Abstract: The present invention discloses a selenium-doped MXene composite nano-material and a preparation method thereof, comprising the following steps: (1) adding MXene and an organic selenium source into a dispersant, and stirring to prepare a dispersion with a concentration of 1 mg/ml to 100 mg/ml; (2) transferring the dispersion into a reaction kettle, then heating, reacting, and then naturally cooling to a room temperature; (3) washing the product obtained in the step (2) with a cleaning agent, then centrifuging to collect a precipitate, and drying the precipitate under vacuum; and (4) placing the sample obtained in the step (3) into a tubular furnace for calcination, introducing protective gas, heating, and then cooling to a room temperature to obtain the selenium-doped MXene composite nano-material. The material prepared by the present invention has high specific surface area, good electrical conductivity, cycle stability performance, rate performance and high theoretical specific capacity.

Abstract: The present invention discloses a selenium-doped MXene material and a preparation method thereof, comprising the following steps: (1) adding MXene and an organic selenium source into a dispersant, and stirring to prepare a dispersion with a concentration of 10 mg/ml to 100 mg/ml, wherein a mass ratio of MXene and an organic selenium source is 0.1 to 1:1; (2) transferring the dispersion into a reaction kettle, heating to 110° C. to 230° C., reacting for 10 h to 30 h, and then naturally cooling to a room temperature; and (3) washing the product obtained in the step (2) with a cleaning agent, centrifuging to collect a precipitate, and drying the precipitate under vacuum to obtain the selenium-doped MXene material. The composite material prepared by the present invention has high specific surface area, good electrical conductivity, cycle stability performance, rate performance and high theoretical specific capacity.

Abstract: The present invention discloses a tellurium-doped MXene composite material and a preparation method thereof, comprising the following steps: (1) adding MXene and a tellurium source into a dispersant to prepare a dispersion, and then stirring the dispersion; (2) heating the dispersion, reacting, and then cooling; (3) centrifuging the product obtained in the step (2), then washing and drying under vacuum; and (4) placing the dry product obtained in the step (3) into a corundum ark, and then transferring into a tubular furnace, heating under the protection of inert gas, retaining the temperature, and then cooling to obtain the tellurium-doped MXene composite material. The composite material prepared by the present invention can be used as a cathode of a potassium ion battery, which increases the interlamellar spacing, and optimizes an ion diffusion channel, so that the electrochemical performance of the potassium ion battery is improved.

Abstract: The present invention discloses a selenium-doped MXene composite nano-material and a preparation method thereof, comprising the following steps: (1) adding MXene and an organic selenium source into a dispersant, and stirring to prepare a dispersion with a concentration of 1 mg/ml to 100 mg/ml; (2) transferring the dispersion into a reaction kettle, then heating, reacting, and then naturally cooling to a room temperature; (3) washing the product obtained in the step (2) with a cleaning agent, then centrifuging to collect a precipitate, and drying the precipitate under vacuum; and (4) placing the sample obtained in the step (3) into a tubular furnace for calcination, introducing protective gas, heating, and then cooling to a room temperature to obtain the selenium-doped MXene composite nano-material. The material prepared by the present invention has high specific surface area, good electrical conductivity, cycle stability performance, rate performance and high theoretical specific capacity.

Abstract: The present invention discloses a tellurium-doped MXene composite material and a preparation method thereof, comprising the following steps: (1) adding MXene and a tellurium source into a dispersant to prepare a dispersion, and then stirring the dispersion; (2) heating the dispersion, reacting, and then cooling; (3) centrifuging the product obtained in the step (2), then washing and drying under vacuum; and (4) placing the dry product obtained in the step (3) into a corundum ark, and then transferring into a tubular furnace, heating under the protection of inert gas, retaining the temperature, and then cooling to obtain the tellurium-doped MXene composite material. The composite material prepared by the present invention can be used as a cathode of a potassium ion battery, which increases the interlamellar spacing, and optimizes an ion diffusion channel, so that the electrochemical performance of the potassium ion battery is improved.

Abstract: The present invention discloses a selenium-doped MXene material and a preparation method thereof, comprising the following steps: (1) adding MXene and an organic selenium source into a dispersant, and stirring to prepare a dispersion with a concentration of 10 mg/ml to 100 mg/ml, wherein a mass ratio of MXene and an organic selenium source is 0.1 to 1:1; (2) transferring the dispersion into a reaction kettle, heating to 110° C. to 230° C., reacting for 10 h to 30 h, and then naturally cooling to a room temperature; and (3) washing the product obtained in the step (2) with a cleaning agent, centrifuging to collect a precipitate, and drying the precipitate under vacuum to obtain the selenium-doped MXene material. The composite material prepared by the present invention has high specific surface area, good electrical conductivity, cycle stability performance, rate performance and high theoretical specific capacity.

Abstract: Disclosed are various embodiments for verifying user-provided data feeds. A data feed is received from a client and stored in a data store. An error detection process is initiated upon the data feed. A flag is set indicating that the data feed is being processed. A detected error from the error detection process is stored in the data store. The flag is updated indicating that processing of the data feed is finished upon completion of the error detection process. Upon a polling of the flag indicating that the processing of the data feed is finished, an update is generated to the user interface employed in the client to transfer the data feed. The update describes the detected error.