Abstract: A steel part having a homogeneous multiphase microstructure in each region of the part, the microstructure containing ferrite, wherein the steel part is obtained by a process involving: cutting a blank from a strip of steel, having a specified composition; optionally, the blank undergoes prior cold deformation; the blank is heated to reach a soak temperature Ts above Ac1 but below Ac3 and held at this soak temperature Ts for a soak time ts adjusted so that the steel, after the blank has been heated, has an austenite content equal to or greater than 25% by area; the heated blank is transferred into a forming tool to hot-form the part; and the part is cooled within the tool at a cooling rate V such that the microstructure of the steel, after cooling the part, is a multiphase microstructure containing ferrite and being homogeneous in each region of the part.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010%?Al?0.070%; 0.015%?Nb?0.100%; 0.030%?Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010%?Al?0.070%; 0.015%?Nb?0.100%; 0.030%?Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010% S?Al?0.070%; 0.015%?Nb?0.100%; 0.030% Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: A steel part having a homogeneous multiphase microstructure in each region of the part, the microstructure containing ferrite, wherein the steel part is obtained by a process involving: cutting a blank from a strip of steel, having a specified composition; optionally, the blank undergoes prior cold deformation; the blank is heated to reach a soak temperature Ts above Ac1 but below Ac3 and held at this soak temperature Ts for a soak time ts adjusted so that the steel, after the blank has been heated, has an austenite content equal to or greater than 25% by area; the heated blank is transferred into a forming tool to hot-form the part; and the part is cooled within the tool at a cooling rate V such that the microstructure of the steel, after cooling the part, is a multiphase microstructure containing ferrite and being homogeneous in each region of the part.

Abstract: The subject of the invention is a process for manufacturing a part made of steel having a multiphase microstructure, said microstructure comprising ferrite and being homogeneous in each of the regions of said part, which process comprises the steps consisting in: cutting a blank from a strip of steel, the composition of which is typical of that of steels having a multiphase microstructure; said blank is heated so as to reach a soak temperature Ts above Ac1 but below Ac3 and held at this soak temperature Ts for a soak time ts adjusted so that the steel, after the blank has been heated, has an austenite content equal to or greater than 25% by area; said heated blank is transferred into a forming tool so as to hot-form said part; and said part is cooled within the tool at a cooling rate V such that the microstructure of the steel, after the part has been cooled, is a multiphase microstructure, said microstructure comprising ferrite and being homogeneous in each of the regions of said part.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010% S?Al?0.070%; 0.015%?Nb?0.100%; 0.030% Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The invention relates to a process for manufacturing a part having very high mechanical properties from a hot-rolled or cold-rolled steel strip, comprising precoating said strip with aluminum or an aluminum alloy, cold deformation of the coated strip, possible cutting of the excess sheet with a view to the final geometry of the part, heating of the part so as to form an intermetallic compound from the steel/precoat interface and to austenitize the steel, transfer of the part to a tool and cooling of the part in the tool at a rate such that the steel has, after being cooled, a martensitic or bainitic structure or a martensite-bainite structure. The precoating is carried out by electroplating, by chemical or physical vapor deposition or by co-rolling.

Abstract: The subject of the invention is a process for manufacturing a part made of steel having a multiphase microstructure, said microstructure comprising ferrite and being homogeneous in each of the regions of said part, which process comprises the steps consisting in: cutting a blank from a strip of steel, the composition of which is typical of that of steels having a multiphase microstructure; said blank is heated so as to reach a soak temperature Ts above Ac1 but below Ac3 and held at this soak temperature Ts for a soak time ts adjusted so that the steel, after the blank has been heated, has an austenite content equal to or greater than 25% by area; said heated blank is transferred into a forming tool so as to hot-form said part; and said part is cooled within the tool at a cooling rate V such that the microstructure of the steel, after the part has been cooled, is a multiphase microstructure, said microstructure comprising ferrite and being homogeneous in each of the regions of said part.

Abstract: The invention relates to a process for manufacturing a part having very high mechanical properties from a hot-rolled or cold-rolled steel strip, comprising precoating said strip with aluminum or an aluminum alloy, cold deformation of the coated strip, possible cutting of the excess sheet with a view to the final geometry of the part, heating of the part so as to form an intermetallic compound from the steel/precoat interface and to austenitize the steel, transfer of the part to a tool and cooling of the part in the tool at a rate such that the steel has, after being cooled, a martensitic or bainitic structure or a martensite-bainite structure. The precoating is carried out by electroplating, by chemical or physical vapor deposition or by co-rolling.

Abstract: Methods and systems for delivering radiation therapy to treat disorders in patients are described herein. In one embodiment, a method includes obtaining imaging data of a target in a patient, irradiating the target with a laser beam directed at the target based on the obtained imaging data, and activating a photodynamic therapy agent in the patient with the laser beam. The target can be subcutaneous, cutaneous, or have both subcutaneous and cutaneous portions.

Abstract: Optical detector capable of operating in proximity mode or in proximity with background elimination mode, including an emission system and a reception system having hardware and software detection and configuration means capable of recognizing the appropriate mode by measuring the distance of the background, comparing a reception signal with at least one threshold, and automatically switching the reception system into proximity mode or proximity with background elimination mode depending on the result of the comparison.

Abstract: Method for configuring the operating mode of an optical detector, by recognition, following an emission in a first operating mode M1, by means of the receiving system. The latter then confirms the detector in the first operating mode or switches it over into a second operating mode M2 according to whether there is recognition of the first mode. Automatic validation or validation carried out by the operator confirms the recognized operating mode. Application to multimode optical detectors able to operate in barrier, reflex, proximity, background suppression proximity mode.

Abstract: Optical detector capable of operating in proximity mode or in proximity with background elimination mode.

Abstract: Method for configuring the operating mode of an optical detector, by recognition, following an emission in a first operating mode M1, by means of the receiving system. The latter then confirms the detector in the first operating mode or switches it over into a second operating mode M2 according to whether there is recognition of the first mode. Automatic validation or validation carried out by the operator confirms the recognized operating mode.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the sheet ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.

Abstract: The invention relates to thieno-triazolo-diazepine derivatives of the formula: ##STR1## wherein Y stands for oxygen or sulphur and R stands for various substituents, to a preparation process of said compounds and to therapeutic compositions containing the same. The compounds are particularly interesting as anti-asthmatic, anti-allergic and gastro-intestinal protectors.

Abstract: This invention relates to thieno-triazolo-diazepine derivatives of the formula ##STR1## wherein R represents various substituents, to a preparation process of these compounds consisting in reacting the thieno-triazolo-diazepine compound of the formula ##STR2## on RSO.sub.2 Cl and to therapeutic compositions containing the same. The compounds are particularly interesting as anti-PAF and anti-ischemic agents.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the sheet ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the shoot ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.