Abstract: A titanium alloy having ultrahigh strength and ultralow elastic modulus, and showing linear elastic deformation behavior is disclosed. The titanium alloy (Ti-20Nb-5Zr-1Fe-O) of the present invention consists of titanium, niobium, zirconium, iron and oxygen. More specifically, the amount of niobium is 18 to 22 at. %, the amount of zirconium is 3 to 7 at. %, the amount of iron is 0.5 to 3.0 at. %, the amount of oxygen is 0.1 to 1.0 wt. %, and the balance is titanium.

Abstract: In a Ti—Ni alloy thin film, Ti and Ni are mixed and deposited on a base material by putting a Ti target and an Ni target at a predetermined distance from each other in a co-sputtering apparatus and simultaneously sputtering the targets by applying different voltages. A method of fabricating a Ti—Ni alloy thin film using co-sputtering includes a target preparing step that prepares a Ti target, a Ni target and a base material, a target disposing step that puts the Ti target and the Ni target at a predetermined distance from each other in a co-sputtering apparatus, an apparatus setting step that sets work conditions of the co-sputtering apparatus, and a thin film depositing step that forms a Ti—Ni alloy thin film with Ti and Ni mixed on the base material by operating the co-sputtering apparatus.

Abstract: A titanium alloy having ultrahigh strength and ultralow elastic modulus, and showing linear elastic deformation behavior is disclosed. The titanium alloy (Ti-20Nb-5Zr-1Fe-O) of the present invention consists of titanium, niobium, zirconium, iron and oxygen. More specifically, the amount of niobium is 18 to 22 at. %, the amount of zirconium is 3 to 7 at. %, the amount of iron is 0.5 to 3.0 at. %, the amount of oxygen is 0.1 to 1.0 wt. %, and the balance is titanium.

Abstract: A multilayer metal structure is provided that includes an inner layer of metal materials which are not titanium and outer layers on both sides of the inner layer which are formed by rolling titanium powders. A method for manufacturing the multilayer metal structure is provided that includes preparing titanium powders and metal materials which are not titanium, feeding the titanium powders and the metal materials to a vertical type rolling mill, simultaneously rolling the titanium powders and the metal materials by the rolling mill and forming the multilayer metal structure consisting of an inner layer and outer layers on both sides of the inner layer, and post-forming the multilayer metal structure to increase a packing density.