Abstract: The present invention relates to an ethylene-vinyl alcohol copolymer composition, a single-layer film and a multilayer structure containing the same. Said ethylene-vinyl alcohol copolymer composition includes an ethylene-vinyl alcohol copolymer, an antioxidant, and a fluorine-containing compound; and the ratio of the antioxidant content to the fluorine content is 0.5 to 65. Thereby, the film containing said ethylene-vinyl alcohol copolymer composition not only has good heat resistance, but also can avoid the situation that a large number of gels are generated during the preparation process.

Abstract: The present invention relates to an ethylene-vinyl alcohol copolymer (EVOH) resin composition, an EVOH film formed therefrom, and a multilayer structure containing the same. The core height difference (Sk) of the surface of the EVOH resin composition is between 0.6 and 2.0 ?m, and the overall standard deviation of Sk is between 0.05 and 0.55. The invention can reduce the torque output during processing to achieve the effect of energy saving, and can also improve the stability during output to obtain a better film appearance.

Abstract: The present invention relates to an ethylene-vinyl alcohol copolymer (EVOH) resin composition, an EVOH film formed therefrom, and a multilayer structure containing the same. The core height difference (Sk) of the surface of the EVOH resin composition is between 0.6 and 2.0 ?m, and the overall standard deviation of Sk is between 0.05 and 0.55. The invention can reduce the torque output during processing to achieve the effect of energy saving, and can also improve the stability during output to obtain a better film appearance.

Abstract: The instant disclosure relates to a fluorine-containing ethylene-vinyl alcohol copolymer (EVOH) resin composition as well as mixture and blend thereof. The fluorine-containing EVOH resin composition comprises EVOH and fluorine-containing particles, wherein the fluorine-containing EVOH resin composition has a total fluoride ion content ranging from 45 to 41000 ppm. The invention can reduce the adhesion of EVOH to the inside of the extruder, and effectively reduce the appearance of gel or gelled substance in subsequent finished products.

Abstract: The instant disclosure relates to a fluorine-containing ethylene-vinyl alcohol copolymer (EVOH) resin composition as well as mixture and blend thereof. The fluorine-containing EVOH resin composition comprises EVOH and fluorine-containing particles, wherein the fluorine-containing EVOH resin composition has a total fluoride ion content ranging from 45 to 41000 ppm. The invention can reduce the adhesion of EVOH to the inside of the extruder, and effectively reduce the appearance of gel or gelled substance in subsequent finished products.

Abstract: The instant disclosure relates to ethylene vinyl alcohol copolymer resin composition and/or pellets thereof including one or more fluorine-containing micro-particles. The ethylene vinyl alcohol copolymer resin compositions and/or pellets thereof may have a melting pressure of 1.7 to 7.0 MPa at a shear rate of 20 s?1 and a melting point temperature of 190° C. EVOH films formed from the EVOH may have a Charpy impact strength of at least 2.3 KJ/m2 according to ISO 179-1 at 23° C. and an elongation at break of at least 17.8% according to ISO 527-2 at 23° C.

Abstract: The instant disclosure relates to ethylene vinyl alcohol copolymer resin composition and/or pellets thereof including one or more fluorine-containing micro-particles. The ethylene vinyl alcohol copolymer resin composition and/or pellets thereof may have a boron content of 10 to 450 ppm. EVOH films formed from the EVOH may have a Charpy impact strength of at least 2.5 KJ/m2 according to ISO 179-1 at 23° C. and an elongation at break of at least 18.2% according to ISO 527-2 at 23° C.

Abstract: The instant disclosure relates to ethylene vinyl alcohol pellets including one or more fluorine-containing micro-particles having a particle size that is not greater than 20 ?m. The EVOH films formed from the EVOH pellets may have a Charpy impact strength of at least 2.45 KJ/m2 according to ISO 179-1 at 23° C. and an elongation at break of at least 17.8% according to ISO 527-2 at 23° C.