Abstract: This disclosure generally relates to high-volume and cost-effective methods for producing non-spherical metal particles, particularly methods for producing metal cubes having rounded edges. The metal cubes having rounded edges are useful as ballistic shot in shotshell loads for hunting, where the particle shape imparted by the disclosed process packs to a higher density than spherical shot in the same volume.

Abstract: This disclosure generally relates to high-volume and cost-effective methods for producing non-spherical metal particles, particularly methods for producing metal cubes having rounded edges. The metal cubes having rounded edges are useful as ballistic shot in shotshell loads for hunting, where the particle shape imparted by the disclosed process packs to a higher density than spherical shot in the same volume.

Abstract: This disclosure generally relates to high-volume and cost-effective methods for producing non-spherical metal particles, particularly methods for producing metal cubes having rounded edges. The metal cubes having rounded edges are useful as ballistic shot in shotshell loads for hunting, where the particle shape imparted by the disclosed process packs to a higher density than spherical shot in the same volume.

Abstract: In making frangible objects, including lead-free bullets and other projectiles, powdered metal primary and powdered ceramic secondary phases are mixed and densified at an elevated temperature such that the ceramic phase forms a brittle network. Any combination of metal and ceramic phases may be used to achieve desired chemical and physical properties. Any appropriate mixing, forming, and/or thermal processing methods and equipment may be used. Degrees of frangibility, strength, and toughness can be adjusted to suit a given application by precursor selection, degree of mixing, relative amounts of metal and ceramic phases, forming method, and thermal and mechanical processing parameters.

Abstract: In making frangible objects, including lead-free bullets and other projectiles, powdered metal primary and powdered ceramic secondary phases are mixed and densified at an elevated temperature such that the ceramic phase forms a brittle network. Any combination of metal and ceramic phases may be used to achieve desired chemical and physical properties. Any appropriate mixing, forming, and/or thermal processing methods and equipment may be used. Degrees of frangibility, strength, and toughness can be adjusted to suit a given application by precursor selection, degree of mixing, relative amounts of metal and ceramic phases, forming method, and thermal and mechanical processing parameters.