Abstract: A method for preparing a rare earth anisotropic bonded magnetic powder, comprises the following steps: (1) preparing raw powder with RTBH as the main component, wherein, R is Nd or Pr/Nd, and T is a transition metal containing Fe; (2) adding La hydride or Ce hydride and copper powder to the raw powder to form a mixture; (3) subjecting the mixture to atmosphere diffusion heat treatment to give the rare earth anisotropic bonded magnetic powder.

Abstract: The invention discloses a composite rare earth anisotropic bonded magnet and a preparation method thereof. The composite rare earth anisotropic bonded magnet comprises a Nd—Fe—B magnetic powder, a Sm—Fe—N magnetic powder, a binder and an inorganic nano-dispersant. The preparation method comprises steps of preparing a Nd—Fe—B magnetic powder by a HDDR method, preparing a Sm—Fe—N magnetic powder by a powder metallurgy method, mixing the Nd—Fe—B magnetic powder, the Sm—Fe—N magnetic powder, the binder and the inorganic nano-dispersant at a specific ratio to finally obtain the composite rare earth anisotropic bonded magnet. The invention, by adding an inorganic nano-dispersant, enables the full dispersion of the fine Sm—Fe—N powder during the mixing process of the binder, the Nd—Fe—B magnetic powder and the Sm—Fe—N powder, and thus makes the fine Sm—Fe—N powder and the binder evenly coated on the surface of the anisotropic Nd—Fe—B magnetic powder.

Abstract: The present invention relates to the field of forming technologies for rubber sealing ring blanks, and more particularly to an automatic forming method and device for a rubber sealing ring blank. A cutting blade is fixedly connected to the surface of a blank forming assembly; an equipment body II is fixedly connected to a sliding table die set; a supporting rod II is fixedly connected to the surface of the equipment body II; a blank box is fixedly connected to the inner side surface of the supporting rod II; and a blank spool is fixedly connected to the tail end of a long blank strip. The method and device disclosed by the present invention have the advantages that the automation degree is high, and the long blank strip conveyed from the blank spool passes through guide wheels and a guide groove and is automatically pressed into a ring through the combined action of the blank forming assembly and the cutting blade.

Abstract: An anisotropic bonded magnet and a preparation method thereof are provided. By stacking magnets having different magnetic properties and/or densities, the magnets in the middle have high properties and the magnets at two ends and/or the periphery have low properties, thereby compensating for a property deviation caused by a difference in pressing densities during a pressing process, and improving the property uniformity of the magnets in an axial direction. The method solves the problem of “low in the middle and high at two ends” caused by the phenomenon of non-uniform magnetic field orientation and density along a height direction during orientation and densification.

Abstract: The present disclosure discloses an yttrium (Y)-added rare-earth permanent magnetic material and a preparation method thereof. A chemical formula of the material expressed in atomic percentage is (YxRE1-x)aFebalMbNc, wherein 0.05?x?0.4, 7?a?13, 0?b?3, 5?c?20, and the balance is Fe, namely, bal=100-a-b-c; RE represents a rare-earth element Sm, or a combination of the rare-earth element Sm and any one or more elements of Zr, Nd and Pr; M represents Co and/or Nb; and N represents nitrogen. In the preparation method, the rare-earth element Y is utilized to replace the element Sm of a samarium-iron-nitrogen material. By regulating a ratio of the element Sm to the element Y, viscosity of an alloy liquid can be reduced, and an amorphous forming ability of the material is enhanced.

Abstract: The present invention discloses rare earth-bonded magnetic powder and a preparation method therefor. The bonded magnetic powder is of a multilayer core-shell structure, and comprises a core layer and an antioxidant layer (3), wherein the core layer is formed by RFeMB, R is Nd and/or PrNd, and M is one or more of Co, Nb, and Zr; and the core layer is coated with an iron-nitrogen layer (2). In addition, the present invention also discloses the preparation method for the rare earth-bonded magnetic powder and a bonded magnet. The oxidation and corrosion of magnetic raw powder during phosphorization and subsequent treatment process are effectively prevented, thereby further improving the long-term temperature resistance and environmental tolerance of the material.

