that are regarded as likely to cause non-plated portions is used as the substrate.

Abstract: A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 ?m, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.

Abstract: A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 ?m, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.

Abstract: The present invention stably provides a high-strength hot-dip galvanized steel sheet having a high tensile strength and no non-plated portions and being excellent in workability and surface properties even when the employed equipment has only a reduction annealing furnace and a steel sheet containing relatively large amounts of Si, Mn and Al that are regarded as likely to cause non-plated portions is used as the substrate.

Abstract: In a method for manufacturing grain-oriented silicon steel with mirror-like surface by applying an aqueous slurry of an annealing separator, magnetic properties are stabilized by controlling the amount of moisture, carried in the annealing separator consisting mainly of alumina after application and drying thereof, to not more than 1.5%, controlling the partial water vapor pressure during finish-annealing and eliminating the variation (instability) in secondary recrystallization caused by the inhibitor reaction at the interface.

Abstract: The present invention provides a method for producing a grain-oriented silicon steel sheet not having inorganic mineral films by using an annealing separator capable of preventing the inorganic mineral films composed of forsterite (Mg2SiO4), and so on, from forming during final annealing, comprising the steps of decarburization annealing followed by coating of annealing separator and final annealing, wherein alumina powder calcined at a calcination temperature of 900 to 1,400° C., or further having a BET specific surface area of 1 to 100 m2/g, an oil absorption of 1 to 70 ml/100 g, and/or having a gamma ratio of 0.001 to 2.0, is used as the annealing separator. Magnesia having a BET specific surface area of 0.5 to 5 m2/g may be added to said alumina powder.

Abstract: The present invention provides a grain-oriented silicon steel sheet excellent in adhesiveness to tension-creating insulating coating films formed on the grain-oriented silicon steel sheet produced by removing inorganic mineral films composed of forsterite and so on with pickling or the like or by deliberately preventing the formation thereof, characterized by: having, at the interface between each of the tension-creating insulating coating films and the steel sheet, an external oxidation type membranous oxide film of 2 to 500 nm in average thickness mainly composed of amorphous silica and/or a mixed oxide film consisting of an external oxidation type membranous oxide film of 2 to 500 nm in average thickness mainly composed of amorphous silica and particulate oxides mainly composed of amorphous silica: and satisfying any one or more of the specified requirements.

Abstract: A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 &mgr;m, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.

Abstract: The present invention provides a method for producing a grain-oriented silicon steel sheet not having inorganic mineral films by using an annealing separator capable of preventing the inorganic mineral films composed of forsterite (Mg2SiO4), and so on, from forming during final annealing, comprising the steps of decarburization annealing followed by coating of annealing separator and final annealing, wherein alumina powder calcined at a calcination temperature of 900 to 1,400° C., or further having a BET specific surface area of 1 to 100 m2/g, an oil absorption of 1 to 70 ml/100 g, and/or having a gamma ratio of 0.001 to 2.0, is used as the annealing separator. Magnesia having a BET specific surface area of 0.5 to 5 m2/g may be added to said alumina powder.

Abstract: The present invention provides a grain-oriented silicon steel sheet excellent in adhesiveness to tension-creating insulating coating films formed on the grain-oriented silicon steel sheet produced by removing inorganic mineral films composed of forsterite and so on with pickling or the like or by deliberately preventing the formation thereof, characterized by: having, at the interface between each of the tension-creating insulating coating films and the steel sheet, an external oxidation type membranous oxide film of 2 to 500 nm in average thickness mainly composed of amorphous silica and/or a mixed oxide film consisting of an external oxidation type membranous oxide film of 2 to 500 nm in average thickness mainly composed of amorphous silica and particulate oxides mainly composed of amorphous silica: and satisfying any one or more of the specified requirements.

Abstract: The present invention, in a method to produce a grain-oriented electrical steel sheet, proposes conditions for stable production by clarifying the causes by which secondary recrystallization is rendered unstable when primary recrystallization is controlled by raising the heating rate of decarburization annealing. The primary recrystallization structure is controlled by changing the heating rate and the oxide layer of a steel sheet is controlled by changing the conditions of soaking annealing in the decarburization annealing. The composition of the (Al, Si)N inhibitor is also controlled in the nitriding treatment thereafter.

Abstract: A high permeability grain-oriented electromagnetic steel sheet with a higher tension-imparting effect and more excellent cohesion and magnetic properties compared to the prior art, which also maintains sufficient corrosion resistance to withstand practical use; the grain-oriented electromagnetic steel sheet has on its surface an insulation coating comprising a first layer composed mainly of a divalent or trivalent metal hydrogen phosphate salt and silica, and a second layer composed mainly of aluminum borate and leaving a surface roughness of 0.1 &mgr;m-0.35 &mgr;m in terms of Ra (center like average roughness).