Abstract: A double oriented electrical steel sheet according to an exemplary embodiment of the present disclosure contains, in wt %, at least 2.0% of Si, more than 0% and 0.02% or less of AI, 0.02-0.50% of Mn, more than 0% and 0.004% or less of C, and 0.0005-0.005% of S, with the remainder comprising Fe and inevitable impurities, wherein the area percentage of grains having a grain size of 2000 ?m or less is 25% or less.

Abstract: A double-oriented electrical steel sheet according to an example of the present invention comprises, by weight 2.0 to 4.0 wt % of Si, 0.01 to 0.04 wt % of Al, 0.0004 to 0.02 wt % of S, 0.05 to 0.3 wt % of Mn, at most 0.01 wt % (exclusive of 0 wt %) of N, at most 0.005 wt % (exclusive of 0 wt %) of C, 0.005 to 0.15 wt % of P, 0.001 to 0.005 wt % of Ti, and 0.0001 to 0.005 wt % of Mg, with the balance being Fe and other inevitable impurities, wherein the area fraction of crystal grains having an orientation within 15° from {100}<001> is 60 to 99%, and the area fraction of crystal grains having an orientation within 15° from {100}<025> is 1 to 30%.

Abstract: In a double-oriented electrical steel sheet according to an embodiment of the present invention, the fraction of crystal grains having an orientation within 15° from {100}<001> is 50 to 75%, and the fraction of crystal grains having an orientation within 15° from {100}<380> is 50 to 75%.

Abstract: A non-oriented electrical steel sheet according to an embodiment of the present invention includes, in wt %, Si: 1.5% or less, C: 0.01% or less (excluding 0%), Mn: 0.03 to 3%, P: 0.01 to 0.2%, S: 0.001 to 0.02%, Al: 0.01% or less (excluding 0%), N: 0.005% or less (excluding 0%), Cu: 0.02 to 0.3%, 0.0001 to 0.005 wt % of Ca and Mg either alone or in total, 0.001 to 0.2 wt % of Sb and Sn either alone or in total, and a balance of Fe and inevitable impurities.