Abstract: Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more specifically, to a zinc alloy plated steel material having excellent surface quality and corrosion resistance, and a method for manufacturing the same.

Abstract: Provided are a hot-dip zinc plated steel material and a method for preparing same, the hot-dip zinc plated steel material comprising: base iron comprising 0.01-1.6 wt % of Si and 1.2-3.1 wt % of Mn; a Zn—Al—Mg alloy plating layer; and an Al-rich layer formed on the interface of the base iron and Zn—Al—Mg alloy plating layer, wherein the rate of occupied surface area of the Al-rich layer is 70% or higher (including 100%).

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: Provided is an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: A plated steel material includes a plated layer containing, by wt %: 0.5 to 14% of Al, 0.5 to 5% of Mg, and the balance being Zn and inevitable impurities. The plated steel material satisfies the following Equation: ([Mg]S?[Mg]1/2)/[Mg]1/2?0.3. [Mg]S means a content (wt %) of Mg in a surface of the plated layer, and [Mg]1/2 means a content (wt %) of Mg at a ½t position (t represents a thickness of the plated layer) from the surface of the plated layer in a thickness direction.

Abstract: Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more specifically, to a zinc alloy plated steel material having excellent surface quality and corrosion resistance, and a method for manufacturing the same.

Abstract: Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more particularly, to a zinc alloy plated steel material having excellent corrosion resistance after being processed and a method for manufacturing the same.

Abstract: Provided is an alloy-plated steel material that can be used in home appliances, automobiles, and construction materials and the like and, more particularly, to an alloy-plated steel material having excellent corrosion resistance and high surface quality.

Abstract: Provided is a method of manufacturing an HPF part comprising: preparing a steel sheet comprising C: 0.18% to 0.25%, Si: 0.1% to 1.0%, Mn: 0.9% to 1.5%, P: 0.03% or less, S: 0.01% or less, Al: 0.01% to 0.05%, Cr: 0.05% to 0.5%, Ti: 0.01% to 0.05%, B: 0.001% to 0.005%, N: 0.009% or less, and a balance of Fe and impurities; heating the steel sheet at 550° C. to 850° C. followed by maintaining at 640° C. to 680° C., and immersing the steel sheet in a hot dip aluminum plating bath, and a balance of Al and impurities; cooling the plated steel sheet at 15° C./s or faster; heating the cooled hot dip aluminum plated steel sheet at 880° C. to 930° C. followed by maintaining for a certain time; and hot forming the alloyed hot dip aluminum plated steel sheet and quenching at a range of 300° C. or lower at the same time.

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: An HPF molding member having a melted aluminum plating layer formed on the surface of a base steel sheet and excellent delamination resistance. The base steel sheet comprises: 0.18-0.25% by weight of C; 0.1-1.0% by weight of Si; 0.9-1.5% by weight of Mn; 0.03% by weight or less of P; 0.01% by weight or less of S; 0.01-0.05% by weight of Al; 0.05-0.5% by weight of Cr; 0.01-0.05% by weight of Ti; 0.001-0.005% by weight of B; 0.009% by weight or less of N; and the balance Fe and other impurities. The plating layer consists of a soft diffusion layer and a hard alloy layer, the hard alloy layer having a tau layer irregularly and non-continuously dispersed and distributed on the inside thereof at 10% or more of the entire area fraction. The difference in hardness between the alloy layer and the diffusion layer is 400 (Hv) or less.

Abstract: Provided is an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: An Al—Fe alloy coated steel sheet includes a base steel sheet and an alloy coating layer, wherein the base steel sheet includes, by wt %, C: 0.1%˜0.5%, Si: 0.01%˜2%, Mn: 0.01%˜10%, P: 0.001%˜0.05%, S: 0.0001%˜0.02%, Al: 0.001%˜1.0%, N: 0.001%˜0.02%, and the balance of Fe and other impurities, wherein the alloy coating layer includes: an Al—Fe alloy layer I formed on the base steel sheet and having a Vickers hardness of 200˜800 Hv; an Al—Fe alloy layer III formed on the Al—Fe alloy layer I and having a Vickers hardness of 700˜1200 Hv; and an Al—Fe alloy layer II formed in the Al—Fe alloy layer III continuously or discontinuously in a length direction of the steel sheet, and having a Vickers hardness of 400˜900 Hv, wherein an average oxygen content at a depth of 0.1 ?m from a surface of the oxide layer is 20% or less by weight.

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: Provided is a Zn—Al—Mg-based alloy-plated steel material that can be used in automobiles and home appliances and the like and, more particularly, to a Zn—Al—Mg-based alloy-plated steel material that can suppress the generation of cracks in a plating layer that are generated during processing.

Abstract: A plated steel material includes a plated layer containing, by wt %: 0.5 to 14% of Al, 0.5 to 5% of Mg, and the balance being Zn and inevitable impurities. The plated steel material satisfies the following Equation: ([Mg]S?[Mg]1/2)/[Mg]1/2?0.3. [Mg]S means a content (wt %) of Mg in a surface of the plated layer, and [Mg]1/2 means a content (wt %) of Mg at a ½t position (t represents a thickness of the plated layer) from the surface of the plated layer in a thickness direction.

Abstract: An Al—Fe alloy coated steel sheet includes a base steel sheet and an alloy coating layer, wherein the base steel sheet includes, by wt %, C: 0.1%˜0.5%, Si: 0.01%˜2%, Mn: 0.01%˜10%, P: 0.001%˜0.05%, S: 0.0001%˜0.02%, Al: 0.001%˜1.0%, N: 0.001%˜0.02%, and the balance of Fe and other impurities, wherein the alloy coating layer includes: an Al—Fe alloy layer I formed on the base steel sheet and having a Vickers hardness of 200˜800 Hv; an Al—Fe alloy layer III formed on the Al—Fe alloy layer I and having a Vickers hardness of 700˜1200 Hv; and an Al—Fe alloy layer II formed in the Al—Fe alloy layer III continuously or discontinuously in a length direction of the steel sheet, and having a Vickers hardness of 400˜900 Hv, wherein an average oxygen content at a depth of 0.1 ?m from a surface of the oxide layer is 20% or less by weight.

Abstract: Provided are a hot press-formed article and a method for manufacturing the same. The article is manufactured by hot press forming a galvanized steel sheet comprising a base steel plate and a zinc-based coat layer formed on a surface of the base steel plate, wherein the zinc-based coat layer contains at least one element selected from the group consisting of Sb, Sn, and Bi in a total amount of 0.05% to 2.0% by weight, and a balanced amount of Zn and inevitable impurities, at least 70% by weight of the at least one element selected from the group consisting of Sb, Sn, Bi being concentrated in a region 3 ?m or less distant from the surface of an alloyed zinc-based coat layer, formed by alloying the zinc-based coat layer, of the hot press-formed article.