Abstract: A zirconia sintered body is provided having a color tone equivalent to the color tone guides of various natural teeth and having the same aesthetics as a natural front tooth. The present invention provides a colored translucent zirconia sintered body comprising zirconia containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe2O3, less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.

Abstract: A zirconia sintered body contains aluminum, cobalt, and manganese and a remaining portion consisting of yttria-containing zirconia. In an oxide exchange, aluminum content is 5.0 wt % or more and 30.0 wt % or less, cobalt content is 0.1 wt % or more and 2.0 wt % or less, and manganese content is 0.5 wt % or more and 7.0 wt % or less.

Abstract: A zirconia sintered body is provided having a color tone equivalent to the color tone guides of various natural teeth and having the same aesthetics as a natural front tooth. The present invention provides a colored translucent zirconia sintered body comprising zirconia containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe2O3, less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.

Abstract: A zirconia sintered body is provided having a color tone equivalent to the color tone guides of various natural teeth and having the same aesthetics as a natural front tooth. The present invention provides a colored translucent zirconia sintered body comprising zirconia containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe2O3, less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.

Abstract: To provide a zirconia sintered body having both excellent translucency and bending strength, specifically a zirconia sintered body having both translucency and strength suitable as a denture for front tooth, and a process for its production. A translucent zirconia sintered body containing more than 4.0 mol % and at most 6.5 mol % of yttria and less than 0.1 wt % of alumina, and having a relative density of at least 99.82%, a total light transmittance of at least 37% and less than 40% to light with a wavelength of 600 nm at a thickness of 1.0 mm, and a bending strength of at least 500 MPa, and a process for its production.

Abstract: A zirconia sintered body is provided having a color tone equivalent to the color tone guides of various natural teeth and having the same aesthetics as a natural front tooth. The present invention provides a colored translucent zirconia sintered body comprising zirconia containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe2O3, less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.

Abstract: To provide a zirconia sintered body having both excellent translucency and bending strength, specifically a zirconia sintered body having both translucency and strength suitable as a denture for front tooth, and a process for its production. A translucent zirconia sintered body containing more than 4.0 mol % and at most 6.5 mol % of yttria and less than 0.1 wt % of alumina, and having a relative density of at least 99.82%, a total light transmittance of at least 37% and less than 40% to light with a wavelength of 600 nm at a thickness of 1.0 mm, and a bending strength of at least 500 MPa, and a process for its production.

Abstract: A pink-colored zirconia sintered body has a high sintered body density and strength, and a colored translucency, which has a color tone similar to teeth and excellent translucency and has high aesthetic properties. A colored translucent zirconia sintered body includes from 2 to 4 mol % of yttria, from 0.02 to 0.8 mol % of Er2O3, at least 20 and less than 2,000 ppm, as calculated as Fe2O3, of an iron compound, at least 0.005 and less than 0.2 wt % of Al2O3 and the rest being zirconia, and having a lightness L* of from 55 to 75, a* of from 0 to 10 and b* of from 0 to 30 as chromatic parameters stipulated in JIS-Z8729, has a relative density of at least 99.80% and has a total light transmittance of at least 18% and at most 40% as measured at a sample thickness of 1 mm using a D65 light source.

Abstract: A subject of the invention relates to providing a powder for a translucent zirconia sintered body which is necessary for the production of a zirconia sintered body having a high sintered-body density and high strength and giving an excellent sense of translucency, without conducting any special sintering, such as HIP sintering. The invention relates to a technique for obtaining, through normal-pressure sintering, a translucent zirconia sintered body characterized by comprising zirconia which contains 2-4 mol % yttria as a stabilizer and has an alumina content of 0.2 wt % or lower, and by having a relative density of 99.8% or higher and a total light transmittance, as measured at a thickness of 1.0 mm, of 35% or higher. It is preferred that a powder containing 0-0.2 wt % alumina with a particle diameter of 0.01-0.5 ?m, having a BET specific surface area of 5-16 m2/g and an average particle diameter of 0.3-0.7 ?m, and having a rate of sintering shrinkage in normal-pressure sintering (??/?T; g/cm3·° C.) of 0.

Abstract: A zirconia sintered body having not only high strength but also excellent aesthetic properties. A colored translucent zirconia sintered body, characterized by containing an iron compound and from 2 to 4 mol % of yttria, showing a lightness L* of from 51 to 80 in L*a*b* color system, and having a relative density of at least 99.80%. The colored zirconia sintered body preferably has a total light transmittance of at least 20% as measured at a sample thickness of 1 mm and with a D65 light source. The colored translucent zirconia sintered body has aesthetic properties equivalent to those of natural teeth and is particularly suitable for a zirconia sintered body to be used for dental applications, and further, suitable for a mill blank such as an artificial tooth material or the like, and an orthodontic bracket.

