Abstract: Methods of forming a film stack may include the plasma accelerated deposition of a silicon nitride film formed from the reaction of nitrogen containing precursor with silicon containing precursor, the plasma accelerated substantial elimination of silicon containing precursor from the processing chamber, the plasma accelerated deposition of a silicon oxide film atop the silicon nitride film formed from the reaction of silicon containing precursor with oxidant, and the plasma accelerated substantial elimination of oxidant from the processing chamber. Process station apparatuses for forming a film stack of silicon nitride and silicon oxide films may include a processing chamber, one or more gas delivery lines, one or more RF generators, and a system controller having machine-readable media with instructions for operating the one or more gas delivery lines, and the one or more RF generators.

Abstract: The present invention provides improved methods of preparing a low-k dielectric material on a substrate. The methods involve multiple operation ultraviolet curing processes in which UV intensity, wafer substrate temperature, UV spectral distribution, and other conditions may be independently modulated in each operation. Operations may be pulsed or even be concurrently applied to the same wafer. In certain embodiments, a film containing a structure former and a porogen is exposed to UV radiation in a first operation to facilitate removal of the porogen and create a porous dielectric film. In a second operation, the film is exposed to UV radiation to increase cross-linking within the porous film.

Abstract: Methods for depositing film stacks by plasma enhanced chemical vapor deposition are described. In one example, a method for depositing a film stack on a substrate, wherein the film stack includes films of different compositions and the deposition is performed in a process station in-situ, is provided. The method includes, in a first plasma-activated film deposition phase, depositing a first layer of film having a first film composition on the substrate; in a second plasma-activated deposition phase, depositing a second layer of film having a second film composition on the first layer of film; and sustaining the plasma while transitioning a composition of the plasma from the first plasma-activated film deposition phase to the second plasma-activated film deposition phase.

Abstract: Disclosed herein are methods of forming a film stack which may include the plasma accelerated deposition of a silicon nitride film formed from the reaction of nitrogen containing precursor with silicon containing precursor, the plasma accelerated substantial elimination of silicon containing precursor from the processing chamber, the plasma accelerated deposition of a silicon oxide film atop the silicon nitride film formed from the reaction of silicon containing precursor with oxidant, and the plasma accelerated substantial elimination of oxidant from the processing chamber. Also disclosed herein are process station apparatuses for forming a film stack of silicon nitride and silicon oxide films which may include a processing chamber, one or more gas delivery lines, one or more RF generators, and a system controller having machine-readable media with instructions for operating the one or more gas delivery lines, and the one or more RF generators.

Abstract: Methods and hardware for depositing film stacks in a process tool in-situ (i.e., without a vacuum break or air exposure) are described. In one example, a method for depositing, on a substrate, a film stack including films of different compositions in-situ in a process station using a plasma is described, the method including, in a first plasma-activated film deposition phase, depositing a first layer of film having a first film composition on the substrate; in a second plasma-activated deposition phase, depositing a second layer of film having a second film composition on the first layer of film; and sustaining the plasma while transitioning a composition of the plasma from the first plasma-activated film deposition phase to the second plasma-activated film deposition phase.