Abstract: The present invention relates to a method for manufacturing a needle-shaped or rod-shaped porous iron powder. Specifically, the present invention provides a method for manufacturing a needle-shaped or rod-shaped porous iron and a needle-shaped or rod-shaped porous iron powder manufactured thereby, the method comprising the steps of: preparing a ferrous chloride dehydrate by concentrating a ferrous chloride aqueous solution; solid-liquid separating the ferrous dichloride to prepare ferrous chloride dehydrate powder; oxidizing the ferrous chloride dehydrate powder; and reducing the oxidized ferrous chloride powder.

Abstract: The present invention relates to a method for recovering nickel and cobalt from a nickel, iron, and cobalt-containing raw material. According to the present invention, high concentrations of valuable metals, such as nickel and cobalt, can be recovered from a raw material containing nickel, iron, and cobalt, and especially, the concentrations of nickel and cobalt are low and the concentration of iron is high, and thus when nickel is leached, and relatively large amount of iron is leached, whereas a small amount of nickel is leached. Therefore, the present invention can be more suitably applied in the smelting of nickel ore in which the separation of iron and nickel is difficult.

Abstract: An aspect of the present disclosure relates to a high strength magnesium alloy with excellent flame retardancy, wherein the magnesium alloy comprises 2.0-13.0 wt % of Al, 0.1-0.5 wt % of Mn, 0.0015-0.025 wt % of B, and 0.1-1.0 wt % of Y with the remainder comprising Mg and other unavoidable impurities, and comprises 6.5% or more of an Mg—Al intermetallic compound in terms of volume fraction, the Mg—Al intermetallic compound having an average grain size of 20-500 nm.