Abstract: The invention relates to a method of producing a binder comprising the steps of preparing (20) a residual material comprising amorphous alumina-rich and/or aluminium hydroxide-rich constituents, heating (30) the residual material to produce a fired material, the heating (30) of the residual material being at a temperature of >800° C.

Abstract: The invention relates to a method of producing a binder comprising the steps of preparing (20) a residual material comprising amorphous alumina-rich and/or aluminium hydroxide-rich constituents, heating (30) the residual material to produce a fired material, the heating (30) of the residual material being at a temperature of >800° C.

Abstract: The invention relates to the use of a hydraulic binder containing calcium aluminate, obtainable by a method in which a) prepared amorphous residual material rich in aluminium oxide and/or aluminium hydroxide is heated after the addition of a b) calcium ion-containing binder component and c) water, for the production of a constructing material.

Abstract: A quick-drying gypsum composition, in particular for use as gypsum filling compound and for the production of floor coverings, wherein the gypsum composition contains 20 to 70% of a mixture of calcium aluminate and calcium sulfate hemihydrate and/or anhydrite and/or calcium sulfate dihydrate as hydraulic binders and 30 to 80% by weight of fillers, and wherein the weight ratio of calcium aluminate to calcium sulfate hemihydrate and/or anhydrite and/or calcium sulfate dihydrate binders lies in the range from 1:1 to 1:5. Gypsum compositions of this type are characterized by a particularly beneficial shrinkage behavior, such that stresses and cracks in the dried composition can be avoided. At the same time, the gypsum compositions dry to readiness for covering in a time that is compatible with conventional cement filling compounds.

Abstract: A quick-drying gypsum composition, in particular for use as gypsum filling compound and for the production of floor coverings, wherein the gypsum composition contains 20 to 70% of a mixture of calcium aluminate and calcium sulfate hemihydrate and/or anhydrite and/or calcium sulfate dihydrate as hydraulic binders and 30 to 80% by weight of fillers, and wherein the weight ratio of calcium aluminate to calcium sulfate hemihydrate and/or anhydrite and/or calcium sulfate dihydrate binders lies in the range from 1:1 to 1:5. Gypsum compositions of this type are characterized by a particularly beneficial shrinkage behavior, such that stresses and cracks in the dried composition can be avoided. At the same time, the gypsum compositions dry to readiness for covering in a time that is compatible with conventional cement filling compounds.