Abstract: An impermeable electrode for batteries, with an impermeable conductive layer of graphite, which is deposited from a suspension comprising graphite at a concentration between 1 and 50 g/l in an organic solvent on a substrate by immersion for a given length of time of, for example, approximately 10 to 60 seconds and wherein, after the deposition, the substrate with the layer of graphite is dried at a temperature between approximately 80 and 150° C. for a given length of time of, for example, approximately 1 minute and, after the drying, is heat-treated at a temperature between approximately 200 and 450° C. for a given length of time of, for example, approximately 5 to 60 minutes.

Abstract: A process for producing an impermeable electrode for electrolytic capacitors, supercapacitors or batteries, with an impermeable conductive layer of graphite, which is deposited from a suspension comprising graphite at a concentration between 1 and 50 g/l in an organic solvent on a substrate by immersion for a given length of time of, for example, approximately 10 to 60 seconds and wherein, after the deposition, the substrate with the layer of graphite is dried at a temperature between approximately 80 and 150° C. for a given length of time of, for example, approximately 1 minute and, after the drying, is heat-treated at a temperature between approximately 200 and 450° C. for a given length of time of, for example, approximately 5 to 60 minutes.

Abstract: A process for producing an impermeable electrode for electrolytic capacitors, supercapacitors or batteries, with an impermeable conductive layer of graphite, which is deposited from a suspension comprising graphite at a concentration between 1 and 50 g/l in an organic solvent on a substrate by immersion for a given length of time of, for example, approximately 10 to 60 seconds and wherein, after the deposition, the substrate with the layer of graphite is dried at a temperature between approximately 80 and 150° C. for a given length of time of, for example, approximately 1 minute and, after the drying, is heat-treated at a temperature between approximately 200 and 450° C. for a given length of time of, for example, approximately 5 to 60 minutes.

Abstract: A process for producing an impermeable electrode for electrolytic capacitors, supercapacitors or batteries, with an impermeable conductive layer of graphite, which is deposited from a suspension comprising graphite at a concentration between 1 and 50 g/l in an organic solvent on a substrate by immersion for a given length of time of, for example, approximately 10 to 60 seconds and wherein, after the deposition, the substrate with the layer of graphite is dried at a temperature between approximately 80 and 150° C. for a given length of time of, for example, approximately 1 minute and, after the drying, is heat-treated at a temperature between approximately 200 and 450° C. for a given length of time of, for example, approximately 5 to 60 minutes.

Abstract: A process for producing an impermeable electrode for electrolytic capacitors, supercapacitors or batteries, with an impermeable conductive layer of graphite, which is deposited from a suspension comprising graphite at a concentration between 1 and 50 g/l in an organic solvent on a substrate by immersion for a given length of time of, for example, approximately 10 to 60 seconds and wherein, after the deposition, the substrate with the layer of graphite is dried at a temperature between approximately 80 and 150 ° C. for a given length of time of, for example, approximately 1 minute and, after the drying, is heat-treated at a temperature between approximately 200 and 450° C. for a given length of time of, for example, approximately 5 to 60 minutes.

Abstract: A metal tape is employed to form electrodes for an electrolytic capacitor. At least one side surface of the metal tape has rigidly adhered thereto a separating sheet of microporous thermoplastic material. This preferably is done by a thermal process or by cementing. Both surfaces of the metal tape, for example formed of aluminum, may have separating sheets applied thereto. Selected regions of such surface or surfaces may be maintained uncoated, whereby subsequent use as electrodes may enable the attachment to such uncoated regions of terminal contacts.

Abstract: The capacitor includes, between an anode and a cathode, a separator formed by at least one porous polymer film and at least one absorbent paper sheet impregnated with an electrolyte, the polymer film being disposed against the anode. The preferred polymer materials are polypropylene and polyester (especially polybutylene terephthalate).

Abstract: An electrolytic filter capacitor has two terminals in a molded insulating cover. The terminals are identical and each is shaped as a polyhedron. The terminals which have means for connection to inner parts of the capacitor and to outer members such as bus bars occupy 15 - 40% of the exposed area of the cover. Each terminal has a plane of symmetry in the direction of maximum size which ae parallel and as closely spaced to each other as insulation requirements permit.