Abstract: The present development is a catalyst for use in water gas shift processes, a method for making the catalyst and a method of using the catalyst. The catalyst is composed of iron oxide, copper oxide, zinc oxide, alumina, and optionally, potassium oxide, and is produced using a hydrothermal synthesis process. The catalyst demonstrates surprising activity for conversion of carbon monoxide under high to moderate temperature shift reaction conditions.

Abstract: The present development is a catalyst for use in water gas shift processes, a method for making the catalyst and a method of using the catalyst. The catalyst is composed of iron oxide, copper oxide, zinc oxide, alumina, and optionally, potassium oxide, and is produced using a hydrothermal synthesis process. The catalyst demonstrates surprising activity for conversion of carbon monoxide under high to moderate temperature shift reaction conditions.

Abstract: A promoted calcium-alumina supported reforming catalyst that is particularly useful for reforming reactions where low H2/CO ratio synthesis gas, such as less than 2.3 is generated directly is disclosed. The catalyst comprises from about 25 wt % to about 98 wt % alumina, from about 0.5 wt % to about 35 wt % calcium oxide, from about 0.01 wt % to about 35 wt % of a promoter, and from about 0.05 wt % to about 30 wt % of an active metal. The promoter is selected from the group consisting of titanium, zirconium, yttrium, niobium, elements of the lanthanum-series, such as, without limitation, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, ytterbium, and combinations thereof. The active metal is selected from the group consisting of nickel, cobalt, rhodium, ruthenium, palladium, platinum, iridium and combinations thereof as active metal, wherein the calcium oxide is combined with the alumina to form aluminum-rich calcium aluminates.