Patents by Inventor Jenny Loiseaux

Jenny Loiseaux has filed for patents to protect the following inventions. This listing includes patent applications that are pending as well as patents that have already been granted by the United States Patent and Trademark Office (USPTO).

  • Method for hot forming a coated metal part and formed part
    Patent number: 9127329
    Abstract: A method for manufacturing a coated part having very high mechanical properties using hot forming techniques. The method includes: —providing an annealed steel strip or blank or pre-shaped part that was coated with a metal or metal alloy before the annealing —if a strip is provided, cutting a blank from the strip before or after the annealing —optionally forming a pre-shaped part from the blank —heating the blank or preshaped part to a temperature of 500° C. at an average heating rate of 16° C./s or more —further heating the blank or pre-shaped part to a temperature between 700 and 1000° C. —hot forming the blank or preshaped part into a hot formed part —hardening the hot formed part. A method for manufacturing a coated steel strip, blank or pre-shaped part, and a coated steel strip, blank or part and a hot formed part.
    Type: Grant
    Filed: July 19, 2011
    Date of Patent: September 8, 2015
    Assignee: TATA STEEL IJMUIDEN B.V.
    Inventors: Willem Cornelis Verloop, Marc Jacco van Genderen, Ronald Theodoor van Tol, Guido Cornelis Hensen, Jenny Loiseaux
  • METHOD FOR HOT FORMING A COATED METAL PART AND FORMED PART
    Publication number: 20130153094
    Abstract: A method for manufacturing a coated part having very high mechanical properties using hot forming techniques. The method includes:—providing an annealed steel strip or blank or pre-shaped part that was coated with a metal or metal alloy before the annealing—if a strip is provided, cutting a blank from the strip before or after the annealing—optionally forming a pre-shaped part from the blank—heating the blank or preshaped part to a temperature of 500° C. at an average heating rate of 16° C./s or more—further heating the blank or pre-shaped part to a temperature between 700 and 1000° C.—hot forming the blank or preshaped part into a hot formed part—hardening the hot formed part. A method for manufacturing a coated steel strip, blank or pre-shaped part, and a coated steel strip, blank or part and a hot formed part.
    Type: Application
    Filed: July 19, 2011
    Publication date: June 20, 2013
    Applicant: TATA STEEL IJMUIDEN B.V.
    Inventors: Willem Cornelis Verloop, Marc Jacco van Genderen, Ronald Theodoor van Tol, Guido Cornelis Hensen, Jenny Loiseaux