Abstract: A non-annealed hot-rolled ferritic stainless steel sheet with excellent impact toughness includes, in percent (%) by weight of the entire composition, C: more than 0 and 0.03% or less, Si: 0.1 to 0.5%, Mn: 1.5% or less, P: 0.04% or less, Cr: 10.5 to 14%, Ni: more than 0 and 1.5% or less, Ti: 0.01 to 0.5%, Cu: more than 0 and 1.0% or less, N: more than 0 and 0.015% or less, Al: 0.1% or less, the remainder of iron (Fe) and other inevitable impurities, and satisfies the following equation (1), and the average grain size of the cross-sectional microstructure in the direction perpendicular to the rolling direction is 60 ?m or less. (1500?(1001.5*C+950.6*Mn+1350.5*Ni+395.6*Cu?0.7*Si?1.0*Ti?0.1*Cr?1.0*P?1.0*Al+1020.5*N)?2200).??(1).

Abstract: The austenitic stainless steel that does not cause defects such as aging crack or delayed fracture even after the expansion and curling process of 5 steps or more is disclosed. In accordance with an aspect of the present disclosure, an austenitic stainless steel with excellent pipe expanding workability and aging crack resistance includes, in percent (%) by weight of the entire composition, C: 0.01 to 0.04%, Si: 0.1 to 1.0%, Mn: 0.1 to 2.0%, Cr: 16 to 20%, Ni: 6 to 10%, Cu: 0.1 to 2.0%, Mo: 0.2% or less, N: 0.035 to 0.07%, the remainder of iron (Fe) and other inevitable impurities, and the C+N satisfies 0.1% or less, the product of the Md30 (° C.) value and average grain size (?m) satisfies less than ?500.

Abstract: The austenitic stainless steel that does not cause defects such as aging crack or delayed fracture even after the expansion and curling process of 5 steps or more is disclosed. In accordance with an aspect of the present disclosure, an austenitic stainless steel with excellent pipe expanding workability and aging crack resistance includes, in percent (%) by weight of the entire composition, C: 0.01 to 0.04%, Si: 0.1 to 1.0%, Mn: 0.1 to 2.0%, Cr: 16 to 20%, Ni: 6 to 10%, Cu: 0.1 to 2.0%, Mo: 0.2% or less, N: 0.035 to 0.07%, the remainder of iron (Fe) and other inevitable impurities, and the C+N satisfies 0.1% or less, the product of the Md30 (° C.) value and average grain size (?m) satisfies less than ?500.

Abstract: A non-annealed hot-rolled ferritic stainless steel sheet with excellent impact toughness includes, in percent (%) by weight of the entire composition, C: more than 0 and 0.03% or less, Si: 0.1 to 0.5%, Mn: 1.5% or less, P: 0.04% or less, Cr: 10.5 to 14%, Ni: more than 0 and 1.5% or less, Ti: 0.01 to 0.5%, Cu: more than 0 and 1.0% or less, N: more than 0 and 0.015% or less, Al: 0.1% or less, the remainder of iron (Fe) and other inevitable impurities, and satisfies the following equation (1), and the average grain size of the cross-sectional microstructure in the direction perpendicular to the rolling direction is 60 ?m or less. (1500?(1001.5*C+950.6*Mn+1350.5*Ni+395.6*Cu?0.7*Si?1.0*Ti?0.1*Cr?1.0*P?1.0*Al+1020.5*N)?2200).

Abstract: A high-strength ferritic stainless steel for clamp includes, in percent (%) by weight of the entire composition, C: 0.04 to 0.1%, Si: 0.2 to 0.6%, Mn: 0.01 to 1.5%, Cr: 14.0 to 18.0%, Al: 0.005 to 0.2%, V: 0.005 to 0.2%, N: 0.02 to 0.1%, the remainder of iron (Fe) and other inevitable impurities, and satisfies following formulas (1) and (2), and the number of precipitates with an average diameter of 0.5 ?m or less is 2.5×106 pieces/mid or more: (1) 0.35%?Si+Al+V?0.6% and (2) 0.09%?C+N?0.12%.