Abstract: A molded, boron carbide-containing, sintered article which includes at least 65 percent by volume boron carbide; and from 5 to 35 percent by volume of at least one binder metal selected from the group consisting of molybdenum, molybdenum alloys, tungsten and tungsten alloys, having a melting point above 1,800.degree. C., and forming no molten borides or carbides within a temperature range of from 1,800.degree. to 1,950.degree. C. A method for producing the article includes the steps of mixing to obtain a homogeneous mixture from 20 to 80 percent by weight boron carbide particles having a particle size ranging from 1 to 1,650 microns with up to 80 percent by weight of particles of the at least one binder metal having a particle size ranging from 35 to 100 microns; introducing the homogeneous mixture into a graphite matrix mold; heating to sinter the homogeneous mixture at a temperature ranging from 1,800.degree. to 2,000.degree. C.