Abstract: A quench solidification method, wherein a steel cast strip having a mean grain size 50 ?m or more is prepared and then the steel cast strip is rolled to produce a non-oriented electrical steel sheet having high magnetic flux density in both L and C directions. However the magnetic flux density reduces when the cold reduction rate exceeds 70%. To avoid this problem the non-oriented electrical steel sheet is manufactured with a ratio of at least 4 of the integrated intensity of the {100} plane for a given sample of steel to the integrated intensity of {100} plane for a “random” sample in which crystal grains have random orientations; and a cold reduction rate of the cold-rolling is between 70% and 85%. The superheating degree of the molten steel can be 70° C. or more.

Abstract: A cooling drum for metal cast strip by continuous casting has dimples 40 to 200 ?m in average depth and 0.5 to 3 mm in diameter of circle equivalent formed on a plated peripheral surface of the cooling drum, adjacent to each other at rims of the dimples; and a film, containing oxides of at least one member selected from the group consisting of Ni—W, Ni—Co—W, Cr, Ni—Fe and Ni—Al, is formed on the peripheral surface.

Abstract: Dimples, preferably 40 to 200 ?m in average depth and 0.5 to 3 mm in diameter of circle equivalent, are formed on the peripheral surface of a cooling drum, adjacent to each other at the rims of the dimples; and fine humps (preferably, fine humps 1 to 50 ?m in height and 5 to 200 ?m in diameter of circle equivalent on the surfaces of the dimples and/or fine humps 1 to 50 ?m in height and 30 to 200 ?m in diameter of circle equivalent at the rims of the dimples), fine holes (preferably, fine holes 5 ?m or more in depth and 10 to 200 ?m in diameter of circle equivalent), or fine unevenness (preferably, fine unevenness 1 to 50 ?m in average depth and 10 to 200 ?m in diameter of circle equivalent) are formed at the rims and/or on the indented surfaces of said dimples.

Abstract: Dimples, preferably 40 to 200 ?m in average depth and 0.5 to 3 mm in diameter of circle equivalent, are formed on the peripheral surface of a cooling drum, adjacent to each other at the rims of the dimples; and fine humps (preferably, fine humps 1 to 50 ?m in height and 5 to 200 ?m in diameter of circle equivalent on the surfaces of the dimples and/or fine humps 1 to 50 ?m in height and 30 to 200 ?m in diameter of circle equivalent at the rims of the dimples), fine holes (preferably, fine holes 5 ?m or more in depth and 10 to 200 ?m in diameter of circle equivalent), or fine unevenness (preferably, fine unevenness 1 to 50 ?m in average depth and 10 to 200 ?m in diameter of circle equivalent) are formed at the rims and/or on the indented surfaces of said dimples.

Abstract: A quench solidification method, wherein a steel cast strip having a mean grain size 50 &mgr;m or more is prepared and then the steel cast strip is rolled to produce a non-oriented electrical steel sheet having high magnetic flux density in both L and C directions. However the magnetic flux density reduces when the cold reduction rate exceeds 70%. To avoid this problem the non-oriented electrical steel sheet is manufactured with a ratio of at least 4 of the integrated intensity of the {100} plane for a given sample of steel to the integrated intensity of {100} plane for a “random” sample in which crystal grains have random orientations; and a cold reduction rate of the cold-rolling is between 70% and 85%. The superheating degree of the molten steel can be 70° C. or more.

Abstract: Dimples, preferably 40 to 200 &mgr;m in average depth and 0.5 to 3 mm in diameter of circle equivalent, are formed on the peripheral surface of a cooling drum, adjacent to each other at the rims of the dimples; and fine humps (preferably, fine humps 1 to 50 &mgr;m in height and 5 to 200 &mgr;m in diameter of circle equivalent on the surfaces of the dimples and/or fine humps 1 to 50 &mgr;m in height and 30 to 200 &mgr;m in diameter of circle equivalent at the rims of the dimples), fine holes (preferably, fine holes 5 &mgr;m or more in depth and 10 to 200 &mgr;m in diameter of circle equivalent), or fine unevenness (preferably, fine unevenness 1 to 50 &mgr;m in average depth and 10 to 200 &mgr;m in diameter of circle equivalent) are formed at the rims and/or on the indented surfaces of said dimples.

Abstract: A tortoise shell pattern having a circle equivalent diameter of 5 to 200 .mu.m surrounded by a dimple having a depth in the range of from 5 to 30 .mu.m is formed on the surface of a thin continuous cast plate for the purpose of preventing the occurrence of surface cracking of the cast plate. The tortoise shell pattern is formed by conducting casting while regulating the overheating temperature, .DELTA.T, of a molten metal in a pouring basin of a movable casting mold type continuous casting machine at 15.degree. C. or below.

Abstract: A cooling drum for continuous-casting machines, for manufacturing thin metallic strips, and having a surface composing part of a casting mold wall in contact with molten metal, wherein the surface has numerous dimples disposed uniformly thereon and not in contact with each other, and each of the dimples has an opening portion in the form of a circle or an oval with a diameter of from 0.1 to 1.2 mm and a depth of from 5 to 100 .mu.m.