Abstract: An embodiment of the present invention provides a hot-rolled steel sheet comprising, by wt %, 0.06-0.12% of C, 0.004-0.4% of Si, 0.8-2.0% of Mn, 0.01-0.05% of Al, 0.05-1.0% of Cr, 0.001-0.3% of Mo, 0.001-0.05% of P, 0.001-0.005% of S, 0.001-0.01% of N, 0.001-0.05% of Nb, 0.001-0.05% of Ti, 0.001-0.005% of B, and the remainder of Fe and other inevitable impurities, satisfying relational formula 1 below, and having a microstructure including, by area, 80% or more of auto-tempered martensite, and a remainder of at least one of fresh martensite, bainite, and ferrite. [Relational formula 1] (10[C]+[Si]+2.5[Mn])/(1.5[Cr]+2.0[Mo]?3.

Abstract: A high-strength structural steel material having excellent fatigue crack propagation inhibitory characteristics according to an aspect of the present invention contains, by weight, 0.02-0.12% of C, 1.7-2.5% of Mn, 0.01-0.8% of Si, 0.005-0.5% of Al, and the balance Fe and unavoidable impurities, wherein a microstructure of the structural steel sheet material is divided into a surface layer portion outside and a central portion inside along a thickness direction; the surface layer portion comprises tempered bainite as a matrix structure, fresh martensite as a second structure, and austenite as a residual structure; and the central portion comprises lath bainite.

Abstract: A structural steel having excellent brittle crack propagation resistance, according to one aspect of the present invention, comprises, by wt %, 0.02-0.12% of C, 0.01-0.8% of Si, 1.7-2.5% of Mn, 0.005-0.5% of Al, and the balance of Fe and inevitable impurities, wherein an outer surface part and an inner center part thereof are microstructurally distinguished in the thickness direction, and the surface part comprises tempered bainite as a base structure, comprises fresh martensite as a second structure and can comprise austenite as a residual structure.

Abstract: A high-strength structural steel having excellent cold bendability, according to one embodiment of the present invention, comprises, by wt %, 0.02-0.1% of C, 0.01-0.6% of Si, 1.7-2.5% of Mn, 0.005-0.5% of Al, 0.02% or less of P, 0.01% or less of S, 0.0015-0.015% of N, and the balance of Fe and other inevitable impurities, wherein an outer surface layer part and an inner central part thereof are microstructurally divided in a thickness direction, the surface layer part can comprise tempered austenite as a matrix structure, and the central part can comprise bainitic ferrite as a matrix structure.

Abstract: A structural steel having excellent brittle fracture resistance according to an aspect of the present invention comprises, by weight %, 0.02-0.12% of C, 0.01-0.8% of Si, 1.5-2.5% of Mn, 0.005-0.5% of Al, 0.02% or less of P, 0.01% or less of S, 0.0015-0.015% of N, and the remainder of Fe and unavoidable impurities, wherein an outer surface layer portion and an inner central portion are microstructurally divided along the thickness direction, the surface layer portion comprises tempered bainite as a matrix structure, the central portion comprises bainitic ferrite as a matrix structure, and the NDT temperature by the NRL drop-weight test may be ?70° C. or lower.

Abstract: An aspect of the present invention relates to a high-strength and high-manganese steel having excellent low-temperature toughness, the high-strength and high-manganese steel comprising, in terms of wt %, 4.3-5.7% of manganese (Mn), 0.015-0.055% of carbon (C), 0.015-0.05% silicon (Si), 0.6-1.7% of aluminum (Al), 0.01-0.1% of niobium (Nb), 0.015-0.055% of titanium (Ti), 0.001-0.005% of boron (B), 0.03% or less of phosphor (P), 0.02% or less of sulfur (S), and the balance iron (Fe) and other inevitable impurities, wherein the microstructure thereof comprises, in terms of percent by volume, 40-60% of martensite and 40-60% of tempered martensite.

Abstract: A structural steel having excellent brittle crack propagation resistance, according to one aspect of the present invention, comprises, by wt %, 0.02-0.12% of C, 0.01-0.8% of Si, 1.7-2.5% of Mn, 0.005-0.5% of Al, and the balance of Fe and inevitable impurities, wherein an outer surface part and an inner center part thereof are microstructurally distinguished in the thickness direction, and the surface part comprises tempered bainite as a base structure, comprises fresh martensite as a second structure and can comprise austenite as a residual structure.

Abstract: A high-strength structural steel material having excellent fatigue crack propagation inhibitory characteristics according to an aspect of the present invention contains, by weight, 0.02-0.12% of C, 1.7-2.5% of Mn, 0.01-0.8% of Si, 0.005-0.5% of Al, and the balance Fe and unavoidable impurities, wherein a microstructure of the structural steel sheet material is divided into a surface layer portion outside and a central portion inside along a thickness direction; the surface layer portion comprises tempered bainite as a matrix structure, fresh martensite as a second structure, and austenite as a residual structure; and the central portion comprises lath bainite.

Abstract: An aspect of the present invention relates to a high-strength and high-manganese steel having excellent low-temperature toughness, the high-strength and high-manganese steel comprising, in terms of wt %, 4.3-5.7% of manganese (Mn), 0.015-0.055% of carbon (C), 0.015-0.05% silicon (Si), 0.6-1.7% of aluminum (Al), 0.01-0.1% of niobium (Nb), 0.015-0.055% of titanium (Ti), 0.001-0.005% of boron (B), 0.03% or less of phosphor (P), 0.02% or less of sulfur (S), and the balance iron (Fe) and other inevitable impurities, wherein the microstructure thereof comprises, in terms of percent by volume, 40-60% of martensite and 40-60% of tempered martensite.

Abstract: The present invention relates to a high hardness wear-resistant steel with excellent toughness and cutting crack resistance, and a method for manufacturing the same. A high hardness wear-resistant steel according to one aspect of the present invention has a composition containing, by weight ratio, 2.1 to 4.0% of manganese (Mn), 0.15 to 0.2% of carbon (C), 0.02 to 0.5% of silicon (Si), 0.2 to 0.7% of chromium (Cr), a remainder of iron (Fe) and other unavoidable impurities, has a microstructure in which prior austenite grain size is 25 ?m or less and martensite is included as a main phase, and has excellent toughness and cutting crack resistance which satisfies a condition in which Ac3-Ac1 is 100° C. or lower.

Abstract: The present invention relates to a wear resistant steel material which can be suitably used for industrial machinery, structural materials, steel materials for slurry pipes, sour steel materials, mining, transportation and storage fields, etc. in the oil gas industry which require properties such as ductility and wear resistance. More particularly, the present invention relates to a wear resistant steel material excellent in toughness and internal quality, and a method for manufacturing the same.