Abstract: A manufacturing process for a remelt block containing aluminum designed for making aluminum alloy for the aircraft industry in which scrap containing mainly aluminum alloys used in the aircraft industry is supplied during a supply stage, the scrap is melted in a smelting furnace in order to obtain an initial molten metal bath during a smelting stage, the initial molten metal bath is subjected to purification by fractional crystallization in order to obtain a solidified mass and a bath of residual liquid during a segregation stage, and the solidified mass is recovered in order to obtain a remelt block during a recovery stage. The invention is particularly useful for the recycling of aluminum alloys used in the aircraft industry as it makes it possible to purify scrap of series 2XXX or series 7XXX alloys for iron and silicon, without eliminating additive elements such as zinc, copper and magnesium.

Abstract: The invention relates to a method of manufacturing aluminium nitride, in which a multilayer structure including rolled aluminium-based products is prepared by stacking or winding, and it is heated under a nitrogenous atmosphere, the majority of the nitriding occurring during a phase in which the temperature of the nitrogenous atmosphere is maintained between 400° C. and 660° C. The invention makes it possible to obtain aluminium nitride via an economic method requiring neither the use of aluminium powder as a raw material nor the use of very high temperatures. The aluminium nitride obtained includes particles the microscopic structure of which is layered.

Abstract: A manufacturing process for a remelt block containing aluminum designed for making aluminum alloy for the aircraft industry in which scrap containing mainly aluminum alloys used in the aircraft industry is supplied during a supply stage, the scrap is melted in a smelting furnace in order to obtain an initial molten metal bath during a smelting stage, the initial molten metal bath is subjected to purification by fractional crystallization in order to obtain a solidified mass and a bath of residual liquid during a segregation stage, and the solidified mass is recovered in order to obtain a remelt block during a recovery stage. The invention is particularly useful for the recycling of aluminum alloys used in the aircraft industry as it makes it possible to purify scrap of series 2XXX or series 7XXX alloys for iron and silicon, without eliminating additive elements such as zinc, copper and magnesium.

Abstract: This invention relates to a thin refined aluminium sheet or strip with purity greater than 99.9%, designed for making anodes of electrolytic capacitors, with an atomic content of between 5 and 25% of aluminium carbide in the 10 nm thick surface layer, and preferably between 10 and 20%.

Abstract: Thin foil of refined aluminum for the manufacture of anodes for electrolytic capacitors, the foil being formed of aluminum of a purity greater than 99.9% by weight and at least one of the elements Pb, B and In with an average total content of these elements of between 0.1 and 10 ppm by weight. The elements are distributed in a surface zone of the foil at a depth of 0.1 &mgr;m, such that a signal current obtained by ionic analysis has a dispersion ratio (Imax−Imin)/Iaverage of less than 5.