Abstract: Methods for improving hybrid bond yield for semiconductor wafers forming 3DIC devices includes first and second wafers having dummy and main metal deposited and patterned during BEOL processing. Metal of the dummy metal pattern occupies from about 40% to about 90% of the surface area of any given dummy metal pattern region. High dummy metal surface coverage, in conjunction with utilization of slotted conductive pads, allows for improved planarization of wafer surfaces presented for hybrid bonding. Planarized wafers exhibit minimum topographic differentials corresponding to step height differences of less than about 400 ?. Planarized first and second wafers are aligned and subsequently hybrid bonded with application of heat and pressure; dielectric-to-dielectric, RDL-to-RDL. Lithography controls to realize WEE from about 0.5 mm to about 1.5 mm may be employed to promote topographic uniformity at wafer edges.

Abstract: Methods for improving hybrid bond yield for semiconductor wafers forming 3DIC devices includes first and second wafers having dummy and main metal deposited and patterned during BEOL processing. Metal of the dummy metal pattern occupies from about 40% to about 90% of the surface area of any given dummy metal pattern region. High dummy metal surface coverage, in conjunction with utilization of slotted conductive pads, allows for improved planarization of wafer surfaces presented for hybrid bonding. Planarized wafers exhibit minimum topographic differentials corresponding to step height differences of less than about 400 ?. Planarized first and second wafers are aligned and subsequently hybrid bonded with application of heat and pressure; dielectric-to-dielectric, RDL-to-RDL. Lithography controls to realize WEE from about 0.5 mm to about 1.5 mm may be employed to promote topographic uniformity at wafer edges.

Abstract: Methods for improving hybrid bond yield for semiconductor wafers forming 3DIC devices includes first and second wafers having dummy and main metal deposited and patterned during BEOL processing. Metal of the dummy metal pattern occupies from about 40% to about 90% of the surface area of any given dummy metal pattern region. High dummy metal surface coverage, in conjunction with utilization of slotted conductive pads, allows for improved planarization of wafer surfaces presented for hybrid bonding. Planarized wafers exhibit minimum topographic differentials corresponding to step height differences of less than about 400 ?. Planarized first and second wafers are aligned and subsequently hybrid bonded with application of heat and pressure; dielectric-to-dielectric, RDL-to-RDL. Lithography controls to realize WEE from about 0.5 mm to about 1.5 mm may also be employed to promote topographic uniformity at wafer edges.