Abstract: The present invention relates to a modified sintered Nd—Fe—B magnet, and a preparation method and a use thereof. The modified sintered Nd—Fe—B magnet is prepared by performing grain boundary diffusion on a matrix, wherein the matrix is a sintered Nd—Fe—B magnet; a grain boundary diffusion source for the grain boundary diffusion consists of a first diffusion source and a second diffusion source; the first diffusion source is a PrMx alloy, M being at least one selected from a group consisted of Cu, Al, Zn, Mg, Ga, Sn, Ag, Pb, Bi, Ni, Nb, Mn, Co, Fe, Ti, Cr, Zr, Mo and Ge; and the second diffusion source is heavy rare earth Dy and/or Tb.

Abstract: An anisotropic bonded magnet and a preparation method thereof are provided. Through a method of stacking magnets which are different in content of SmFeN and/or have different densities, the magnets in the middle have high properties and the magnets at two ends and/or the periphery have low properties, thereby compensating for a property deviation caused by a difference in densities during a pressing process, and improving the property uniformity of the magnets in an axial direction. The method avoids the phenomenon of non-uniform magnetic field orientation and density in a height direction during orientation and densification as well as the phenomenon of low in the middle and high at two ends.

Abstract: An anisotropic bonded magnet and a preparation method thereof are provided. By stacking magnets having different magnetic properties and/or densities, the magnets in the middle have high properties and the magnets at two ends and/or the periphery have low properties, thereby compensating for a property deviation caused by a difference in pressing densities during a pressing process, and improving the property uniformity of the magnets in an axial direction. The method solves the problem of “low in the middle and high at two ends” caused by the phenomenon of non-uniform magnetic field orientation and density along a height direction during orientation and densification.

Abstract: The present invention discloses an yttrium-added rare earth permanent magnet material and a preparation method therefor. The chemical formula of the material is expressed as (YxRe1-x)aFe100-a-b-cMbBc according to the mass percentage, wherein 0.05?x?0.5, 20?a?28, 0.5?b?2, 0.5?c?1.5, Re is Nd and/or Pr, and M is Al and/or Nb. According to the present invention, the relatively surplus and inexpensive rare earths yttrium and cerium are used to replace Nd and/or Pr in NdFeB. By controlling the ratio of the rare earth elements such as yttrium, cerium and neodymium, and adding an appropriate amount of Nb and/or Al element, the rare earth elements are used in a comprehensive and balanced manner while better magnetic properties are maintained.

Abstract: The present invention discloses rare earth-bonded magnetic powder and a preparation method therefor. The bonded magnetic powder is of a multilayer core-shell structure, and comprises a core layer and an antioxidant layer (3), wherein the core layer is formed by RFeMB, R is Nd and/or PrNd, and M is one or more of Co, Nb, and Zr; and the core layer is coated with an iron-nitrogen layer (2). In addition, the present invention also discloses the preparation method for the rare earth-bonded magnetic powder and a bonded magnet. The oxidation and corrosion of magnetic raw powder during phosphorization and subsequent treatment process are effectively prevented, thereby further improving the long-term temperature resistance and environmental tolerance of the material.

Abstract: The invention discloses an anisotropic bonded magnetic powder and a preparation method thereof. The anisotropic bonded magnetic powder has a general formula of R1R2TB, wherein R1 is a rare earth element containing Nd or PrNd, R2 is one or two of La and Ce, T is a transitional element, and B is boron. The preparation method includes the steps of smelting the master alloy to prepare ingot(s), preparing a rare earth hydride of formula R1TBHX, preparing a hydride diffusion source of formula R1R2THX, mixing, heat treating, and high-vacuum dehydrogenating, to obtain the anisotropic bonded magnetic powder. The invention uses La and Ce hydrides as the diffusion source, can save cost, remove hydrogen from the diffusion source at a lower dehydrogenation temperature, avoid crystal grain growth at a high temperature, and ensure the quality of the product.

Abstract: A method for preparing a rare earth anisotropic bonded magnetic powder, comprises the following steps: (1) preparing raw powder with RTBH as the main component, wherein, R is Nd or Pr/Nd, and T is a transition metal containing Fe; (2) adding La/Ce hydride and copper powder to the raw powder to form a mixture; (3) subjecting the mixture to atmosphere diffusion heat treatment to give the rare earth anisotropic bonded magnetic powder. The invention selects high-abundance rare earth elements La, Ce to replace Dy, Tb, Nd, Pr and other medium and heavy rare earth elements, which can achieve the same coercivity improvement effect while also significantly reducing the cost, thereby achieving efficient application of low-cost and high-abundance rare earths.

