Abstract: Flexible hydrogenated block copolymers can be successfully used in a variety of applications including films, profiles, sheets, coatings, injection molded articles, blow or rotational molded articles and pultruded articles.

Abstract: Compositions comprising hydrogenated block copolymers can be successfully used in a variety of applications including films, profiles, sheets, pultruded articles, fibers, coated articles, injection molded articles and blow or rotational molded articles.

Abstract: The present invention provides a process for preparing a stable dispersion of a preformed polymer in a polyol in a single mixer. A preformed polymer is mixed under sufficient heat and shear to reduce its particle size to a desired size in the presence of a polyol. The present invention also provides stable dispersions of polymers in polyols and polyurethane formulations containing stable dispersions made by the process of the present invention.

Abstract: Stable aqueous dispersions or emulsions can be prepared by merging into a mechanical disperser a stream of a molten or liquid disperse phase with a stream of a molten or liquid continuous phase to form a dispersion or emulsion. The molten or liquid disperse phase stream contains a polymer that is preferably a solid at room temperature, but molten at some advanced temperature. The polymer is formed in a molten state or formed and melted by a continuous reaction process such as an extrusion process, including melt extrusion or compound extrusion. It has been discovered that low polydisperse submicron sized dispersion can be prepared by the method of the present invention.

Abstract: A polyurethane/urea/thiourea latex having a narrow molecular weight polydispersity and sub-micron particle size can be prepared by first preparing a high internal phase ratio (HIPR) emulsion of a polyurethane/urea/thiourea prepolymer, then contacting the emulsion with a chain-extending reagent under such conditions to form the polymer latex.

Abstract: The present invention is a method of preparing a high internal phase ratio emulsion without phase inversion comprising the steps of:a) continuously merging into a disperser and in the presence of an emulsifying and a stabilizing amount of a surfactant, a continuous phase liquid stream having a flow rate R.sub.1, and a disperse phase liquid stream having a flow rate R.sub.2 ; andb) mixing the merged streams with a sufficient amount of shear, and with R.sub.2 :R.sub.1 sufficiently constant, to form the high internal phase ratio emulsion without phase inversion or stepwise distribution of an internal phase into an external phase;wherein R.sub.2 :R.sub.1 encompasses a range, the lower limit of which range being defined by a point where the volume average particle size of the high internal phase ratio emulsion begins to show an inverse dependence on R.sub.2 :R.sub.1, and wherein the upper limit of which range is just less than an R.sub.2 :R.sub.