Abstract: The present invention relates to a flame retardant thermoplastic resin composition that contains a phenol resin derivative having good char formability, regardless of the base resin. A flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of a phenol resin derivative, and (C) about 0.1˜50 parts by weight of a phosphorous compound or a mixture of phosphorous compounds.

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that contains a phenol resin derivative having good char formability, regardless of the base resin. A flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of a phenol resin derivative, and (C) about 0.1˜50 parts by weight of a phosphoric acid ester morpholide compound or a mixture of phosphoric acid ester morpholide compounds. Another flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of polyphenylene ether, (C) about 0.1˜100 parts by weight of a phenol resin derivative, and (D) about 0.1˜50 parts by weight of a phosphoric acid ester morpholide compound or a mixture of phosphoric acid ester morpholide compounds.

Abstract: The present invention relates to a method for measuring the content of Lanthanides dissolved in uranium oxide, wherein the Lanthanides content in the nuclear fuel pellet is measured using the thermo gravimetric analysis which measures the weight variation caused by the oxidation and heat treatment of the nuclear fuel pellet. This method provides an advantage in that the Lanthanide content can be measured using relatively simple equipments such as an electric furnace and a balance.

Abstract: An apparatus for forming a thin film on a substrate includes a chamber having a gas inlet, an upper electrode in the chamber, the upper electrode having a plurality of nozzles, a lower electrode in the chamber for supporting the substrate thereon, the lower electrode being spaced apart from the upper electrode, and a selective injection plate above the upper electrode, the selective injection plate including a selective injection valve for selectively concentrating a gas supplied through the gas inlet onto a portion of the upper electrode.

Abstract: The present invention relates to a nuclear fuel body comprising tungsten network and a method for manufacturing the same, more particularly, a nuclear fuel body in which tungsten network is continuously formed over the entire or some parts of a sintered body and a method for manufacturing the same. The sintered body in the nuclear fuel body of the present invention contains tungsten network having excellent heat conductivity, leading to the enhancement of heat conductivity of the nuclear fuel sintered body itself with decreasing the temperature of the nuclear fuel, so that it can contribute to the improvement in safety and performance of nuclear fuel.

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that comprises (A) about 40 to 95 parts by weight of a rubber modified styrene-containing resin, (B) about 5 to 60 parts by weight of polyphenylene ether resin, (C) about 2 to 30 parts by weight of a styrene-containing copolymer resin having about 5 to 18 % by weight of acrylonitrile in the copolymer per 100 parts by weight of the sum of (A) and (B), (D) about 0.5 to 20 parts by weight of an oxaphospholane compound per 100 parts by weight of the sum of (A) and (B), and (E) about 0 to 30 parts by weight of a phosphoric acid ester compound per 100 parts by weight of the sum of (A) and (B).

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that contains a polyphenylene ether resin and a phenol resin derivative, both of them having good char formability, regardless of the base resin. A flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of polyphenylene ether, (C) about 0.1˜100 parts by weight of a phenol resin derivative, and (D) about 0.1˜50 parts by weight of a phosphorous compound or a mixture of phosphorous compounds. The thermoplastic resin composition may contain up to 5.0 parts by weight of an anti-dripping agent based on 100 parts by weight of the base resin.

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that contains a phenol resin derivative having good char formability, regardless of the base resin. A flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of a phenol resin derivative, and (C) about 0.1˜50 parts by weight of a phosphorous compound or a mixture of phosphorous compounds.

Abstract: The present invention relates to a flame retardant styrenic resin composition that comprises (A) about 5 to 95 parts by weight of a rubber modified styrene-containing resin; (B) about 95-5 parts by weight of polyphenylene ether; and (C) about 3-20 parts by weight of an oxaphospholane compound based on 100 parts by weight of the sum of (A) and (B). The resin composition of the present invention exhibits good flame resistance without the use of halogen flame retardant and does not emit harmful gases when burned.

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that contains a phenol resin derivative having good char formability, regardless of the base resin. A flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of a phenol resin derivative, and (C) about 0.1˜50 parts by weight of a phosphoric acid ester morpholide compound or a mixture of phosphoric acid ester morpholide compounds. Another flame retardant thermoplastic resin composition according to the present invention comprises (A) 100 parts by weight of a thermoplastic resin as a base resin, (B) about 0.1˜100 parts by weight of polyphenylene ether, (C) about 0.1˜100 parts by weight of a phenol resin derivative, and (D) about 0.1˜50 parts by weight of a phosphoric acid ester morpholide compound or a mixture of phosphoric acid ester morpholide compounds.

Abstract: The present invention relates to a nuclear fuel body comprising tungsten network and a method for manufacturing the same, more particularly, a nuclear fuel body in which tungsten network is continuously formed over the entire or some parts of a sintered body and a method for manufacturing the same. The sintered body in the nuclear fuel body of the present invention contains tungsten network having excellent heat conductivity, leading to the enhancement of heat conductivity of the nuclear fuel sintered body itself with decreasing the temperature of the nuclear fuel, so that it can contribute to the improvement in safety and performance of nuclear fuel.

Abstract: The present invention relates to a flame retardant styrenic resin composition that comprises (A) about 5 to 95 parts by weight of a rubber modified styrene-containing resin; (B) about 95-5 parts by weight of polyphenylene ether; and (C) about 3-20 parts by weight of an oxaphospholane compound based on 100 parts by weight of the sum of (A) and (B). The resin composition of the present invention exhibits good flame resistance without the use of halogen flame retardant and does not emit harmful gases when burned.

Abstract: The present invention relates to a method for measuring the content of Lanthanides dissolved in uranium oxide, wherein the Lanthanides content in the nuclear fuel pellet is measured using the thermo gravimetric analysis which measures the weight variation caused by the oxidation and heat treatment of the nuclear fuel pellet. This method provides an advantage in that the Lanthanide content can be measured using relatively simple equipments such as an electric furnace and a balance.

Abstract: The present invention relates to a flame retardant thermoplastic resin composition that comprises (A) about 40 to 95 parts by weight of a rubber modified styrene-containing resin, (B) about 5 to 60 parts by weight of polyphenylene ether resin, (C) about 2 to 30 parts by weight of a styrene-containing copolymer resin having about 5 to 18 % by weight of acrylonitrile in the copolymer per 100 parts by weight of the sum of (A) and (B), (D) about 0.5 to 20 parts by weight of an oxaphospholane compound per 100 parts by weight of the sum of (A) and (B), and (E) about 0 to 30 parts by weight of a phosphoric acid ester compound per 100 parts by weight of the sum of (A) and (B).