Abstract: A rolling-sliding member that is high in hardness and continues to have a passivation film reliably even after being subjected to a process that does not require any processing for removal of scale, etc., as well as a rolling bearing using the same and a method for manufacturing the rolling-sliding member.

Abstract: A rolling-sliding member that is high in hardness and continues to have a passivation film reliably even after being subjected to a process that does not require any processing for removal of scale etc., as well as a rolling bearing using the same and a method for manufacturing the rolling-sliding member.

Abstract: A rolling-sliding member that is high in hardness and continues to have a passivation film reliably even after being subjected to a process that does not require any processing for removal of scale, etc., as well as a rolling bearing using the same and a method for manufacturing the rolling-sliding member.

Abstract: A rolling-sliding member that is high in hardness and continues to have a passivation film reliably even after being subjected to a process that does not require any processing for removal of scale etc., as well as a rolling bearing using the same and a method for manufacturing the rolling-sliding member.

Abstract: A steel part having a long rolling contact fatigue life and capable of further increasing the life of a bearing under severer using condition than usual conditions. The steel part includes steel having a composition containing 0.7% by mass to 1.1% by mass of C, 0.5% by mass to 2.0% by mass of Si, 0.4% by mass to 2.5% by mass of Mn, 1.6% by mass to 5.0% by mass of Cr, 0.1% by mass to less than 0.5% by mass of Mo, 0.010% by mass to 0.050% by mass of Al, less than 0.0015% by mass of Sb as an impurity, and the balance composed of Fe and inevitable impurities, the steel being hardened and tempered. In the steel structure of a portion from the surface to a depth of 5 mm, residual cementite has a grain diameter of 0.05 to 1.5 ?m, prior austenite has a grain diameter of 30 ?m or less, and the ratio by volume of the residual austenite is less than 25%.

Abstract: Provided are a steel having excellent rolling contact fatigue life and the manufacturing method thereof. The steel consists essentially of 0.7 to 1.1% C, 0.2 to 2.0% Si, 0.4 to 2.5% Mn, 1.6 to 4.0% Cr, 0.1% or more and less than 0.5% Mo, 0.010 to 0.050% Al, bymass, and balance of Fe and inevitable impurities, is treated by quenching and tempering, has residual cementite grain sizes ranging from 0.05 to 1.5 ?m, and has prior-austenite grain sizes of 30 ?m or smaller. When the steel is used to bearing steel, the bearing life extends even under service in more severe environments.

Abstract: A steel part having a long rolling contact fatigue life and capable of further increasing the life of a bearing under severer using condition than usual conditions. The steel part includes steel having a composition containing 0.7% by mass to 1.1% by mass of C, 0.5% by mass to 2.0% by mass of Si, 0.4% by mass to 2.5% by mass of Mn, 1.6% by mass to 5.0% by mass of Cr, 0.1% by mass to less than 0.5% by mass of Mo, 0.010% by mass to 0.050% by mass of Al, less than 0.0015% by mass of Sb as an impurity, and the balance composed of Fe and inevitable impurities, the steel being hardened and tempered. In the steel structure of a portion from the surface to a depth of 5 mm, residual cementite has a grain diameter of 0.05 to 1.5 ?m, prior austenite has a grain diameter of 30 ?m or less, and the ratio by volume of the residual austenite is less than 25%.

Abstract: A rolling/sliding member used for a toroidal continuously variable transmission according to the present invention is made of steel containing at least C: not less than 0.8 wt % and not more than 1.5 wt %, Si: not less than 0.9 wt % and not more than 2.1 wt % and Cr: not less than 2 wt % and not more than 5 wt %, and by applying surface hardening through machining to a surface whose surface hardness is set to not less than 60 HRC and not more than 64 HRC through quenching/tempering, surface compression residual stress thereof is set to not less than 700 MPa and not more than 1100 MPa. Furthermore, the amount of reduction of surface hardness when heated at 300° C. is set to not more than 1 HRC.

Abstract: A steel part having a long rolling contact fatigue life and capable of further increasing the life of a bearing under severer using condition than usual conditions. The steel part includes steel having a composition containing 0.7% by mass to 1.1% by mass of C, 0.5% by mass to 2.0% by mass of Si, 0.4% by mass to 2.5% by mass of Mn, 1.6% by mass to 5.0% by mass of Cr, 0.1% by mass to less than 0.5% by mass of Mo, 0.010% by mass to 0.050% by mass of Al, less than 0.0015% by mass of Sb as an impurity, and the balance composed of Fe and inevitable impurities, the steel being hardened and tempered. In the steel structure of a portion from the surface to a depth of 5 mm, residual cementite has a grain diameter of 0.05 to 1.5 ?m, prior austenite has a grain diameter of 30 ?m or less, and the ratio by volume of the residual austenite is less than 25%.

Abstract: Provided are a steel having excellent rolling contact fatigue life and the manufacturing method thereof. The steel consists essentially of 0.7 to 1.1% C, 0.2 to 2.0% Si, 0.4 to 2.5% Mn, 1.6 to 4.0% Cr, 0.1% or more and less than 0.5% Mo, 0.010 to 0.050% Al, bymass, and balance of Fe and inevitable impurities, is treated by quenching and tempering, has residual cementite grain sizes ranging from 0.05 to 1.5 ?m, and has prior-austenite grain sizes of 30 ?m or smaller. When the steel is used to bearing steel, the bearing life extends even under service in more severe environments.

Abstract: Bearing steel containing 0.10 wt % to 0.35 wt % of C, less than 0.5 wt % of Si, 0.3 wt % to 1.5 wt % of Mn, 0.03 wt % or less of P, 0.03 wt % or less of S, 1.0 wt % to 3.5 wt % of Ni, 1.0 wt % to 5.0 wt % of Cr, 0.03 wt % to 2.5 wt % of Mo, 0.005 wt % to 0.050 wt % of Al, 0.003 wt % or less of Ti, 0.0015 wt % or less of O, 0.025 wt % or less of N, and a substantially residual part of Fe, wherein the bearing steel after carburizing or carbonitriding treatment exhibits a surface C concentration of not lower than 0.9%, contains 15% by area or less of carbide and contains 0.1% by area or less of rod-like carbide 10 having an aspect ratio of not lower than 3 in terms of the ratio of major diameter to minor diameter and having a minor diameter of not smaller than 2 &mgr;m.