Abstract: The disclosure provides a laser surface treatment method and a laser surface treatment station. The laser surface treatment method is applied to a surface to be adhesively bonded of a casting of a vehicle body-in-white part, wherein the laser surface treatment method comprises the following steps: S1: providing the casting of the vehicle body-in-white part, the casting having been demolded and machined; and S2: performing laser surface treatment on the surface to be adhesively bonded of the casting, the surface to be adhesively bonded being used for a subsequent adhesive application process for connection of the casting, wherein the laser surface treatment is carried out by pulse laser, and the laser surface treatment employs the following parameters: an average laser power greater than 500 W; a laser frequency ranging from 5 kHz to 10 kHz; and laser single-point energy greater than 50 mJ.

Abstract: The disclosure relates to an aluminum alloy and a component part prepared therefrom. The aluminum alloy comprises: 7-9 wt% of silicon (Si), 0.15-0.45 wt% of chromium (Cr), 0.1-0.3 wt% of vanadium (V), at least 0.01 wt% of strontium (Sr), 0.1-0.2 wt% of titanium (Ti), 0-0.5 wt% of manganese (Mn), 0-0.8 wt% of iron (Fe) and the balance being aluminum and inevitable impurities. The aluminum alloy of the disclosure can be exempt from heat treatment process after casting in the processing process, so as to contribute to energy conservation and emission reduction, and the component part prepared therefrom can achieve desired mechanical properties.

Abstract: The disclosure relates to an aluminum alloy and a component part prepared therefrom. The aluminum alloy comprises: 7-9 wt % of silicon (Si), 0.2-0.7 wt % of manganese (Mn), 0.09-0.4 wt % of iron (Fe), 0.1-0.3 wt % of vanadium (V), 0.1-0.2 wt % of titanium (Ti), 0.01-0.03 wt % of strontium (Sr), and the balance being aluminum and inevitable impurities, wherein the weight ratio of the manganese (Mn) to the iron (Fe) is not less than 1. The aluminum alloy of the disclosure can be exempt from heat treatment process after casting in the processing process, so as to contribute to energy conservation and emission reduction, and the component part prepared therefrom can achieve desired mechanical properties.