Abstract: The present invention relates to a phosphor having excellent emission brightness by inclusion of Si or Fe in the phosphor having a TbAG:Ce composition, and a white LED. The white photoluminescent device in accordance with the present invention comprises at least one light-emitting diode emitting light with a wavelength of 430 to 470 nm and a phosphor having a composition of TbAG:Ce, wherein the phosphor having a composition of TbAG:Ce is composed of a compositional formula of (Tb1-xCex)3(Al1-yMy)5O12, wherein x is between 0.01 and 0.4, y is between 0.0 and 0.1, and M is selected from the group consisting of Si and Fe.

Abstract: The present invention is directed to phosphors and white light emitting diodes and a method for preparing a Ce3+ doped calcium silicate phosphor represented by a chemical formula of (Ca1-yMy)2-x-zSiO4:Ce3+x,N+z, wherein x is 0<x?0.5, y is 0?y?0.5, z is 0<z?0.5, M is at least one metal selected from Mg, Sr and Ba, and N is at least one metal selected from Li, Na, K and Rb, as well as white LEDs produced comprising the same. The phosphor of the present invention can be excited using conventional InGaN-based blue light emitting diodes, as well as GaN-based near-UV light emitting diodes to emit light across the visible spectrum.

Abstract: The present invention relates to a phosphor having excellent emission brightness by inclusion of Si or Fe in the phosphor having a TbAG:Ce composition, and a white LED. The white photoluminescent device in accordance with the present invention comprises at least one light-emitting diode emitting light with a wavelength of 430 to 470 nm and a phosphor having a composition of TbAG:Ce, wherein the phosphor having a composition of TbAG:Ce is composed of a compositional formula of (Tb1-xCex)3 (Al1-yMy)5O12, wherein x is between 0.01 and 0.4, y is between 0.0 and 0.1, and M is selected from the group consisting of Si and Fe.

Abstract: The present invention relates to a phosphor and a white LED, more particularly, to a method for fabricating a yellow emitting Ce3+-activated silicate phosphor with a new composition represented as (Sr1-y-zMyNz)3-xSiO5:Ce3+x, (0<x?0.3, M includes at least one selected from alkaline earth metals on the periodic table, 0?y?1, N is at least one selected from alkali metals on the periodic table and 0?z?0.3) and a preparation method thereof and an LED using the same. The phosphor according to the present invention shows a broad band emission when it is excited by the existing InGaN-based blue LED and GaN-based ultraviolet LED with long wavelength. The LED using the phosphor according to the present invention has a broad emission with a wide spectral range and good color purity and very high light emitting efficiency when is applied to a LED and a backlight source of a liquid crystal display.