Abstract: A pink-colored zirconia sintered body has a high sintered body density and strength, and a colored translucency, which has a color tone similar to teeth and excellent translucency and has high aesthetic properties. A colored translucent zirconia sintered body includes from 2 to 4 mol % of yttria, from 0.02 to 0.8 mol % of Er2O3, at least 20 and less than 2,000 ppm, as calculated as Fe2O3, of an iron compound, at least 0.005 and less than 0.2 wt % of Al2O3 and the rest being zirconia, and having a lightness L* of from 55 to 75, a* of from 0 to 10 and b* of from 0 to 30 as chromatic parameters stipulated in JIS-Z8729, has a relative density of at least 99.80% and has a total light transmittance of at least 18% and at most 40% as measured at a sample thickness of 1 mm using a D65 light source.

Abstract: A subject of the invention relates to providing a powder for a translucent zirconia sintered body which is necessary for the production of a zirconia sintered body having a high sintered-body density and high strength and giving an excellent sense of translucency, without conducting any special sintering, such as HIP sintering. The invention relates to a technique for obtaining, through normal-pressure sintering, a translucent zirconia sintered body characterized by comprising zirconia which contains 2-4 mol % yttria as a stabilizer and has an alumina content of 0.2 wt % or lower, and by having a relative density of 99.8% or higher and a total light transmittance, as measured at a thickness of 1.0 mm, of 35% or higher. It is preferred that a powder containing 0-0.2 wt % alumina with a particle diameter of 0.01-0.5 ?m, having a BET specific surface area of 5-16 m2/g and an average particle diameter of 0.3-0.7 ?m, and having a rate of sintering shrinkage in normal-pressure sintering (??/?T; g/cm3·° C.) of 0.

Abstract: A zirconia sintered body having not only high strength but also excellent aesthetic properties. A colored translucent zirconia sintered body, characterized by containing an iron compound and from 2 to 4 mol % of yttria, showing a lightness L* of from 51 to 80 in L*a*b* color system, and having a relative density of at least 99.80%. The colored zirconia sintered body preferably has a total light transmittance of at least 20% as measured at a sample thickness of 1 mm and with a D65 light source. The colored translucent zirconia sintered body has aesthetic properties equivalent to those of natural teeth and is particularly suitable for a zirconia sintered body to be used for dental applications, and further, suitable for a mill blank such as an artificial tooth material or the like, and an orthodontic bracket.

Abstract: A subject of the invention relates to providing a powder for a translucent zirconia sintered body which is necessary for the production of a zirconia sintered body having a high sintered-body density and high strength and giving an excellent sense of translucency, without conducting any special sintering, such as HIP sintering. The invention relates to a technique for obtaining, through normal-pressure sintering, a translucent zirconia sintered body characterized by comprising zirconia which contains 2-4 mol % yttria as a stabilizer and has an alumina content of 0.2 wt % or lower, and by having a relative density of 99.8% or higher and a total light transmittance, as measured at a thickness of 1.0 mm, of 35% or higher. It is preferred that a powder containing 0-0.2 wt % alumina with a particle diameter of 0.01-0.5 ?m, having a BET specific surface area of 5-16 m2/g and an average particle diameter of 0.3-0.7 ?m, and having a rate of sintering shrinkage in normal-pressure sintering (??/?T; g/cm3·° C.) of 0.

Abstract: A zirconia-containing powder including 2 to 6 weight % of a pigment which has a spinel structure represented by the chemical formula (Co1-xZnx)(Fe1-yAly)2O4(0?x?0.5, 0<y?0.5) or which is a coprecipitated material containing Co, Zn, Fe, and Al and has the same spinel structure after calcination, 0.05 to 6 weight % of Al2O3, and 3.60 to 7.10 weight % of Y2O3; and a black zirconia sintered body obtained by sintering the zirconia-containing powder within a temperature range of 1300 to 1500° C.

Abstract: A zirconia-containing powder including 2 to 6 weight % of a pigment which has a spinel structure represented by the chemical formula (Co1-xZnx)(Fe1-yAly)2O4(0?x?0.5, 0<y?0.5) or which is a coprecipitated material containing Co, Zn, Fe, and Al and has the same spinel structure after calcination, 0.05 to 6 weight % of Al2O3, and 3.60 to 7.10 weight % of Y2O3; and a black zirconia sintered body obtained by sintering the zirconia-containing powder within a temperature range of 1300 to 1500° C.

Abstract: A combustion catalyst for removing organic compounds from a gas stream containing the same and a process for removing organic compounds from the gas stream using the catalyst are disclosed. The combustion catalyst comprises a first catalyst comprising a metal oxide containing at least one of the elements of the platinum group, and a second catalyst comprising a mixture of zeolite with a metal oxide containing at least one of the elements of the platinum group, in a manner such that the organic compounds are contacted first with the first catalyst and then with the second catalyst, whereby the organic compounds can be efficiently removed at a low temperature.

Abstract: A combustion catalyst for removing organic compounds from a gas stream containing the same and a process for removing organic compounds from the gas stream using the catalyst are disclosed. The combustion catalyst comprises a first catalyst comprising a metal oxide containing at least one of the elements of the platinum group, and a second catalyst comprising a mixture of zeolite with a metal oxide containing at least one of the elements of the platinum group, in a manner such that the organic compounds are contacted first with the first catalyst and then with the second catalyst, whereby the organic compounds can be efficiently removed at a low temperature.