Patents by Inventor Jason Michael Rycroft
Jason Michael Rycroft has filed for patents to protect the following inventions. This listing includes patent applications that are pending as well as patents that have already been granted by the United States Patent and Trademark Office (USPTO).
-
Publication number: 20230038732Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: ApplicationFiled: July 7, 2022Publication date: February 9, 2023Applicant: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Patent number: 11414538Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: GrantFiled: March 5, 2020Date of Patent: August 16, 2022Assignee: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Publication number: 20200199338Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: ApplicationFiled: March 5, 2020Publication date: June 25, 2020Applicant: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Patent number: 10626258Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: GrantFiled: February 19, 2018Date of Patent: April 21, 2020Assignee: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Publication number: 20180171126Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: ApplicationFiled: February 19, 2018Publication date: June 21, 2018Applicant: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Patent number: 9932466Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: GrantFiled: April 6, 2016Date of Patent: April 3, 2018Assignee: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Publication number: 20160222199Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: ApplicationFiled: April 6, 2016Publication date: August 4, 2016Applicant: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Patent number: 9353250Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: GrantFiled: March 12, 2014Date of Patent: May 31, 2016Assignee: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman
-
Publication number: 20140275426Abstract: A polymer suitable for use in a thin film hinge (living hinge) comprising from about 0.1 to about 5 weight % of a C4-8 comonomer and the balance ethylene, said composition having a density as determined according to ASTM D 792 from about 0.945 to about 0.965 g/cm3; a melt index as determined according to ASTM D1238 (2.16 kg/190° C.) from about 10 to about 20 g/10 min; a weight average molecular weight (Mw) from about 45,000 to about 55,000 g/mol; a polydispersity from about 2.5 to about 3.1 and when molded into a strip having a length of about 13 cm and gross thickness from about 50 to about 70 mil (about 1 to about 2 mm) and completely bent over end to end four times to create a thinned region or crease having a thickness from about 15 to about 30 mil (about 0.3 to about 0.7 mm) tested by bending and releasing the deformed thinned region of the strip through a radius of curvature from about 180 to about 190° about a rounded plate goes through not less than 500 cycles without breaking.Type: ApplicationFiled: March 12, 2014Publication date: September 18, 2014Applicant: NOVA Chemicals (International) S.A.Inventors: Jason Michael Rycroft, Gilbert Alexander Arnould, Matthew Zaki Botros, Mark Rejman