Abstract: An exemplary etching composition includes about 0.1 to 8% by weight of hydrogen fluoride, about 10 to 25% by weight of ammonium fluoride, about 0.0001 to 3% by weight of a non-ionic polymer surfactant, and water. Using the composition in a wet etching process, an oxide layer may be selectively removed while a pattern or storage electrode including polysilicon may be effectively passivated. The oxide layer may be removed with a high etching selectivity, while at the same time minimizing damage to the polysilicon layer.

Abstract: A passivation layer pattern having an opening is formed on a substrate having a metal wiring pattern formed thereon. The opening partially exposes an upper surface of the metal wiring pattern. A photoresist pattern is formed on the passivation layer pattern. The photoresist pattern has an opening that exposes the opening of the passivation layer pattern, and metal is electroplated in the openings to form a bump electrode. The photoresist pattern is removed using a composition including monoethanolamine and dimethylacetamide.

Abstract: Monitoring metal contamination of a rinsing solution may include providing a sample of the rinsing solution, and mixing the sample of the rinsing solution with a monitoring reagent to provide a monitoring mixture. A property of the monitoring mixture that is dependent on a concentration of a metal in the rinsing solution may then be measured. More particularly, the property of the monitoring mixture may be an absorbency of the monitoring mixture with respect to electromagnetic radiation transmitted through the monitoring mixture. Related systems and reagents are also discussed.

Abstract: An exemplary etching composition includes about 0.1 to 8% by weight of hydrogen fluoride, about 10 to 25% by weight of ammonium fluoride, about 0.0001 to 3% by weight of a non-ionic polymer surfactant, and water. Using the composition in a wet etching process, an oxide layer may be selectively removed while a pattern or storage electrode including polysilicon may be effectively passivated. The oxide layer may be removed with a high etching selectivity, while at the same time minimizing damage to the polysilicon layer.

Abstract: A passivation layer pattern having an opening is formed on a substrate having a metal wiring pattern formed thereon. The opening partially exposes an upper surface of the metal wiring pattern. A photoresist pattern is formed on the passivation layer pattern. The photoresist pattern has an opening that exposes the opening of the passivation layer pattern, and metal is electroplated in the openings to form a bump electrode. The photoresist pattern is removed using a composition including monoethanolamine and dimethylacetamide.