Abstract: This invention provides a new dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin with excellent heat resistance, low dielectric constant Dk, low dissipation factor Df having the formula 1. Preparation of dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin in two steps: Step 1, reacting (a1) dicyclopentadiene phenol resin represented by formula 2 with (a2) 2,6-dimethyl phenol in the presence of acid catalyst by (a3) aldehyde compounds to synthesize dicyclopentadiene phenol-2,6-dimethyl phenol copolymer, and Step 2, reacting dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer with excess epichlorhydrin under NaOH condition to prepare dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin.

Abstract: The invention provides a polyphenylene ether modified phenol-benzaldehyde multifunctional epoxy resin with formula (I) wherein A is: PPE are: Z are: Y are: Their manufactured is following steps: polyphenylene ether 100 parts is dissolved in solvent, then phenol-benzaldehyde multifunctional epoxy resin 100˜450 parts and catalyst 0.01˜5 parts are added, stirred and mixed at 90˜180, for 1˜4 hour, to obtain formula (I) solution. Said product is formulated with compositions for laminate, having excellent electrical properties and heat resistance. The dielectric constant is 4.03(1 GHz), dissipation factor is 0.0046(1 GHz) and no delamination longer than 60 minutes dipping in 288 soldering test after 2 hours pressure cooking test. Application is insulating materials for highly reliable electronic components such as EMC, PCB substrates, laminate and insulating plates.

Abstract: This invention provides a new dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin with excellent heat resistance, low dielectric constant Dk, low dissipation factor Df having the formula 1. Preparation of dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin in two steps: Step 1, reacting (a1) dicyclopentadiene phenol resin represented by formula 2 with (a2) 2,6-dimethyl phenol in the presence of acid catalyst by (a3) aldehyde compounds to synthesize dicyclopentadiene phenol-2,6-dimethyl phenol copolymer, and Step 2, reacting dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer with excess epichlorhydrin under NaOH condition to prepare dicyclopentadiene phenol and 2,6-dimethyl phenol copolymer epoxy resin.

Abstract: The invention provides a polyphenylene ether modified phenol-benzaldehyde multifunctional epoxy resin with formula (I). wherein A is: PPE are: Z are: Y are: Their manufactured is following steps: polyphenylene ether 100 parts is dissolved in solvent, then phenol-benzaldehyde multifunctional epoxy resin 100˜450 parts and catalyst 0.01˜5 parts are added, stirred and mixed at 90˜180?, for 1˜4 hour, to obtain formula (I) solution. Said product is formulated with compositions for laminate, having excellent electrical properties and heat resistance. The dielectric constant is 4.03 (1 GHz), dissipation factor is 0.0046 (1 GHz) and no delamination longer than 60 minutes dipping in 288 soldering test after 2 hours pressure cooking test. Application is insulating materials for highly reliable electronic components such as EMC, PCB substrates, laminate and insulating plates.