Abstract: A catalyst can be used for removing carbonyl sulfide in natural gas. The catalyst has a carrier, and an alkali metal oxide and nickel oxide which are loaded on the carrier. Based on the total weight of the catalyst, the content of the carrier is 90-97 wt %, the content of the alkali metal oxide is 2-6 wt %, and the content of the nickel oxide is 1-4 wt %. At least part of the carrier is AlO(OH), ?-Al2O3 and ?-Al2O3 phases. The catalyst can achieve a COS conversion rate of greater than or equal to 99% and a service life of 8 years or above, and can effectively reduce the content of carbonyl sulfur in natural gas.

Abstract: A molecular sieve complex contains an oxide of aluminum, an oxide of an alkaline earth metal and a rare earth-modified molecular sieve. The rare earth-modified molecular sieve is a molecular sieve doped by a rare earth element. The percentage of the pore volume occupied by pores of 3 nm or less to the total pore volume in the molecular sieve complex is greater than or equal to 63.5%. The content of the rare earth element and the contents of the oxide of aluminum, the oxide of the alkaline earth metal and the molecular sieve satisfy a certain relationship. The composite material contains a molecular sieve complex and an auxiliary agent loaded on the molecular sieve complex, and the composite material may be applied to flue gas adsorption and desulfurization.

Abstract: Preparation methods of a high modulus carbon fiber (HMCF) and a precursor (mesophase pitch (MP)) thereof are provided. The preparation method of MP includes: separating components with a molecular weight distribution (MWD) of 400 to 1,000 from a heavy oil raw material through size-exclusion chromatography (SEC); subjecting the components to ion-exchange chromatography (IEC) to obtain modified feedstock oil, where, the components are passed through macroporous cation-exchange and anion-exchange resins in sequence to remove acidic and alkaline components; and subjecting the modified feedstock oil to thermal polycondensation and carbonization to obtain high-quality MP with prominent spinnability. With high mesophase content, low softening point, low viscosity, and prominent meltability and spinnability, the obtained MP is a high-quality raw material for preparing HMCFs. The obtained MP can be subjected to melt spinning, pre-oxidation, carbonization, and graphitization to obtain an MP-based HMCF.