Abstract: A casting method wherein casting cycles are continuously performed with respective molds and a common mass of molten metal accommodated in a container, such that in each casting cycle, the mold cavity is filled with the molten metal through a pouring tube connected at one end to a sprue hole of the mold and immersed at the other end in the molten metal mass, due to a difference between pressures to which the mold and the container are exposed, and wherein the molten metal temperature is estimated from the detected amount of consumption of the immersed tube, and the actual molten metal temperature is regulated, on the basis of a difference between a predetermined desired temperature of the molten metal, and the estimated temperature which changes with the actual temperature.

Abstract: Disclosed are a Ti--Al alloy including aluminum (Al) in an amount of 30 to 38% by weight, nitrogen (N) in an amount of 0.2 to 1.0% by weight, and titanium (Ti), substantially the balance, and a process for producing the same. Since the Ti--Al alloy includes the nitrogen in the predetermined amount, the microstructure of the Ti--Al alloy can be micro-fined and made into a uniform one, and accordingly the shrinkage cavities can be reduced remarkably. Therefore, the strength, the ductility or the like of the Ti--Al alloy can be improved remarkably. With the production process, it is possible to produce the Ti--Al alloy including the nitrogen in the predetermined range.

Abstract: Disclosed are a Ti-Al alloy including aluminum (Al) in an amount of 30 to 38% by weight, nitrogen (N) in an amount of 0.2 to 1.0% by weight, and titanium (Ti), substantially the balance, and a process for producing the same. Since the Ti-Al alloy includes the nitrogen in the predetermined amount, the microstructure of the Ti-Al ally can be micro-fined and made into a uniform one, and accordingly the shrinkage cavities can be reduced remarkably. Therefore, the strength, the ductility or the like of the Ti-Al alloy can be improved remarkably. With the production process, it is possible to produce the Ti-Al alloy including the nitrogen in the predetermined range.

Abstract: The container for use in the transporation of fresh provisions comprises a storage chamber for containing perishable foods and a machine room divided from each other by partition walls, main cold air flow channels opened at one end on the side of a door and auxiliary cold air flow channels closed at the other end on the side of the door, both of which are respectively disposed to the surface of the bottom wall, top wall or one side wall of the storage chamber, apparatus for blowing cold airs having ports perforated substantially over the entire region at the surface of the auxiliary cold air flow channels on the side of the storage chamber, apparatus disposed within the machine room for controlling the temperature of the recycled cold airs from the storage chamber and then supplying them by way of the main cold air flow channels to the inside of the storage chamber, and apparatus disopsed within the machine room for pressurizing the circulated cold airs from the storage chamber and then feeding them by way of

Abstract: A durable protective tube for a thermocouple having an extended serviceable life is obtained by covering a tubular preform of ceramic material with a refractory coating. The refractory coating is an alternate arrangement of one or more fine refractory layers of fine particulate refractory material having a particle size of 150 mesh to 500 mesh and one or more coarse refractory layers of coarse particulate refractory material having a particle size of 0.1 mm to 2.0 mm. The refractory coating is prepared by alternately applying a slurry of fine refractory particulates in a colloidal silica or ethyl silicate hydrolyzate binder and then coarse refractory particulates on the outer surface of the tubular preform followed by optional sintering.