Abstract: Process for dealkylation of alkylaromatic compounds which process comprises contacting an alkylaromatic feedstock with i) a first catalyst comprising a) a carrier comprising of from 20 to 70 wt. % of refractory oxide binder and of from 30 to 80 wt. % of dealuminated ZSM-5 having a crystallite size of from 500 to 10,000 nm and a silica to alumina molar ratio (SAR) of from 20 to 100; b) of from 0.001 to 5 wt. % metal chosen from the group consisting of Groups 6, 9 and 10; and optionally c) up to 0.5 wt. % of a Group 14 metal, and ii) a subsequent catalyst comprising a) a carrier comprising of from 20 to 70 wt. % of refractory oxide binder and of from 30 to 80 wt. % of ZSM-5 having a crystallite size of from 3 to 100 nm and a SAR of from 20 to 200; b) of from 0.001 to 5 wt. % of metal chosen from the group consisting of Groups 6, 9 and 10; and optionally c) up to 0.5 wt. % of a Group 14 metal.

Abstract: A process for preparing a catalyst composition comprising (a) preparing a carrier comprising (i) mordenite in an amount in the range of from 20 to 80 wt %, based on total weight of carrier, (ii) ZSM-5 type zeolite in an amount in the range of from 10 to 70 wt %, based on total weight of carrier; and (iii) an inorganic binder in an amount in the range of from 10 to 50 wt %, based on total weight of carrier; (b) incorporating in the carrier molybdenum in an amount in the range of from 1 to 10 wt %, as metal based on total weight of catalyst composition, and subjecting the thus treated carrier to a temperature of from 100 to at most 300° C. and (c) incorporating in the molybdenum containing carrier obtained in step (b) platinum in an amount of from 0.005 to 1 wt %, as metal based on total weight of catalyst composition, and subjecting the thus treated carrier to a temperature of from 200 to at most 600° C.

Abstract: A process for preparing a catalyst composition comprising (a) preparing a carrier comprising (i) mordenite in an amount in the range of from 20 to 80 wt %, based on total weight of carrier, (ii) ZSM-5 type zeolite in an amount in the range of from 10 to 70 wt %, based on total weight of carrier; and (iii) an inorganic binder in an amount in the range of from 10 to 50 wt %, based on total weight of carrier; (b) incorporating in the carrier molybdenum in an amount in the range of from 1 to 10 wt %, as metal based on total weight of catalyst composition, and subjecting the thus treated carrier to a temperature of from 100 to at most 300° C. and (c) incorporating in the molybdenum containing carrier obtained in step (b) platinum in an amount of from 0.005 to 1 wt %, as metal based on total weight of catalyst composition, and subjecting the thus treated carrier to a temperature of from 200 to at most 600° C.

Abstract: A process for preparing an alkylaromatics isomerisation catalyst comprising at least 0.01% wt of platinum on a carrier comprising of from 1 to 9 wt % of ZSM-12 and inorganic binder, which process comprises treating the carrier with an impregnation solution comprising base and an anionic platinum complex which impregnation solution has a pH of from 5.5 to 8; and a process for the isomerisation of alkylaromatics with the help of catalyst thus obtained.

Abstract: Process for dealkylation of alkylaromatic compounds which process comprises contacting an alkylaromatic feedstock with i) a first catalyst comprising a) a carrier comprising of from 20 to 70 wt. % of refractory oxide binder and of from 30 to 80 wt. % of dealuminated ZSM-5 having a crystallite size of from 500 to 10,000 nm and a silica to alumina molar ratio (SAR) of from 20 to 100; b) of from 0.001 to 5 wt. % metal chosen from the group consisting of Groups 6, 9 and 10; and optionally c) up to 0.5 wt. % of a Group 14 metal, and ii) a subsequent catalyst comprising a) a carrier comprising of from 20 to 70 wt. % of refractory oxide binder and of from 30 to 80 wt. % of ZSM-5 having a crystallite size of from 3 to 100 nm and a SAR of from 20 to 200; b) of from 0.001 to 5 wt. % of metal chosen from the group consisting of Groups 6, 9 and 10; and optionally c) up to 0.5 wt. % of a Group 14 metal.

Abstract: A catalyst composition which comprises a) a carrier which comprises at least 30 wt % of a binder selected from silica, zirconia and titania; at least 20 wt % of a pentasil zeolite, having a bulk silica to alumina ratio in the range of from 20 to 150 and being in its H+ form; and less than 10 wt % of other components, all percentages being on the basis of total carrier; b) platinum in an amount in the range of from 0.001 to 0.1 wt %, on the basis of total catalyst; and c) tin in an amount in the range of from 0.01 to 0.5 wt %, on the basis of total catalyst; its preparation and use; are provided.

