Abstract: A method for production of a fuel cladding tube for a nuclear reactor, characterized by the preparation of an ingot of an alloy of zirconium with the following composition by weight %: 0.8%?Nb?2.8%, traces?Sn?0.65%, 0.015%?Fe?0.40%, C?100 ppm, 600 ppm?O?2300 ppm, 5 ppm?S?100 ppm, Cr+V?0.25%, Hf?75 ppm and F?1 ppm the remainder being zirconium and impurities arising from production. The ingot is then subjected to forging, a hardening and thermomoechanical treatments comprising cold laminations separated by intermediate annealing, all intermediate annealings being carried out at a temperature below the ???+? transition temperature of the alloy, finishing with a recrystallization annealing and resulting in the production of a tube, whereupon an optional external cleaning of the tube is carried out and a mechanical polishing of the external surface of the tube is carried out to give a roughness Ra less than or equal to 0.5 ?m. The invention further relates to a fuel cladding tube obtained thereby.

Abstract: A method for production of a fuel cladding tube for a nuclear reactor, characterised by the preparation of an ingot of an alloy of zirconium with the following composition by weight %: 0.8%?Nb?2.8%, traces?Sn?0.65%, 0.015%?Fe?0.40%, C?100 ppm, 600 ppm?O?2300 ppm, 5 ppm?S?100 ppm, Cr+V?0.25%, Hf?75 ppm and F?1 ppm the remainder being zirconium and impurities arising from production. The ingot is then subjected to forging, a hardening and thermomoechanical treatments comprising cold laminations separated by intermediate annealing, all intermediate annealings being carried out at a temperature below the ???+? transition temperature of the alloy, finishing with a recrystallisation annealing and resulting in the production of a tube, whereupon an optional external cleaning of the tube is carried out and a mechanical polishing of the external surface of the tube is carried out to give a roughness Ra less than or equal to 0.5 ?m. The invention further relates to a fuel cladding tube obtained thereby.

Abstract: A tubular blank (22) is rolled on a mandrel (14) in a pilgrim rolling mill. In a first rolling stage, a first part of the blank (22) is rolled on a first part (18,19) of the mandrel (14), with a reduction of the outside diameter of the blank (22) to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to one of a first wall thickness (e1) and a second wall thickness (e2) exceeding the first wall thickness (e1). The mandrel (14) is advanced in the axial direction. A second part of the blank (22) is rolled on a second part (20,21) of the mandrel spaced from the first part in the axial direction with a reduction of the outside diameter of the blank to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to the other of the first wall thickness (e1) and second wall thickness (e2).

Abstract: A tubular blank (22) is rolled on a mandrel (14) in a pilgrim rolling mill. In a first rolling stage, a first part of the blank (22) is rolled on a first part (18, 19) of the mandrel (14), with a reduction of the outside diameter of the blank (22) to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to one of a first wall thickness (e1) and a second wall thickness (e2) exceeding the first wall thickness (e1). The mandrel (14) is advanced in the axial direction. A second part of the blank (22) is rolled on a second part (20,21) of the mandrel spaced from the first part in the axial direction with a reduction of the outside diameter of the blank to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to the other of the first wall thickness (e1) and second wall thickness (e2).

Abstract: A tubular blank (22) is rolled on a mandrel (14) in a pilgrim rolling mill. In a first rolling stage, a first part of the blank (22) is rolled on a first part (18,19) of the mandrel (14), with a reduction of the outside diameter of the blank (22) to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to one of a first wall thickness (e1) and a second wall thickness (e2) exceeding the first wall thickness (e1). The mandrel (14) is advanced in the axial direction. A second part of the blank (22) is rolled on a second part (20,21) of the mandrel spaced from the first part in the axial direction with a reduction of the outside diameter of the blank to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to the other of the first wall thickness (e1) and second wall thickness (e2).

Abstract: A tubular blank (22) is rolled on a mandrel (14) in a pilgrim rolling mill. In a first rolling stage, a first part of the blank (22) is rolled on a first part (18,19) of the mandrel (14), with a reduction of the outside diameter of the blank (22) to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to one of a first wall thickness (e1) and a second wall thickness (e2) exceeding the first wall thickness (e1). The mandrel (14) is advanced in the axial direction. A second part of the blank (22) is rolled on a second part (20,21) of the mandrel spaced from the first part in the axial direction with a reduction of the outside diameter of the blank to the outside diameter of the guide tube and a reduction of the wall thickness of the blank (22) to the other of the first wall thickness (e1) and second wall thickness (e2).