Abstract: Luff guiding device for a sail, the sail being able to be wound on a boom of a sail boat, comprising a first element including a continuous groove in which a luff of a sail is engaged to freely circulate, the sail being able to be wound on a boom of a sail boat. The first element is positioned at a rear of a mast, and is pivotally mounted around a longitudinal axis extending through the element on both sides of a plane of symmetry of the sailboat.

Abstract: The present invention is directed to a four-step process for molding glass articles of high precision and excellent surface figure. A glass preform having an overall geometry closely approximating that of the desired final product is placed into a mold, the mold and preform are brought to a temperature at which the glass exhibits a viscosity between 10.sup.8 -10.sup.12 poises, a load is applied to shape the glass into conformity with the mold, and thereafter the resulting glass article is removed from the mold at a temperature above the transformation range of the glass. The glass article is then annealed.

Abstract: The present invention is directed to a four-step process for molding glass articles of high precision and excellent surface figure. A glass preform having an overall geometry closely approximating that of the desired final product is placed into a mold, the mold and preform are brought to a temperature at which the glass exhibits a viscosity between 10.sup.8 -10.sup.12 poises, a load is applied to shape the glass into conformity with the mold, and thereafter the glass shape is removed from the mold at a temperature above the transformation range of the glass and annealed.

Abstract: The present invention is directed to a four-step process for molding glass articles of high precision and excellent surface figure. A glass preform having an overall geometry closely approximating that of the desired final product is placed into a mold, the mold and preform are brought to a temperature at which the glass exhibits a viscosity between 10.sup.8 -10.sup.12 poises, a load is applied to shape the glass into conformity with the mold, and thereafter the glass shape is removed from the mold at a temperature above the transformation range of the glass and annealed.

Abstract: The present invention is directed to a four-step process for molding glass articles of high precision and excellent surface figure. A glass preform having an overall geometry closely approximating that of the desired final product is placed into a mold, the mold and preform are brought to a temperature at which the glass exhibits a viscosity between 10.sup.8 -10.sup.12 poises, a load is applied to shape the glass into conformity with the mold, and thereafter the glass shape is removed from the mold at a temperature above the transformation range of the glass and annealed.