Abstract: The invention discloses a composite rare earth anisotropic bonded magnet and a preparation method thereof. The composite rare earth anisotropic bonded magnet comprises a Nd—Fe—B magnetic powder, a Sm—Fe—N magnetic powder, a binder and an inorganic nano-dispersant. The preparation method comprises steps of preparing a Nd—Fe—B magnetic powder by a HDDR method, preparing a Sm—Fe—N magnetic powder by a powder metallurgy method, mixing the Nd—Fe—B magnetic powder, the Sm—Fe—N magnetic powder, the binder and the inorganic nano-dispersant at a specific ratio to finally obtain the composite rare earth anisotropic bonded magnet. The invention, by adding an inorganic nano-dispersant, enables the full dispersion of the fine Sm—Fe—N powder during the mixing process of the binder, the Nd—Fe—B magnetic powder and the Sm—Fe—N powder, and thus makes the fine Sm—Fe—N powder and the binder evenly coated on the surface of the anisotropic Nd—Fe—B magnetic powder.

Abstract: The present disclosure discloses an yttrium (Y)-added rare-earth permanent magnetic material and a preparation method thereof. A chemical formula of the material expressed in atomic percentage is (YxRE1-x)aFebalMbNc, wherein 0.05?x?0.4, 7?a?13, 0?b?3, 5?c?20, and the balance is Fe, namely, bal=100-a-b-c; RE represents a rare-earth element Sm, or a combination of the rare-earth element Sm and any one or more elements of Zr, Nd and Pr; M represents Co and/or Nb; and N represents nitrogen. In the preparation method, the rare-earth element Y is utilized to replace the element Sm of a samarium-iron-nitrogen material. By regulating a ratio of the element Sm to the element Y, viscosity of an alloy liquid can be reduced, and an amorphous forming ability of the material is enhanced.

Abstract: The application discloses a rare-earth permanent magnetic powder, a bonded magnet, and a device using the bonded magnet. The rare-earth permanent magnetic powder comprises 4 to 12 at. % of Nd, 0.1 to 2 at. % of C, 10 to 25 at. % of N and 62.2 to 85.9 at. % of T, wherein T is Fe or FeCo and the main phase of the rare-earth permanent magnetic powder is a hard magnetic phase with a TbCu7 structure. Material volatilization can be avoided effectively during a preparation process of the rare earth permanent magnetic powder, thus improving the wettability with a water-cooling roller during the preparation process and final prepared materials are provided with good magnetic properties.

Abstract: The application discloses a rare-earth permanent magnetic powder, a bonded magnet, and a device using the bonded magnet. The rare-earth permanent magnetic powder comprises 4 to 12 at. % of Nd, 0.1 to 2 at. % of C, 10 to 25 at. % of N and 62.2 to 85.9 at. % of T, wherein T is Fe or FeCo and the main phase of the rare-earth permanent magnetic powder is a hard magnetic phase with a TbCu7 structure. Material volatilization can be avoided effectively during a preparation process of the rare earth permanent magnetic powder, thus improving the wettability with a water-cooling roller during the preparation process and final prepared materials are provided with good magnetic properties.

Abstract: The invention is directed to the field of natural medicine, specifically to alkaloid extracts of Huperzia serrata (Thunb.) Trev. A Huperzia serrata (Thunb.) Trev. composition and the method for preparing it are provided. The Huperzia serrata (Thunb.) Trev. composition comprises Huperzine A and Huperzine B, wherein the total content of the said Huperzine A and Huperzine B is 50-99 wt % of total alkaloids and the weight ratio of the said Huperzine A and Huperzine B is 1:0.5-5. The Huperzia serrata (Thunb.) Trev. composition of the invention has good therapeutic effect and improved safety.

Abstract: The invention is directed to the field of natural medicine, specifically to alkaloid extracts of Huperzia serrata (Thunb.) Trev. A Huperzia serrata (Thunb.) Trev. composition and the method for preparing it are provided. The Huperzia serrata (Thunb.) Trev. composition comprises Huperzine A and Huperzine B, wherein the total content of the said Huperzine A and Huperzine B is 50-99 wt % of total alkaloids and the weight ratio of the said Huperzine A and Huperzine B is 1:0.5-5. The Huperzia serrata (Thunb.) Trev. composition of the invention has good therapeutic effect and improved safety.