Abstract: An aircraft transparency in a glass piece, wherein the glass piece includes a chemically tempered first major surface and a chemically tempered opposite second major surface, a first case depth begins at the first major surface, a second case depth begins at the second major surface, and a tensile stress zone is within the glass piece between the end points of the first and the second case depths. The glass between the end points of the first and second case depth has a glass composition including: Ingredient Percent by weight SiO2 60 to 75; Al2O3 18 to 28; and Li2O 3 to 9, and the glass has at least one of the following properties (a) a log 10 viscosity temperature of at least 1413° F. and (b) a liquidus temperature of at least 2436° F.

Abstract: A glass composition for chemical tempering includes oxides in wt % ranges of: SiO2 60 to 75; Al2O3 18 to 28; Li2O 3 to 9; Na2O 0 to 3; K2O 0 to 0.5; CaO 0 to 3; MgO 0 to 3; ZrO2 0 to 3; where MgO+CaO is 0 to 6 wt %; Al2O3+ZrO2 is 18 to 28 wt %, and Na2O+K2O is 0.05 to 3.00 wt %. The glass has a log 10 viscosity temperature in the temperature range of 1328° F. (720° C.) to 1499° F. (815° C.); a liquidus temperature in the temperature range of 2437° F. (1336° C.) to 2575° F. (1413° C.), and a log 7.6 softening point temperature in the temperature range of 1544° F. (840° C.) to 1724° F. (940° C.). The chemically tempered glass has, among other properties, an abraded modulus of rupture of 72 to 78 KPSI, and a modulus of rupture of 76 to 112 KPSI.

Abstract: A glass composition for chemical tempering includes oxides in wt % ranges of: SiO2 60 to 75; Al2O3 18 to 28; Li2O 3 to 9; Na2O 0 to 3; K2O 0 to 0.5; CaO 0 to 3; MgO 0 to 3; ZrO2 0 to 3; where MgO+CaO is 0 to 6 wt %; Al2O3+ZrO2 is 18 to 28 wt %, and Na2O+K2O is 0.05 to 3.00 wt %. The glass has a log 10 viscosity temperature in the temperature range of 1328° F. (720° C.) to 1499° F. (815° C.); a liquidus temperature in the temperature range of 2437° F. (1336° C.) to 2575° F. (1413° C.), and a log 7.6 softening point temperature in the temperature range of 1544° F. (840° C.) to 1724° F. (940° C.). The chemically tempered glass has, among other properties, an abraded modulus of rupture of 72 to 78 KPSI, and a modulus of rupture of 76 to 112 KPSI.

Abstract: An aircraft transparency in a glass piece, wherein the glass piece includes a chemically tempered first major surface and a chemically tempered opposite second major surface, a first case depth begins at the first major surface, a second case depth begins at the second major surface, and a tensile stress zone is within the glass piece between the end points of the first and the second case depths. The glass between the end points of the first and second case depth has a glass composition including: Ingredient Percent by weight SiO2 60 to 75; Al2O3 18 to 28; and Li2O 3 to 9, and the glass has at least one of the following properties (a) a log 10 viscosity temperature of at least 1413° F. and (b) a liquidus temperature of at least 2436° F.

Abstract: A glass composition for chemical tempering includes oxides in wt % ranges of: SiO2 60 to 75; Al2O3 18 to 28; Li2O 3 to 9; Na2O 0 to 3; K2O 0 to 0.5; CaO 0 to 3; MgO 0 to 3; ZrO2 0 to 3; where MgO+CaO is 0 to 6 wt %; Al2O3+ZrO2 is 18 to 28 wt %, and Na2O+K2O is 0.05 to 3.00 wt %. The glass has a log 10 viscosity temperature in the temperature range of 1328° F. (720° C.) to 1499° F. (815° C.); a liquidus temperature in the temperature range of 2437° F. (1336° C.) to 2575° F. (1413° C.), and a log 7.6 softening point temperature in the temperature range of 1544° F. (840° C.) to 1724° F. (940° C.). The chemically tempered glass has, among other properties, an abraded modulus of rupture of 72 to 78 KPSI, and a modulus of rupture of 76 to 112 KPSI.

Abstract: A glass composition that includes a base glass composition including: SiO2 from 65 to 75 weight percent, Na2O from 10 to 20 weight percent, CaO from 5 to 15 weight percent, MgO from 0 to 5 weight percent, Al2O3 from 0 to 5 weight percent, K2O from 0 to 5 weight percent and BaO 0 to 1 weight percent, and a colorant and property modifying portion including total iron from 0.25 to 0.9 weight percent, Cr2O3 from 6 PPM to 400 PPM, Er2O3 from 0.3 to 3.0 weight percent, and TiO2 from 0.1 to 0.8 weight percent, wherein the glass composition has a redox ratio ranging from 0.15 to 0.62.

Abstract: The present invention provides a blue glass that can be essentially free of selenium and cobalt but still has a blue color and desired luminous transmittance. Additionally, the amount of iron present is comparable to conventional soda-lime-silica glass. The glass of the present invention can have a soda-lime-silica glass base portion, with major colorants that provide the blue color.

Abstract: A glass composition for chemical tempering includes oxides in wt % ranges of: SiO2 60 to 75; Al2O3 18 to 28; Li2O 3 to 9; Na2O 0 to 3; K2O 0 to 0.5; CaO 0 to 3; MgO 0 to 3; ZrO2 0 to 3; where MgO+CaO is 0 to 6 wt %; Al2O3+ZrO2 is 18 to 28 wt %, and Na2O+K2O is 0.05 to 3.00 wt %. The glass has a log 10 viscosity temperature in the temperature range of 1328° F. (720° C.) to 1499° F. (815° C.); a liquidus temperature in the temperature range of 2437° F. (1336° C.) to 2575° F. (1413° C.), and a log 7.6 softening point temperature in the temperature range of 1544° F. (840° C.) to 1724° F. (940° C.). The chemically tempered glass has, among other properties, an abraded modulus of rupture of 72 to 78 KPSI, and a modulus of rupture of 76 to 112 KPSI.

Abstract: The present invention provides a method of producing patterned and/or textured glass by applying a material onto at least a portion of a glass substrate, e.g., a float glass ribbon, at or above a softening point of the material and/or the glass substrate. The material is configured to affect the surface of the glass substrate to scatter light rays. An apparatus of the invention for forming patterned glass in a float glass process includes an applicator extensible into and out of a float bath chamber above a molten metal bath. A glass article of the invention includes a first surface and a second surface spaced from the first surface. The second surface includes a patterned portion configured to scatter light rays.