Abstract: A geopolymer cement and a method of producing the same are provided. A geopolymer cement binder may be provided including a geopolymer precursor and magnesium oxide as an alkali activator. The geopolymer cement binder may be mixed with water using high shear mixing.

Abstract: Portland Cement-based concretes and mortars exhibit significant reduction in shrinkage cracking when combined with Magnesium Oxide (MgO), Shrinkage Reduction Admixtures (SRA) and Super Absorbent Polymers (SAP). However, MgO is a solid that reacts with water, SRA is a liquid, and SAP if not added properly could pull water out of the system and thus increase shrinkage. Unique admixture blends used as supplementary cementing materials that do not significantly affect concrete or cement strength properties of Portland cement itself address such issues. Proper ratios of MgO, SRA and/or SAP perform better against crack reduction when compared to commonly used Expansive Cements (EC).

Abstract: Despite the excellent properties associated with Magnesium OxyChloride (Sorel) based cements and Magnesium OxySulfate based cements, water and corrosion resistance has been limiting factors for achieving greater commercial applications. Such issues can be addressed by incorporating various alkali metal phosphates, such as Magnesium mono- or dihydrogen phosphate (MgHPO4 or MgH2PO4) with alkali metal fatty acids; such as Magnesium Stearate; and metal or alkali metal sulfates such as Aluminum Sulfate or Magnesium Sulfate. Water resistance is further enhanced by either pre-carbonating the mix water or the liquid magnesium chloride phase of the cements, or by adding a carbonate into the powder phase. Accelerated cure of this system has also been obtained by using various inorganic metal oxides. Additionally, improved corrosion resistance is achieved through the use of certain phosphates, zeolites, nitrites and other novel additives.