Abstract: A method of manufacturing a polyolefin foam sheet composition includes extruding a polyolefin sheet, irradiating the extruded sheet to obtain a physically crosslinked sheet, foaming the physically crosslinked sheet with heat to obtain a foamed layer, and skiving the foamed layer to obtain a foam sheet with at least one skived surface. The surface roughness of the skived surface of the foam sheet is different from the surface roughness of an unskived surface.

Abstract: A method of making a foam composition includes blending a composition including (i) about 15 to about 75 parts by weight of an olefin block copolymer with a controlled block sequence having a melt flow index of about 0.1 to about 15 grams per 10 minutes at 190° C. and a melting temperature of at least about 115° C., (ii) about 25 to about 85 parts by weight of at least one polypropylene based polymer having a melt flow index from about 0.1 to about 25 grams per 10 minutes at 230° C., (iii) a crosslinking monomer and (iv) a chemical blowing agent to produce a blended composition; crosslinking the blended composition to obtain a crosslinked composition having a crosslinking degree of about 20 to about 75%; and foaming the crosslinked composition at an elevated temperature to obtain a foam composition having a density of about 20 to about 250 kg/m3.

Abstract: A method of manufacturing a polyolefin foam sheet composition includes extruding a polyolefin sheet, irradiating the extruded sheet to obtain a physically crosslinked sheet, foaming the physically crosslinked sheet with heat to obtain a foamed layer, and skiving the foamed layer to obtain a foam sheet with at least one skived surface. The surface roughness of the skived surface of the foam sheet is different from the surface roughness of an unskived surface.

Abstract: A method of making a foam composition includes blending a composition including (i) about 15 to about 75 parts by weight of an olefin block copolymer with a controlled block sequence having a melt flow index of about 0.1 to about 15 grams per 10 minutes at 190° C. and a melting temperature of at least about 115° C., (ii) about 25 to about 85 parts by weight of at least one polypropylene based polymer having a melt flow index from about 0.1 to about 25 grams per 10 minutes at 230° C., (iii) a crosslinking monomer and (iv) a chemical blowing agent to produce a blended composition; crosslinking the blended composition to obtain a crosslinked composition having a crosslinking degree of about 20 to about 75%; and foaming the crosslinked composition at an elevated temperature to obtain a foam composition having a density of about 20 to about 250 kg/m3.

Abstract: A crosslinked, closed cell polyolefin foam sheet has exceptional softness, haptics, moldability, thermal stability and shear strength as well as a laminate and uses thereof.

Abstract: A foam composition comprising about 50 to about 95 parts by weight of at least one polypropylene polymer having a density of about 85 to about 125 kg/m3, wherein the composition has blister rating of 1-2, an unaged peel tear strength of at least about 34 N and a heat aged peel tear strength of at least about 28 N when laminated to a support layer.

Abstract: A crosslinked, closed cell polyolefin foam sheet has exceptional softness, haptics, moldability, thermal stability and shear strength as well as a laminate and uses thereof.