Abstract: Provided is a polychloroprene latex that shows favorable low-temperature stability without deterioration in the rubber agglutinating property during production of the dip-molded article, a rubber composition, and a dip-molded article, prepared by using the same. Prepared is a polychloroprene latex of a chloroprene copolymer obtained by polymerization of raw monomers at least containing chloroprene and 2,3-dichloro-1,3-butadiene, which is dispersed in water, wherein the 2,3-dichloro-1,3-butadiene content in the raw monomers is controlled to 1 to 30 mass % and the potassium ion content is adjusted to 0.7 to 1.5 parts by mass and the sodium ion content to 0.2 part or less by mass with respect to 100 parts by mass of the solid matter. In addition, a metal oxide: 1 to 10 parts by mass, sulfur: 0.1 to 3 parts by mass, an aging inhibitor: 0.1 to 5 parts by mass and a surfactant: 0.

Abstract: Provided are a polychloroprene latex giving a rubber-asphalt composition superior in low-temperature stability and film-forming property on the material to be coated, a rubber-asphalt composition and a utilization method thereof, a sheet, and a waterproof coating film. The rubber-asphalt composition includes a major agent containing 10 to 40 mass % of the anionic polychloroprene latex comprising potassium ions in an amount of 0.7 to 1.5 parts by mass and sodium ions in an amount of controlled to be 0.2 part by mass or less with respect to 100 parts by mass of the solid matter and 60 to 90 mass % of an anionic asphalt emulsion; and a coagulating agent of an aqueous solution containing a polyvalent metal salt as the principal component.

Abstract: Provided is a polychloroprene latex that shows favorable low-temperature stability without deterioration in the rubber agglutinating property during production of the dip-molded article, a rubber composition, and a dip-molded article, prepared by using the same. Prepared is a polychloroprene latex of a chloroprene copolymer obtained by polymerization of raw monomers at least containing chloroprene and 2,3-dichloro-1,3-butadiene, which is dispersed in water, wherein the 2,3-dichloro-1,3-butadiene content in the raw monomers is controlled to 1 to 30 mass % and the potassium ion content is adjusted to 0.7 to 1.5 parts by mass and the sodium ion content to 0.2 part or less by mass with respect to 100 parts by mass of the solid matter. In addition, a metal oxide: 1 to 10 parts by mass, sulfur: 0.1 to 3 parts by mass, an aging inhibitor: 0.1 to 5 parts by mass and a surfactant: 0.

Abstract: Provided are a polychloroprene latex giving a rubber-asphalt composition superior in low-temperature stability and film-forming property on the material to be coated, a rubber-asphalt composition and a utilization method thereof, a sheet, and a waterproof coating film. The rubber-asphalt composition includes a major agent containing 10 to 40 mass % of the anionic polychloroprene latex comprising potassium ions in an amount of 0.7 to 1.5 parts by mass and sodium ions in an amount of controlled to be 0.2 part by mass or less with respect to 100 parts by mass of the solid matter and 60 to 90 mass % of an anionic asphalt emulsion; and a coagulating agent of an aqueous solution containing a polyvalent metal salt as the principal component.

Abstract: Provided are a polychloroprene latex composition giving immersion-molded articles superior in releasability from the mold during immersion molding and also superior in flexibility, a production method thereof and a molded article prepared by using the same. A polychloroprene latex composition containing an alkyldiphenyletherdisulfonic acid alkali-metal salt in an amount of 0.01 to 1.0 part by mass with respect to 100 parts by mass of a polychloroprene latex is prepared by emulsion polymerization of the monomer in the presence of a rosin acid alkali-metal salt and an alkyldiphenyletherdisulfonic acid alkali-metal salt each in an amount of 3 parts or less by mass with respect to 100 parts by mass of the monomer.

Abstract: Provided are a polychloroprene latex composition giving immersion-molded articles superior in releasability from the mold during immersion molding and also superior in flexibility, a production method thereof and a molded article prepared by using the same. A polychloroprene latex composition containing an alkyldiphenyletherdisulfonic acid alkali-metal salt in an amount of 0.01 to 1.0 part by mass with respect to 100 parts by mass of a polychloroprene latex is prepared by emulsion polymerization of the monomer in the presence of a rosin acid alkali-metal salt and an alkyldiphenyletherdisulfonic acid alkali-metal salt each in an amount of 3 parts or less by mass with respect to 100 parts by mass of the monomer.