Abstract: The composition for forming a non-flammable coating comprising (a) 50.4-64.8 wt % of at least one type of a binder resin selected from aqueous or waterborne acrylic resin and aqueous or waterborne vinyl resin; (b) 19.6-25.2 wt % of water; (c) 6-26 wt % of expanded graphite; and (d) 2-4 wt % of kerosene and a non-flammable coating obtained from the composition are disclosed herein. The composition for forming a non-flammable coating according to the invention is superior in terms of drying rate and long-term storage properties, and this composition can be used to form a dense non-flammable coating of a resin-expanded graphite composite on the surface of a base easily so that the non-flammable coating with superior water resistance, heat resistance and mechanical strength may be formed.

Abstract: The composition for forming a non-flammable coating comprising (a) 50.4-64.8 wt % of at least one type of a binder resin selected from aqueous or waterborne acrylic resin and aqueous or waterborne vinyl resin; (b) 19.6-25.2 wt % of water; (c) 6-26 wt % of expanded graphite; and (d) 2-4 wt % of kerosene and a non-flammable coating obtained from the composition are disclosed herein. The composition for forming a non-flammable coating according to the invention is superior in terms of drying rate and long-term storage properties, and this composition can be used to form a dense non-flammable coating of a resin-expanded graphite composite on the surface of a base easily so that the non-flammable coating with superior water resistance, heat resistance and mechanical strength may be formed.