Abstract: The present invention relates to aspartic acid ester-functional polysiloxanes, their use in the manufacture of curable compositions using polyisocyanate crosslinkers, in particular, in the manufacture of coating compositions, cured compositions obtained from said curable compositions and articles comprising the cured compositions.

Abstract: The present invention relates to aspartic acid ester-functional polysiloxanes, their use in the manufacture of curable compositions using polyisocyanate crosslinkers, in particular, in the manufacture of coating compositions, cured compositions obtained from said curable compositions and articles comprising the cured compositions.

Abstract: The present invention relates to an oil-bleed self-bonding liquid silicone rubber composition having both self-bonding and self-lubricating capabilities. The oil-bleed self-bonding liquid silicone rubber composition exhibits self-bonding capability in particular to substrates that contain residual hydroxyl groups or other residual hydrosilyl-reacting groups on their surface, including polycarbonate, polyester, polyamide, polysulfone, polyurethane, phenolic resin, epoxy resin, cellulose, glass and the mixture thereof.

Abstract: Disclosed herein are compositions, comprising linear polydiorganosiloxanes having enhanced reactivity and their use to prepare polydiorganosiloxane-polyorgano block copolymers.

Abstract: Disclosed herein are compositions, comprising linear polydiorganosiloxanes having enhanced reactivity and their use to prepare polydiorganosiloxane-polyorgano block copolymers.

Abstract: Disclosed herein is a process for preparing a linear hydroxyaryloxy-functional polydiorganosiloxanes having controlled structures. The process includes the step of reacting a linear ?,?-bisacyloxypolydiorganosiloxane with at least one bisphenolic compound, or hydroxy-functional oligomer thereof, in such a molar ratio that the phenolic groups in the bisphenolic compound or the hydroxy-functional oligomer thereof to the acyloxy groups in the ?,?-bisacyloxypolydiorganosiloxane is less than 2.0. Also disclosed are hydroxyaryloxy-functional polydiorganosiloxanes produced from the process and the polysiloxane/polyorgano block copolymers made using the hydroxyaryloxy-functional siloxanes.

Abstract: Disclosed herein is a process for the production of a polysiloxane-polyorgano block copolymer. The process includes reacting a reaction mixture containing (a) an ester-functional polydiorganosiloxane and (b) a bisphenolic compound or a bisphenolic compound oligomer. This process has the advantage of yielding block copolymers with controlled block structures and avoiding the impurities that may be carried over from the conventional hydroxyaryloxy-terminated-polydiorganosiloxanes.

Abstract: Disclosed herein is a process for preparing a linear hydroxyaryloxy-functional polydiorganosiloxanes having controlled structures. The process includes the step of reacting a linear ?,?-bisacyloxypolydiorganosiloxane with at least one bisphenolic compound, or hydroxy-functional oligomer thereof, in such a molar ratio that the phenolic groups in the bisphenolic compound or the hydroxy-functional oligomer thereof to the acyloxy groups in the ?,?-bisacyloxypolydiorganosiloxane is less than 2.0. Also disclosed are hydroxyaryloxy-functional polydiorganosiloxanes produced from the process and the polysiloxane/polyorgano block copolymers made using the hydroxyaryloxy-functional siloxanes.

Abstract: Disclosed herein is a process for the production of a polysiloxane-polyorgano block copolymer. The process includes reacting a reaction mixture containing (a) an ester-functional polydiorganosiloxane and (b) a bisphenolic compound or a bisphenolic compound oligomer. This process has the advantage of yielding block copolymers with controlled block structures and avoiding the impurities that may be carried over from the conventional hydroxyaryloxy-terminated-polydiorganosiloxanes. Also disclosed are ester-functional polysiloxanes and polysiloxane-polyorgano block copolymers prepared by the process of the invention. These copolymers exhibit advantageous properties such as improved low temperature properties, improved rheological properties during molding, improved clarity, chemical, scratch resistance, and improved electrical insulation properties.

Abstract: The invention relates to novel polyorganosiloxanes, methods for their preparation and their use, in particular as force and/or heat transmitting liquids, such as hydraulic liquids, and in cosmetic compositions.

Abstract: The present invention relates to novel processes for the manufacture of poly-organosiloxanes comprising (C6-C60)-alkylmethylsiloxy-groups and dimethyl-siloxy groups, polyorganosiloxanes obtainable by such processes, preferably aqueous emulsions comprising such polyorganosiloxanes and the use of such polyorganosiloxanes.

