Abstract: The present invention relates to a single step process for the synthesis of nanoparticles of phase pure ceramic oxides of a single or a multi-component system comprising one or more metal ions. The process comprises preparing a solution containing all the required metal ions in stoichiometric ratio by dissolving their respective soluble salts in an organic solvent or in water, preparing a precursor, adjusting the nitrate/ammonia content in the system, and heating the system.

Abstract: The present invention relates to a single step process for the synthesis of nanoparticles of phase pure ceramic oxides of a single or a multi-component system comprising one or more metal ions. The process comprises preparing a solution containing all the required metal ions in stoichiometric ratio by dissolving their respective soluble salts in an organic solvent or in water, preparing a precursor, adjusting the nitrate/ammonia content in the system, and heating the system.

Abstract: The present invention relates to a single step process for the synthesis of nanoparticles of phase pure ceramic oxides of a single or a multi-component system comprising one or more metal ions. The process comprises preparing a solution containing all the required metal ions in stoichiometric ratio by dissolving their respective soluble salts in an organic solvent or in water, preparing a precursor, adjusting the nitrate/ammonia content in the system, and heating the system.

Abstract: A novel ceramic substrate useful for the preparation of superconductors, said substrate having the formula Ba.sub.2 DyMO.sub.5.5 where M represents at least one of the metals Zr, Sn and Hf and a process for the preparation of said ceramic substrate, which comprises (i) Reacting salts of dysprosium, barium and Zr, Sn or Hf in an organic medium, (ii) Pressing the resultant mixture in the form of pellets, (iii) Calcining the pellets by heating at a temperature in the range of 1000 to 1200.degree. C., (iv) Repeating the calcination process for 30-45 h at temperature in the range of 1000-1200.degree. C. until a highly homogenous mixture is formed. (v) Grinding the calcined material and pelletising at a pressure in the range of 3 to 4 tons/cm.sup.2, (vi) Sintering the resultant product at a temperature in the range of 1200 to 1600.degree. C. for a period of 10 to 30 h, and then furnace cooled to room temperature.

Abstract: A novel ceramic substrate useful for the preparation of superconducting films, said substrate having the formula REBa.sub.2 MO.sub.6 where RE represents rare earth metals--Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and M represents metals Nb, Sb, Sn, Hf, Zr; and a process for the preparation of superconducting YBa.sub.2 Cu.sub.3 O.sub.7-.delta. thick films on new ceramic substrate.

Abstract: A novel ceramic substrate useful for the preparation of superconducting films, said substrate having the formula REBa.sub.2 MO.sub.6 where RE represents rare earth metals--Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and M represents metals Nb, Sb, Sn, Hf, Zr; and a process for the preparation of superconducting YBa.sub.2 Cu.sub.3 O.sub.7-.delta. thick films on new ceramic substrate.

Abstract: A novel ceramic substrate useful for the preparation of superconducting films, said substrate having the formula REBa.sub.2 MO.sub.6 where RE represents rare earth metals--Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and M represents metals Nb, Sb, Sn, Hf, Zr; and a process for the preparation of superconducting YBa.sub.2 Cu.sub.3 O.sub.7-.delta. thick films on new ceramic substrate.

Abstract: A novel ceramic substrate useful for the preparation of superconductors, said substrate having the formula Ba.sub.2 DyMO.sub.5.5 where M represents at least one of the metals Zr, Sn and Hf and a process for the preparation of said ceramic substrate, which comprises (i)Reacting salts of dysprosium, barium and Zr, Sn or Hf in an organic medium, (ii) Pressing the resultant mixture in the form of pellets, (iii)Calcining the pellets by heating at a temperature in the range of 1000.degree. to 1200.degree. C., (iv)Repeating the calcination process for 30-45 h at temperature in the range of 1000.degree.-1200.degree. C. until a highly homogenous mixture is formed, (v)Grinding the calcined material and pelletizing at a pressure in the range of 3 to 4 tons/cm.sup.2, (vi) Sintering the resultant product at a temperature in the range of 1200.degree. to 1600.degree. C. for a period of 10 to 30 h, and then furnace cooled to room temperature.