Abstract: An alkylaromatics isomerisation catalyst, which catalyst comprises at least 50 wt % of an inorganic binder; at least 0.01 wt % of a Group VIII metal and 1-9 wt % ZSM-12 zeolite wherein the silica to alumina molar ratio (SAR) of the ZSM-12 zeolite is in the range of from 60 to 200, and a process for the isomerisation of alkylaromatics to provide a reaction mixture, said process comprising contacting a hydrocarbon stream comprising alkylaromatics with such catalyst.

Abstract: A catalyst composition which comprises a) a carrier which comprises at least 30 wt % of a binder selected from silica, zirconia and titania; at least 20 wt % of a pentasil zeolite, having a bulk silica to alumina ratio in the range of from 20 to 150 and being in its H+ form; and less than 10 wt % of other components, all percentages being on the basis of total carrier; b) platinum in an amount in the range of from 0.001 to 0.1 wt %, on the basis of total catalyst; and c) tin in an amount in the range of from 0.01 to 0.5 wt %, on the basis of total catalyst; its preparation and use; are provided.

Abstract: A catalyst composition which comprises: a) a carrier which comprises at least 30 wt % of a binder selected from silica, zirconia and titania; at least 20 wt % of a pentasil zeolite, having a bulk silica to alumina ratio in the range of from 20 to 150 and being in its H+ form; and less than 10 wt % of other components, all percentages being on the basis of total carrier; b) platinum in an amount in the range of from 0.001 to 0.1 wt %, on the basis of total catalyst; and c) tin in an amount in the range of from 0.01 to 0.5 wt %, on the basis of total catalyst; its preparation and use; are provided.

Abstract: A process for preparing an alkylaromatics isomerisation catalyst comprising at least 0.01% wt of platinum on a carrier comprising of from 1 to 9 wt % of ZSM-12 and inorganic binder, which process comprises treating the carrier with an impregnation solution comprising base and an anionic platinum complex which impregnation solution has a pH of from 5.5 to 8; and a process for the isomerisation of alkylaromatics with the help of catalyst thus obtained.

Abstract: An alkylaromatics isomerisation catalyst, which catalyst comprises at least 50 wt % of an inorganic binder; at least 0.01 wt % of a Group VIII metal and 1-9 wt % ZSM-12 zeolite wherein the silica to alumina molar ratio (SAR) of the ZSM-12 zeolite is in the range of from 60 to 200, and a process for the isomerisation of alkylaromatics to provide a reaction mixture, said process comprising contacting a hydrocarbon stream comprising alkylaromatics with such catalyst.

Abstract: Method for impregnating a Group VIII metal on a molecular sieve—binder extrudate wherein the binder comprises a low acidity refractory oxide binder material, which is essentially free of alumina, by a) contacting the molecular sieve—binder extrudate with an aqueous solution of a corresponding Group VIII metal nitrate salt having a pH of below 8, wherein the molar ratio between the Group VIII metal cations in the solution and the number of sorption sites present in the extrudate is equal to or larger than 1, and b) drying the molecular sieve—binder extrudate obtained from step a).

Abstract: A method for the catalytic conversion of organic carbonate, wherein organic carbonate is contacted with alcohol and/or water in the presence of a lanthanum catalyst comprising at least about 7 wt. % of lanthanum supported on a support.

Abstract: Method for impregnating a Group VIII metal on a molecular sieve-binder extrudate wherein the binder comprises a low acidity refractory oxide binder material, which is essentially free of alumina, by

Abstract: Method for impregnating a Group VIII metal on a molecular sieve-binder extrudate wherein the binder comprises a low acidity refractory oxide binder material, which is essentially free of alumina, by a) contacting the molecular sieve-binder extrudate with an aqueous solution of a corresponding Group VIII metal nitrate salt having a pH of below 8, wherein the molar ratio between the Group VIII metal cations in the solution and the number of sorption sites present in the extrudate is equal to or larger than 1, and b) drying the molecular sieve-binder extrudate obtained from step a).

Abstract: A method for the catalytic conversion of organic carbonate, wherein organic carbonate is contacted with alcohol and/or water in the presence of a lanthanum catalyst comprising at least about 7 wt. % of lanthanum supported on a support.

Abstract: The present invention provides a catalyst comprising a very ultrastable zeolite Y (VUSY) in which less than 15% of the total amount of aluminum (Al) present is octahedrally coordinated; a process for preparing the zeolite; and a hydrocarbon conversion process using the catalyst.