Abstract: Cosmetic formulations comprising alkyl-substituted siloxanes as vaporizable carriers.

Abstract: The invention relates to a process for manufacturing chlorosilanes, in which methyl-rich disilane, polysilane and siloxane residues from the Müller-Rochow synthesis or a chlorosilane synthesis are reduced in quantity. It comprises the steps: a) reaction of silicon with alkyl halogenides, aryl halogenides or hydrogen chloride, b) reaction of at least one high-boiling product fraction from step a) with at least one halogenide and c) reaction of at least one high-boiling product fraction resulting from step b) with alkyl halogenides, aryl halogenides and/or chlorosilanes.

Abstract: The invention relates to the use of siloxanes as vaporizable carriers, in particular to the use of siloxanes in cosmetic formulations, and to cleaning and care products, to processes for the preparation of the siloxanes, and to compositions comprising them.

Abstract: Process for the preparation of organofunctional polysiloxanes, which comprises reacting cyclic dialkylsiloxanes with at least one compound of the type HO—R′—X, wherein X═—OH, —COOH, —NR″2—, —CR″═CR″2, and R═alkyl, aryl, alkylene, oxyalkylene or arylene, in the presence of an equilibration catalyst.

Abstract: Novel liquid organopolysiloxane resins of the average composition[R.sup.1 Si(CH.sub.3).sub.2 O.sub.1/2 ].sub.a [(CH.sub.3).sub.3 SiO.sub.1/2 ].sub.b [R.sup.2 O.sub.1/2 ].sub.c [R.sup.1 Si(CH.sub.3)O].sub.d [(CH.sub.3).sub.2 SiO].sub.e [SiO.sub.2 ],whereinR.sup.1 is a C.sub.2 -C.sub.8 -alkenyl group,R.sup.2 is an optionally substituted, linear or branched C.sub.1 -C.sub.8 -alkyl group or a mixture thereof,a+b+c+d+e is about 1 to 6,d+e is about 0 to 3,the resin has a viscosity of 0.1 to 1000 Pas at 25.degree. C., andthe alkenyl or vinyl content of the resin is in the range of 0.4 to 4 mmol/g,and their preparation by reacting at least one of tetraalkoxysilane and its partial hydrolyzate with at least one organosiloxane and a strong acid as catalyst in the presence of water and optionally an organic solvent at a temperature of about >40.degree. C. They are formulated into novel low viscosity polydiorganosiloxane compositions.

Abstract: Novel liquid organopolysiloxane resins of the average composition ?R.sup.1 Si(CH.sub.3).sub.2 O.sub.1/2 !.sub.a ?(CH.sub.3).sub.3 SiO.sub.1/2 !.sub.b ?R.sup.2 O.sub.1/2 !.sub.c ?R.sup.1 Si(CH.sub.3)O!.sub.d ?(CH.sub.3).sub.2 SiO!.sub.e ?SiO.sub.2 !,whereinR.sup.1 is a C.sub.2 -C.sub.8 -alkenyl group,R.sup.2 is an optionally substituted, linear or branched C.sub.1 -C.sub.8 -alkyl group or a mixture thereof,a+b+c+d+e is about 1 to 6,d+e is about 0 to 3,the resin has a viscosity of 0.1 to 1000 Pas at 25.degree. C., andthe alkenyl or vinyl content of the resin is in the range of 0.4 to 4 mmol/g,and their preparation by reacting at least one of tetraalkoxysilane and its partial hydrolyzate with at least one organosiloxane and a strong acid as catalyst in the presence of water and optionally an organic solvent at a temperature of about >40.degree. C. They are formulated into novel low viscosity polydiorganosiloxane compositions.

Abstract: The present invention relates to novel polysiloxane-polyether-based copolymers which contain T units and comprise randomly linked organopolysiloxane units and linear polyether units, to a method for their preparation and their use.

Abstract: Siloxanes containing epoxy groups having the formula 1 ##STR1## Formula 1 whereinA means a C.sub.1 -C.sub.20 alkyl radical with epoxy groupsB means R.sup.1 or AR.sup.1, R.sup.2 independently of each other, means C.sub.1 -C.sub.20 alkyl or C.sub.6 -C.sub.10 aryla means zero or a whole number from 1-100b means zero or a whole number from 1-100c means a whole number from 1-5.