Abstract: A polyethylene composition having the following features: 1) density from 0.945 to 0.958 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from 20 to 43; 3) MIF from 4.0 to less than 8.5 g/10 min.; 4) HMWcopo index from 3.5 to 20; and 5) long-chain branching index, LCBI, equal to or lower than 0.82. The polyethylene composition can be used to produce blown films.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.951 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 25 to about 43; 3) MIF from about 3.5 to less than about 8.5 g/10 min.; 4) HMWcopo index from about 1 to about 40; and 5) long-chain branching index, LCBI, equal to or greater than about 0.83. The polyethylene composition can be used to produce pipes.

Abstract: Polyethylene composition for injection molding with a beneficial balance of environmental stress cracking resistance and impact resistance in combination with low warpage and beneficial processing behavior, said composition having the following features: 1) density of 0.945 g/cm3 or higher; 2) MIE from 1 to 30 g/10 min.; 3) ratio MIF/MIE from 15 to 30; 4) ER values from 0.40 to 0.52.

Abstract: A process for the preparation of polyolefins by polymerizing olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst and an antistatically acting composition in a polymerization reactor, wherein the antistatically acting composition is a mixture comprising an oil-soluble surfactant and water and the use of an antistatically acting composition comprising an oil-soluble surfactant and water as antistatic agent for the polymerization of olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.951 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 25 to about 43; 3) MIF from about 3.5 to less than about 8.5 g/10 min.; 4) HMWcopo index from about 1 to about 40; and 5) long-chain branching index, LCBI, equal to or greater than about 0.83. The polyethylene composition can be used to produce pipes.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.958 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 20 to about 43; 3) MIF from about 4.0 to less than about 8.5 g/10 min.; 4) HMWcopo index from about 3.5 to about 20; and 5) long-chain branching index, LCBI, equal to or lower than about 0.82. The polyethylene composition can be used to produce blown films.

Abstract: A process for the preparation of polyolefins by polymerizing olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst and an antistatically acting composition in a polymerization reactor, wherein the antistatically acting composition is a mixture comprising an oil-soluble surfactant and water and the use of an antistatically acting composition comprising an oil-soluble surfactant and water as antistatic agent for the polymerization of olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst.

Abstract: A process for the preparation of polyolefins by polymerizing olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst and an antistatically acting composition in a polymerization reactor, wherein the antistatically acting composition is a mixture comprising an oil-soluble surfactant and water and the use of an antistatically acting composition comprising an oil-soluble surfactant and water as antistatic agent for the polymerization of olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-molded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present technology relates to a polyethylene composition suitable for producing small articles such as flexible and collapsible tubes by blow molding comprising: 1) a density from 0.948 to 0.955 g/cm3; 2) a MIF/MIP ratio from 12 to 25; 3) a MIF from 25 to 40 g/10 min; 4) a Mz from 1000000 to 2000000 g/mol; and 5) a long-chain branching index, LCBI, equal to or greater than 0.55.

Abstract: Polyethylene composition for injection molding with a beneficial balance of environmental stress cracking resistance and impact resistance in combination with low warpage and beneficial processing behavior, said composition having the following features: 1) density of 0.945 g/cm3 or higher; 2) MIE from 1 to 30 g/10 min.; 3) ratio MIF/MIE from 15 to 30; 4) ER values from 0.40 to 0.52.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) a density from 0.952 to 0.960 g/cm3; 2) an MIF/MIP ratio from 17 to 30; and 3) a Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties for use in preparing blow-moulded articles and having the following features: 1) a density from 0.945 to less than 0.952 g/cm3; 2) an MIF/MIP ratio from 15 to 30; 3) a Shear-Induced Crystallization Index (SIC) from 2.5 to 5.5.

Abstract: Polyethylene composition with improved balance of environmental stress cracking resistance (FNCT) and impact resistance (Charpy), particularly suited for preparing pipes, said composition having the following features: 1) density from 0.945 to 0.955 g/cm3; 2) ratio MIF/MIP from more than 30 to 45; 3) Shear-Induced Crystallization Index SIC from 1.0 to 2.5; 4) Long Chain Branching index equal to or greater than 0.85.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-molded articles, said composition having the following features: 1) density from 0.945 to less than 0.952 g/cm3; 2) ratio MIF/MIP from 15 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.5.

Abstract: The present disclosure relates to a polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) a density from 0.952 to 0.960 g/cm3; 2) an MIF/MIP ratio from 17 to 30; and 3) a Shear-Induced Crystallization Index SIC from 2.5 to 5.0.

Abstract: The present technology relates to a polyethylene composition suitable for producing small articles such as flexible and collapsible tubes by blow molding comprising: 1) a density from 0.948 to 0.955 g/cm3; 2) a MIF/MIP ratio from 12 to 25; 3) a MIF from 25 to 40 g/10 min; 4) a Mz from 1000000 to 2000000 g/mol; and 5) a long-chain branching index, LCBI, equal to or greater than 0.55.

Abstract: Polyethylene composition with improved swell ratio and mechanical properties, particularly suited for preparing blow-moulded articles, said composition having the following features: 1) density from 0.952 to 0.960 g/cm3; 2) ratio MIF/MIP from 17 to 30; 3) Shear-Induced Crystallization Index SIC from 2.5 to 5.0.