Abstract: An aqueous emulsion copolymer of monoethylenically unsaturated monomers which provide a copolymer having a glass transition temperature below 20.degree. C., is modified to include from about 0.3% to about 10% of a monoethylenically unsaturated copolymerizable polyether containing a chain of from about 6 to about 150 C.sub.2 -C.sub.4 oxyalkylene groups, the terminal hydroxy group provided by said chain of oxyalkylene groups being capped with a monofunctional hydrophobic group. These polyethers improve the brush drag of paints made with the emulsion copolymers, and in some instances the leveling is simultaneously improved.

Abstract: Alkali soluble thickeners are disclosed which are aqueous emulsion copolymers of:(A) about 20-70 weight percent of an alpha, beta-monoethylenically unsaturated carboxylic acid, typically methacrylic acid;(B) about 20-80 weight percent of a monoethylenically unsaturated monomer lacking surfactant capacity, typically ethyl acrylate;(C) about 0.5-60 weight percent of a nonionic urethane monomer which is the urethane reaction product of a monohydric nonionic surfactant with a monoethylenically unsaturated monoisocyanate, preferably one lacking ester groups like alpha, alpha-dimethyl-m-isopropenyl benzyl isocyanate; and(D) from 0 up to about 2 weight percent of a polyethylenically unsaturated monomer. These emulsion copolymers are solubilized in water with the aid of an alkali, like ammonium hydroxide. When the copolymers are added to latex paints and neutralized, the viscosity of the paint is increased, brush drag is increased, and the paint rheology is otherwise improved.

Abstract: Alkali soluble thickeners are disclosed which are aqueous emulsion copolymers of:(A) about 20-70 weight percent of an alpha, beta-monoethylenically unsaturated carboxylic acid, typically methacrylic acid,(B) about 20-80 weight percent of a monoethylenically unsaturated monomer lacking surfactant capacity, typically ethyl acrylate;(C) about 0.5-60 weight percent of a nonionic urethane monomer which is the urethane reaction product of a monohydric nonionic surfactant with a monoethylenically unsaturated monoisocyanate, preferably one lacking ester groups like alpha, alpha-dimethyl-m-isopropenyl benzyl isocyanate; and(D) from 0 up to about 2 weight percent of a polyethylenically unsaturated monomer. These emulsion copolymers are solubilized in water with the aid of an alkali, like ammonium hydroxide. When the copolymers are added to latex paints and neutralized, the viscosity of the paint is increased, brush drag is increased, and the paint rheology is otherwise improved.